Abstract
An Al-5.8 at. pct Mg (5.2 wt pct Mg) alloy was deformed in torsion within the solute drag regime to various strains, up to the failure strain of 10.8. Optical microscopy (OM) and transmission electron microscopy (TEM) were used to analyze the evolution of the microstructure and to determine the dynamic restoration mechanism. Transmission electron microscopy revealed that subgrain formation is sluggish but that subgrains eventually (ε ≈ 1) fill the grains. The “steady-state” subgrain size (λ ≈ 6 μm) and misorientation angle (θ ≈ 1.6 deg) are reached by ε ≈ 2. These observations confirm that subgrains eventually form during deformation in the solute drag regime, though they do not appear to significantly influence the strength. At low strains, nearly all of the boundaries form by dislocation reaction and are low angle (θ < 10 deg). At a strain of 10.8, however, the boundary misorientation histogram is bimodal, with nearly 25 pct of the boundaries having high angles due to their ancestry in the original grain boundaries. This is consistent with OM observations of the elongation and thinning of the original grains as they spiral around the torsion axis. No evidence was found fordiscontinuous dynamic recrystallization, a repeating process in which strain-free grains nucleate, grow, deform, and give rise to new nuclei. It is concluded that dynamic recovery in the solute drag regime gives rise togeometric dynamic recrystallization in a manner very similar to that already established for pure aluminum, suggesting that geometric dynamic recrystallization may occur generally in materials with a high stacking-fault energy (SFE) deformed to large strains.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
M.E. Kassner and M.E. McMahon:Metall. Trans. A, 1987, vol. 18A, pp. 835–46.
M.E. Kassner:Metall. Trans. A, 1989, vol. 20A, pp. 2182–85.
M.E. Kassner, N.Q. Nguyen, G.A. Henshall, and H.J. McQueen:Mater. Sci. Eng., 1991, vol. A132, pp. 97–105.
M.E. Kassner, M.M. Myshlyaev, and H.J. McQueen:Mater. Sci. Eng., 1989, vol. A108, pp. 45–61.
H.J. McQueen, E. Evangelista, and M.E. Kassner:Z. Metallkd., 1991, vol. 82, pp. 336–45.
J.K. Solberg, H.J. McQueen, N. Ryum, and E. Nes:Phil. Mag. A, 1989, vol. 60A, pp. 447–71.
H.J. McQueen, J.K. Solberg, N. Ryum, and E. Nes:Phil. Mag. A, 1989, vol. 60A, pp. 473–85.
H.J. McQueen, O. Knustad, N. Ryum, and J.K. Solberg:Scripta Metall., 1985, vol. 19, pp. 73–78.
H.J. McQueen and J.J. Jonas:J. Appl. Metalwork, 1984, vol. 3, pp. 233–41.
H.J. McQueen and J.J. Jonas:J. Appl. Metalwork, 1984, vol. 3, pp. 410–20.
E. Usui, T. Inaba, and N. Shinano:Z. Metallkd., 1986, vol. 77, pp. 684–93.
E. Usui, T. Inaba, and N. Shinano:Z. Metallkd., 1986, vol. 77, pp. 179–87.
M. Raghavan and E. Shapiro:Metall. Trans. A, 1980, vol. 11A, pp. 117–21.
K.J. Gardner and R. Grimes:Met. Sci., 1979, vol. 13, pp. 216–22.
F.J. Humphreys and M.R. Drury:Aluminum Technology, T. Sheppard, ed., Institute of Metals, London, 1986, pp. 191–96.
M.R. Drury and F.J. Humphreys:Acta Metall., 1986, vol. 34, pp. 2259–71.
T. Sheppard, M.B. Tutcher, and H.M. Flower:Met. Sci., 1979, vol. 13, pp. 473–81.
M. Ueki, S. Horie, and T. Nakamura:Aluminum Alloys Physical and Mechanical Properties, E.A. Starke and T.H. Sanders, eds., EMAS, Warley, U.K., 1986, pp. 419–22.
X.Y. An, J.P. Lin, T.C. Lei, and B.T. Yu:Strength of Metals and Alloys, P.O. Kettunen, T.K. Lepisto, and M.E. Lehtonen, eds., Pergamon Press, Oxford, 1989, vol. 2, pp. 971–76.
C.M. Young and O.D. Sherby:Metal Forming: Interpretation between Theory and Practice, A.L. Hoffmanner, ed., Plenum Press, New York, NY, 1971, p. 429.
D.S. Fields and W.A. Backofen:Proc. ASTM, 1957, vol. 57, p. 1259.
N. Matsuno and H. Oikawa:Scripta Metall., 1981, vol. 15, pp. 319–22.
P. Yavari and T.G. Langdon:Acta Metall., 1982, vol. 30, pp. 2181–96.
P. Yavari, F.A. Mohamed, and T.G. Langdon:Acta Metall., 1981, vol. 29, pp. 1495–1507.
G.A. Henshall: Ph.D. Dissertation, Stanford University, Stanford, CA, 1987.
H. Oikawa, K. Honda, and S. Ito:Mater. Sci. Eng., 1984, vol. 64, pp. 237–45.
M.J. Mills, J.C. Gibeling, and W.D. Nix:Acta Metall., 1985, vol. 33, pp. 1503–14.
W.D. Nix and B. Ilschner:Strength of Metals and Alloys, P. Haasen, V. Gerold, and G. Kostorz, eds., 1979, pp. 1503–30.
A. Orlová and J. Cadek:Z. Metallkd., 1974, vol. 65, pp. 200–04.
E. Weckert and W. Blum:Strength of Metals and Alloys, H.J. McQueen, J.-P. Bailon, J.I. Dickson, J.J. Jonas, and M.G. Akben, eds., Pergamon Press, Oxford, 1985, pp. 773–78.
L. Ivanchev and D. Chevdarova:Plasticity and Resistance to Metal Deformation, S. Blecic, ed., University of Titograd, Titograd, Yugoslavia, 1986, pp. 348–61.
T.J. Ginter and F.A. Mohamed:J. Mater. Sci., 1982, vol. 17, pp. 2007–12.
M.A. Morris and J.L. Martin:Acta Metall., 1984, vol. 32, pp. 549–61.
T.R. McNelly, D.J. Michel, and A. Salama:Scripta Metall., 1989, vol. 23, pp. 1657–62.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Henshall, G.A., Kassner, M.E. & McQueen, H.J. Dynamic restoration mechanisms in Al-5.8 At. Pct Mg deformed to large strains in the solute drag regime. Metall Trans A 23, 881–889 (1992). https://doi.org/10.1007/BF02675565
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02675565