Stoichiometric hydroxyapatite with Ca/P molar ratio, 1.67, was synthesized using hen’s eggshell as calcium source and phosphoric acid by precipitation method. Conventional EDTA titration and gravimetric methods were adopted to estimate the amount of calcium and phosphorous, respectively. Fourier-transform infrared (FT-IR) and X-ray diffraction (XRD) techniques were employed to investigate the formation of the HAP phase. Thermal analysis (TG-DTA) was carried out to investigate the thermal stability of HAP powder. FT-IR spectra show the characteristic peaks for phosphate and hydroxyl groups. XRD results reveal that the major characteristic peaks of HAP appear in the region of approximately 26°, 28°, 29°, 30–35°, 39°, 46°, 49° and 50° (2θ) and also indicate that there are no occurrences of secondary phases during HAP formation. TG-DTA result depicts that the synthesized HAP was stable up to 1300°C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Asada M, Oukami K, Nakamura S and Takahashi K 1987J. Ceram. Soc. Jap. 95 703
Cowin S C, Vanburskirk W C and Ashaman R B 1987Hand- book of bioengineering (eds) R Skalak and S Chien (New York: McGraw-Hill)
Fowler B O 1974Inorg. Chem. 13 207
Koumoulidis G C, Vaimakia T C, Sdoukos A T, Boukos N K and Trapalis C C 2001J. Am. Ceram. Soc. 84 1203
Liu Changsheng, Huang Yue, Shen Wei and Cui Jinghua 2001Biomaterials 22 301
Milev A, Kannangara G S K and Ben-Nissan B 2003Mater. Lett. 57 2003
Monma H and Kamiyua V 1987J. Mater. Sci. 22 4247
Osaka A, Miura Y, Takeuchi K, Asada M and Takahashi K 1991J. Mater. Sci. Mater. Med. 2 51
Sada V, Kumazawa V and Murakami Y 1991Chem. Eng. Comm. 103 57
Senya I and Akira O 1987J. Ceram. Soc. Jap. 95 759
Simpson D R 1968Am. Miner. 53 1953
Sinha Amit, Ingle A, Munim K R, Vaidya S N, Sharma B P and Bhisey A N 2001Bull. Mater. Sci. 24 653
Stoch A, Jastrzebski W, Brozek A, Stoch J, Szaraniec J, Trybalska B and Kmita G 2000J. Mol. Struct. 555 375
Takeo H, Yasuhiko I and Hiroshi I 1987J. Ceram. Soc. Jap. 95 825
Takeo H, Yasuhiko H and Murakami Y 1989J. Mater. Sci. Lett. 8 305
Yoshio M, Kazuo M and Sumio S 1990J. Ceram. Soc. Jap. 98 1255
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Prabakaran, K., Balamurugan, A. & Rajeswari, S. Development of calcium phosphate based apatite from hen’s eggshell. Bull Mater Sci 28, 115–119 (2005). https://doi.org/10.1007/BF02704229
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02704229