The effect of air dielectric barrier discharge plasma treatment on the chemical structure and morphology of polypropylene (PP) film was studied using UV-VIS (ultraviolet-visible), FT-IR, (Fourier transform infrared), SEM (scanning electron microscopy) and AFM (atomic force microscopy). Polypropylene samples were printed using solvent-based gravure ink. An evaluation of the print quality criteria of the treated PP films included measurement of print density and print gloss. SEM investigated the ink laydown on the modified PP film. The results showed that after a few seconds of plasma treatment, both the surface energy and the surface roughness of the treated PP film increased. There was an increase in the absorbance at the almost-visible range, and C=C and C=O bands were found after the air discharge plasma treatment. A short plasma treatment of 15 seconds was found to bring about a dramatic increase in the print density readings, but a decrease in print gloss. The time of the air discharge plasma treatment was found to have no effect on the print density or print gloss at a high ink film thickness. The results showed that air dielectric barrier discharge plasma treatment, for a few seconds, is effective in printing and is economical for industrial use (this will be studied in detail in future work).
Résumé
On a étudié l’effet du traitement par plasma d’air obtenu par décharge à barrière diélectrique sur la structure chimique et sur la morphologie de films polypropylène (PP) grâce à l’ultraviolet visible (UV-VIS), à l’infrarouge par transformée de Fourier (FT-IR), à la microscopie électronique à balayage (SEM) et à la microscopie à-force atomique (AFM). Des échantillons de polypropylène ont été imprimés en utilisant de l’encre de gravure au solvant. Une évaluation des critères pour la qualité d’impression des films PP traités comprenait la mesure de la densité de l’éncre aussi bien que celle du brillant de l’impression. La déposition de l’encre sur le film modifié a été investiguée par SEM. Les résultats ont montré, qu’après quelques secondes de traitement par le plasma, l’énergie de surface, aussi bien que la rugosité de la surface du film PP traité, ont augmenté. L’absorbance a augmenté dans la gamme presque visible et des bandes C=C et C=O ont été trouvées après le traitement par le plasma d’air obtenu par décharge à barrière diélectrique. On a trouvé qu’un court traitement, de 15 secondes, par le plasma a augmenté d’une manière dramatique les mesures de la densité de l’encre mais a diminué le brillant de l’impression. On a trouvé que la durée du traitement par plasma d’air obtenu par décharge à barrière diélectrique n’avait ni deffet sur la densité de l’impression ni d’effet sur le brillant de l’impression quand le film d’encre était d’une épaisseur élevée. Les résultats ont montré que le traitement par le plasma d’air obtenu par dêcharge à barrière diélectrique, quand il s’agit d’une duree de quelques secondes, est efficace pour ce qui est de l’impression et rentable pour ce qui est de son usage commercial. (Ce dernier sera étudié minutieusement dans une œuvre future.)
Zusammenfassung
Der Effekt einer Luft-dielektrisch behinderten barrierenentladenem Plasmabehandlung (“Plasma-Printing”) auf die chemische Struktur und Morphologie eines Polypropylenfilms (PP) wurde mittels UV-Sichtbar Spektroskopie (UV-VIS), FT-IR Spektroskopie, Scan-Elektron-Mikroskopie (SEM) und Rasterkraft-Mikroskopie (AFM) erforscht. Die Druckeignung der behandelten PP-Filme wurde bewertet, insbesondere die Druckdichte und der Glanz sowie — mittels SEM — die Tintenniederlegung. Die Ergebnisse — bei Verwendung von lösungsmittelhaltigen Gravurtinten — zeigten, daß ein paar Sekunden Plasmabehandlung sowohl die Oberflächenenergie als auch die Obverflächenrauheit des behandelten Filmes erhöhte. Die Plasmabehandlung erhöhte die Absorptionskraft des Filmes im fast-sichtbaren Bereich sowie in der C=C und C=O Breite. Eine kurze Plasmabehandlung von 15 Sekunden erzielte einen dramatischen Anstieg der Druckdichte, aber eine Verringerung des Glanzes. Bei dicken Tintenfilmen hatte die Länge der Plasmabehandlung keinen Einfluß mehr auf die Druckdichte und den Glanz. Die Ergebnisse zeigten aber daß eine kurze Plasmabehandlung von ein paar Sekunden eine effektive Druckmethode ist und in der Industrie kostengünstig angewendet warden kann (eine weitere Arbeit wird sich mit dieser Frage eingehender beschäftigen).
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Prinz E and F Forster, ‘Surface tension measurements on plastics under practical conditions’,Coating,27, (9), 309–11, 1994
Rease D E, ‘The challenges of printing plastic packaging films’,Felxo,18, (3), 14, 16, 19, 27, 1993
Millward J, ‘A trick to treat?’,Package Print,48, (1), 40, 42, 44–5, 2001
Menges G, W Michaeli, R Ludwig and K Scholl, ‘Corona treatment of polypropylene films’,Kunstst Ger Plast,80, (11), 1245–9, 1990
Breard D, ‘Polyolefin’s surface energy and screen printing, Part 2’,Screen Print,91, (11), 60–4, 2001
Carrino L, G Moroni and W Polini, ‘Cold plasma treatment of polypropylene surface: A study on wettability and adhesion’,J Mater Process Technol,121, 373–82, 2002
Guthrie J T, ‘Pretreatments and their effect on the adhesion of coatings’,Surface Coatings International Part B: Coatings Transactions,85, (B1), 27–33, 2002
Cui N Y and N M D Brown, ‘Modification of the surface properties of polypropylene (PP) film using an air dielectric barrier discharge plasma’,App Surf Sci,189, 31–8, 2002
Middleton W, ‘Using films in labelling is increasing due to developments in surface treatment’,Labels Labelling,19, (6), 100, 1997
Middleton W, ‘Surface treatment pushes filmic label growth’,Packag Rev,24, (6), 24–5, 1998
Strong A, ‘Plastic labels — new design opportunities — dynamic growth’, Proceedings from Europak ′93 Conference at Dusseldorf, Germany, 67–75, 4th to 5th May 1993
Weinberg M L, ‘Under pressure’,Package Print-Converting,43, (11), 28, 30, 32, 35, 1996
Thompson B (ed),Printing Materials: Science and Technology, Pira International, UK, 189–91, 1998, ISBN: 1-85802-150-2
Hanke K, ‘Qualitative evaluation of print’,Druckfarben Echo/Drucklabor,3, 16–21, 1989
Kajanto I M, ‘Pointwise dependence between local grammage and local print density’,Pap Puu,73, (4), 338–45, 1991
ASTM: D2578-94, ‘Standard test method for wetting tension of polyethylene and polypropylene films’,Annual Book of ASTM Standards,08.01, 67–9, 1994
En ISO 2409, ‘Paints and varnishes — cross-cut test (ISO 2409: 1992)’, 1992
Williams R L,Paper and Ink Relationships, 81–4, Mennonite Press Inc, Kansas 67502, 1988
ASTM: D2457-97, ‘Standard test method for specular gloss of plastic films and solid plastics’,Annual Book of ASTM Standards,06.01, 9–13, 1997
Saha A, V Chakraborty and S N Chintalapudi, ‘Chemical modification of polypropylene induced by high energy carbon ions’,J Nucl Instr and Meth in Phys Res B,168, 245–51, 2000
Caiazzo F, P Canonico, R Nigro and V Tagliaferri, ‘Electrode discharge for plasma surface treatment of polymeric materials’,J Mater Process Technol,58, 96–9, 1996
Tripathy S P, R Mishra, K K Dwivedi, D T Khathing, S Ghosh and D Fink, ‘Dose-dependent modification of polypropylene by 62MeV protons’,J Radiation Measurements,35, 95–8, 2002
Brun C, A Chambaudet, C Mavon, F Berger, M Fromm and F Jaffiol, ‘Modification of polypropylene surface properties by alpha ionizing radiation’,J App Surf Sci,157, 85–91, 2000
Upadhyay D J, N Y Cui, C A Anderson and N M D Brown, ‘Surface oxygenation of polypropylene using an air dielectric barrier discharge: The effect of different electrode-platen combinations’,J App Surf Sci,229, 346–52, 2004
De Grace J H and P J Mangin, ‘A mechanistic approach to ink transfer. Part I: Effect of substrate properties and press conditions’,Advances in Printing Science and Technology, (ed) W Banks, Proceedings of the 17th International Conference of Printing Research Institutes, held in Saltsjobaden, Sweden, [London: Pentech Press for IARIGAI, 1984],17, 312–32, June 1983, 1984
Sosa R, ‘Effect of temperature control on gravure packaging inks’,American Ink Maker,77, (10), 121–7, 1999
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Morsy, F.A., Elsayad, S.Y., Bakry, A. et al. Surface properties and printability of polypropylene film treated by an air dielectric barrier discharge plasma. Surface Coatings International Part B: Coatings Transactions 89, 49–55 (2006). https://doi.org/10.1007/BF02699614
Issue Date:
DOI: https://doi.org/10.1007/BF02699614