Abstract
Solder joints in electronic packages experience cyclical thermally induced strain when temperature fluctuations are encountered in service. This study investigates three parameters that affect the microstructure and therefore the thermal fatigue behavior of 60Sn-40Pb solder joints. These parameters are: 1) the effect of a tensile component in thermal fatigue, 2) solder joint thickness variations, and 3) hold time variations at the elevated temperature portion of the thermal cycle. Solder joints were thermally fatigued in a tension/compression deformation mode. Cracks developed both in the interfacial intermetallic layer (early in thermal fatigue) and in the coarsened regions of the microstructure of the solder joint (after many more cycles). The effect of joint thickness on solder joints thermally fatigued in shear was also explored. Solder joint thickness was found not to significantly affect fatigue lifetimes. The effect of an increase in the hold time at the elevated temperature portion of the thermal fatigue cycle was also investigated. It was found that time spent at the high temperature end of the fatigue cycle does not determine solder joint lifetime, rather it is the combination of the amount of deformation induced during thermal fatigue in concert with the elevated temperature.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
E. R. Bangs and R. E. Beal, Welding Res. Supp.54, 377s (1975).
J. F. Burgess, R. O. Carlson, H. H.GlascockII, C. A. Neugebauer, and H. F. Webster, IEEECHMT-7, 405 (1984).
E. Levine and J. Ordenez, IEEE Trans. Components, Hybrids, and Manufacturing Tech.,CHMT-4, 515 (1981).
S. K. Kang, N. D. Zommer, D. L. Feucht, and R. W. Heckel, IEEE Trans. Parts, Hybrids, and PackagingPHP-13, 318 (1977).
H. N. Keller, IEEE Trans. Components, Hybrids, and Manufacturing Tech.CHMT-4, 132 (1981).
E. C. Kubik and T. P. L. Li, Microelectronics Center, Martin Marrietta Aerospace, Orlando FL 32855.
J. T. Lynch, M. R. Ford, and A. Boetti, IEEE Trans. Components, Hybrids, and Manufacturing Tech.CHMT-6, 237 (1983).
J. W. Munford, IEEE Trans. Parts, Hybrids, and PackagingPHP-11, 296 (1975).
R. N. Wild,Welding Research Supp. 51, 521s (1972).
E. A. Wright and W. M. Wolverton, Proc. 34th Electron. Components Conf.34, 149 (1984).
H. B. Ellis, Proc. 11th Naval Weapons Electron. Manufacturing Seminar, China Lake, CA 377 (1987).
D. Frear, D. Grivas, M. McCormack, D. Tribula, and J. W. Morris, Jr., Effect of Load and Thermal Histories on Mechanical Behavior, TMS Spring Conf. Denver, CO, 113 (1987).
D. Frear, D. Grivas, M. McCormack, D. Tribula, and J. W.Morris, Jr., Proc. 3rd Ann. Electronic Packaging and Corrosion in Microelectronics Conf.3, 269 (1987).
D. Frear, D. Grivas, and J. W. Morris, Jr., J. Electron. Mater.17, 171 (1988).
P. M. Hall, T. D. Dudderar, and J. F. Argyle, IEEE Trans. Components, Hybrids, and Manufacturing Tech.CHMT-6, 544 (1983).
D. Frear, D. Grivas, L. Quan, and J. W. Morris, Jr., Mat. Res. Soc. Symp.72, 181 (1986).
L. Quan, D. Frear, D. Grivas, and J. W. Morris, Jr., J. Electron. Mater.16, 203 (1987).
D. Tribula, D. Grivas, and J. W. Morris, Jr., submitted to J. Electron. Mater..
H. D.Solomoz, Proc. 38th Electron. Comp. Conf., 38, 7 (207).
H. D. Solomon, private communication.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Frear, D., Grivas, D. & Morris, J.W. Parameters affecting thermal fatigue behavior of 60Sn-40Pb solder joints. J. Electron. Mater. 18, 671–680 (1989). https://doi.org/10.1007/BF02657518
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02657518