Abstract
Ceria stabilized zirconia powders with ceria concentration varying from 6 to 16 mol% were synthesized using spray drying technique. Powders were characterized for their particle size distribution and specific surface area. The dense sintered ceramics fabricated using these powders were characterized for their microstructure, crystallite size and phase composition. The flexural strength, fracture toughness and microhardness of sintered ceramics were measured. High fracture toughness and flexural strength were obtained for sintered bodies with 12 mol% of CeO2. Flexural strength and fracture toughness were dependent on CeO2 concentration, crystallite size and phase composition of sintered bodies. Correlation of data has indicated that the transformable tetragonal phase is the key factor in controlling the fracture toughness and strength of ceramics. It has been demonstrated that the synthesis method is effective to prepare nanocrystalline tetragonal ceria stabilized zirconia powders with improved mechanical properties. Ce-ZrO2 with 20 wt% alumina was also prepared with flexural strength, 1200 MPa and fracture toughness, 9.2 MPa√m.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Chen I W and Reyes-Morel P E 1986J. Am. Ceram. Soc. 69 181
Chen Y L and Brook R 1989J. Br. Ceram. Trans. J. 88 7
Cutler R A, Mayhew R J, Prettyman K M and Virkar A V 1991J. Am. Ceram. Soc. 74 179
Evans A G and Cannon R M 1986Acta Metall. 34 761
Garvie R C, Hannink R H J and Pascoe R T 1975Nature 258 703
Gokhale N M, Dayal R, Sharma S C and Lal R 1994J. Mater. Sci. 29 5709
Hannink R H J, Kelly P M and Muddle B C 2000J. Am. Ceram. Soc. 83 461
Klug H P and Alexander L E 1954X-ray diffraction procedures (New York: Wiley) Ch. 9
Kojima T, Sakamato W, Yogo T, Fuji T and Hirano S 2000J. Am. Ceram. Soc. 83 281
Lal R, Sharma S C and Dayal R 1993Ferroelectrics 141 165
Lange F F 1982J. Mater. Sci. 17 225
Maschio S, Sbaizero O and Meriani S 1992J. Euro. Ceram. Soc. 9 127
Maschio S, Pezzotto G and Sbaizero O 1998J. Euro. Ceram. Soc. 18 1979
Matsui K and Ohgai M 1999J. Am. Ceram. Soc. 82 3017
Matsumato R K 1978J. Am. Ceram. Soc. 71 C128
McMeeking R and Evans A G 1982J. Am. Ceram. Soc. 65 242
Nettleship I and Stevens R 1987Int. J. High Tech. Ceram. 3 1
Osendi M I, Moya J S, Serna C J and Soria J 1985J. Am. Ceram. Soc. 68 135
Quinelato A L, Longo E, Perzolli L A and Varela J A 2000J. Eur. Ceram. Soc. 20 1077
Tsukuma K and Shimada M 1985J. Mater. Sci. 20 1178
Wang J, Zheng X H and Stevens R 1992J. Mater. Sci. 27 5348
Yin S, Uchida S, Fujishiro Y, Ohmori M and Sato T 1999Br. Ceram. Trans. J. 98 19
Yoshioka T, Dosaka K, Sato T, Okuwaki S, Tanno S and Miura T 1992J. Mater. Sci. Lett. 11 61
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sharma, S.C., Gokhale, N.M., Dayal, R. et al. Synthesis, microstructure and mechanical properties of ceria stabilized tetragonal zirconia prepared by spray drying technique. Bull Mater Sci 25, 15–20 (2002). https://doi.org/10.1007/BF02704588
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02704588