Abstract
Al4.5Zn1.5Mg and Al5Mg were reacted in water-vapor saturated air (WVSA) at 120°C and tensile tested. After an initial loss of ductility with exposure time, probably caused by hydrogen embrittlement of the grain boundaries, between 15 hours and 25 hours exposure the mechanical properties of Al4.5Zn1.5Mg improved, this effect being due both to a reduced corrosion activity of the grain boundaries in producing embrittling hydrogen at the external surface and to grain boundary MgZn2 precipitates acting as hydrogen traps. After 25 hours exposure water was shown to penetrate the grain boundaries, and a layered corrosion product identified as the aluminum hydroxides boehmite and diaspore was formed. This resulted in a marked fall of ductility. Re-solution heat treatment and reaging partially recovered the mechanical properties of Al4.5Zn1.5Mg if the exposure time was less than 50 hours, and would not recover properties for longer exposure times. Small additions (0.1 pct) of iron and nickel to Al4.5Zn1.5Mg lessened the grain boundaries’ sensitivity to corrosive attack whereas the addition of 0.1 pct copper did not. Also, the former two additions did not cause the relative ductility increase during 15 to 25 hours exposure in WVSA at 120°C shown by Al4.5Zn1.5Mg. It is proposed that these elements alter the magnesium segregation levels at the grain boundaries which in turn affects their electrochemical attack.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
M. D. Speidel: “Stress Corrosion and Corrosion Fatigue Crack Growth in Aluminium Alloys”, NATO Advanced Study Institute in Stress Corrosion Cracking, Copenhagen, Denmark, 1975.
C. D. S. Tuck and G. M. Scamans: Proc. 2nd Int. Congress on Hydrogen in Metals, Paris, 1977, Paper 4A 11.
P. K. Poulouse, J. E. Moral, and A. J. McEvily:Metall. Trans., 1974, vol. 5, pp. 1393–400.
L. Montgrain, G. M. Scamans, and P. R. Swann:Proc. 3rd Tewkes-bury Symposium on Fracture Processes, C. J. Osborn and R. C. Gifkins, eds., University at Melbourne, Australia, 1974, pp. 194–200.
G. M. Scamans, R. Alani, and P. R. Swann:Jnl. Corr. Sci., 1976, vol. 16, pp. 443–60.
D. Hardie, N. J. H. Holroyd, and R. N. Parkins:Metal Science, 1979, vol. 13, pp. 603–11.
S. P. Lynch:3rd Int. Conference on the Effects of Hydrogen on Behavior of Materials, I. M. Bernstein and A. W. Thompson, eds., TMS-AIME, 1980, pp. 863–71.
S.W. Ciaraldi, J.L. Nelson, R. A. Yeske, and E.N. Pugh:ibid., pp. 437–47.
C.D.S. Tuck:ibid., pp. 503–11.
L. Christodoulou and H. M. Flower:ibid., pp. 493–501.
L. Christodoulou and H.M. Flower:Acta Metall., 1980, vol. 28, pp. 481–87.
G.M. Scamans:Jnl. Mat. Sci., 1978, vol. 13, pp. 27–36.
R. Alani and P.R. Swann:Br. Corros. Jnl., 1977, vol. 12, no. 2, pp. 80–85.
T. Schober:Metall. Trans. A, 1981, vol. 12A, pp. 951–57.
N.J.H. Holroyd and G.M. Scamans:Environment-Sensitive Fracture: Evaluation and Comparison of Test Methods, S. W. Dean, E. N. Pugh, and G.M. Ugiansky, eds., ASTM, Philadelphia, PA, 1984, pp. 202–41.
G.M. Scamans and A. S. Rehal:Jnl. Mat. Sci., 1979, vol. 14, pp. 2459–70.
R. Roy and F. F. Osbom:Amer. Mineral, 1954, vol. 39, pp. 853–85.
R. S. Alwitt: “The Aluminum-Water System”, inOxide and Oxide Films, J.W. Diggle, ed., Marcel Dekker, New York, NY, 1976, vol. 4, pp. 169–254.
M. J. Robinson: “Mechanics of Exfoliation Corrosion in High Strength Aluminium Alloys” presented at Conference “Control and Exploitation of the Corrosion of Aluminium Alloys,” Inst. Corrosion Science and Technology, Cranfield, U.K., 1983.
G. M. Scamans, N. J. H. Holroyd, and C. D. S. Tuck: “The Role of Magnesium Segregation in the Intergranular Stress Corrosion Cracking of Aluminium Alloys,” paper presented at TMS-AIME Fall Meeting, St. Louis, MO, October 1982.
J. M. Chen, T. S. Sun, R.K. Vishwanatham, and J.A.S. Green:Metall. Trans. A, 1977, vol. 8A, pp. 1935–40.
P. Doig and J.W. Edington:Metall. Trans. A, 1975, vol. 6A, pp. 943–45.
T. N. Dymova, Z. K. Zterlyadkina, and V. G. Safronov:Russ. J. Inorg. Chem., 1961, vol. 6, pp. 389–92.
J. Genossar and P. S. Rudman:Zeitschrift f. Phys. Chem. Neue Folge, 1979, vol. 116, pp. 215–24.
M. C. Flemmings:Solidification Processing, McGraw-Hill, New York, NY, 1974, ch. 3, pp. 58–92, ch. 5, pp. 146–48.
C. J. Peel and P. Poole:International Conference on Mechanisms of Environment Sensitive Fracture of Materials, P. R. Swann, F. P. Ford, and A.R.C. Westwood, eds., The Metals Society, London, 1977, pp. 147–57.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Tuck, C.D.S. The embrittlement of Al-Zn-Mg and Al-Mg alloys by water vapor. Metall Trans A 16, 1503–1514 (1985). https://doi.org/10.1007/BF02658682
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02658682