Both pure TiB2 and carbon/TiB2 composites are potential cathode materials for aluminum reduction cells. An important requirement for this application is that the material be wetted by aluminum in cryolite melts. A sessile drop technique combined with X-ray radiography was used to measure the contact angle formed between aluminum and pure hot-pressed TiB2, carbon/TiB2 composite, graphite, and a carbonaceous cement in cryolite melts. Pure hot-pressed TiB2 was found to be completely wetted by aluminum in cryolite melts. Graphite and the carbonaceous cement were nonwetted by aluminum in cryolite melts, the contact angles being in the range of 144 to 158 deg. The contact angle formed by aluminum on the carbon/TiB2 composite in cryolite melts exhibited time dependency. It was proposed the time dependency was due to (1) removal of contamination from the composite surface and (2) removal of aluminum from the drop. The wettability of the composite material increased as the TiB2 content increased.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J.B. Todd:J. Met., 1981, Sept., pp. 42–45.
K. Grjotheim and B.J. Welch:Aluminium Smelter Technology, Aluminium-Verlag, Dusseldorf, Federal Republic of Germany, 1988.
R.C. Donvard:J. Appl. Electrochem., 1983, vol. 13, pp. 569–75.
Understanding the Hall-Heroult Process for Production of Aluminium, K. Grjotheim and H. Kvande, eds., Aluminium-Verlag, Dusseldorf, Federal Republic of Germany, 1986.
K. Billehaug and H.A. Oye:Aluminium, 1980, vol. 56 (10), pp. 642–48; (11), pp. 713-18.
L.G. Boxall, A.V. Cooke, and H.W. Hayden:Light Metals 1984, AIME, Warrendale, PA, pp. 573–88.
J.T. Gee, K.W. Tucker, L.A. Joo, D.Y. Stewart, T. Alcorn, and A. Tabereaux: U.S. Dept. of Energy Report No. DOE/ID/ 12689-1, 1989, prepared by Great Lakes Research, Elizabethton, TN and Reynolds Metals Company, Sheffield, AL.
C.E. Ransley:J. Met., 1962, vol. 14 (2), pp. 129–35.
S.K. Rhee:J. Am. Ceram. Soc., 1970, vol. 53 (7), pp. 386–89.
G.V. Samsonov, A.D. Pnasyuk, and M.S. Borovikova:Poroshk. Metall., 1973, vol. 6 (126), pp. 51–57.
X. Liao and Y. Liu:Light Metals 1990, AIME, Warrendale, PA, pp. 409–12.
T.A. Utigard: Ph.D. Thesis, University of Toronto, ON, Canada, 1985.
T.A. Utigard and J.M. Toguri:Metall. Trans. B, 1985, vol. 16B, pp. 333–38.
H. John and H. Hausner:J. Mater. Sci. Lett., 1986, vol. 5, pp. 549–51.
R.E. Johnson and R.H. Dettre:Am. Chem. Soc., 1963, no. 43, pp. 112-15.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Watson, K.D., Toguri, J.M. The wettability of carbon/TiB2 composite materials by aluminum in cryolite melts. Metall Trans B 22, 617–621 (1991). https://doi.org/10.1007/BF02679016
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02679016