The oxides formed on large-grained (∼40 °m) and small-grained (∼4 μm) 304 stainless steel oxidized in air at 800 °C have been examined and compared by Auger electron spectroscopy to learn more about the role of grain boundaries in the oxidation of the materials. For vacuum preannealed specimens, relatively thick iron oxides formed over the grains and thin, chromium-rich oxides formed over grain boudaries of large-grained material. The oxide formed over the entire surface of the small-grained material was a thin chromium-rich layer similar to that formed over grain boundaries of the large-grained samples. The oxidation of both small- and large-grained samples was consistent with selective formation of Cr2O3 at grain boundaries followed by a lateral diffusion of Cr and spreading of Cr2O3. A protective Cr2O3 layer formed readily on small-grained material but not on large-grained material. In contrast to the differences in oxide morphology for small- and large-grained preannealed specimens, oxide morphologies were similar for small- and large-grained material when the outer surface layer was removed by polishing after annealing and before oxidation tests. Surface differences, not adequately defined by Auger and SEM studies, caused marked changes in oxide morphologies for large-grained material. The difference in oxidation behavior before and after polishing was attributed to enhanced oxidation at grain boundaries during the vacuum preannealing treatment and to differences in defect concentrations in the surface region.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
M. D. Merz:Met. Trans. A., 1979, vol. 10A, p. 71.
A. J. Sedriks:Corrosion of Stainless Steels, p. 242, John Wiley and Sons, New York, NY, 1979.
B. Chattopadhyay and G. C. Wood:J. Eleclrochem. Soc, 1970, vol. 117, p. 1163.
C. S. Giggins and F. S. Pettit:Trans. TMS-AIME, 1969, vol. 245, p. 2495.
C. S. Giggins and F. S. Pettit:Trans. TMS-AIME, 1969, vol. 245, p. 2509.
J. C. Kolleen, A. E. Smith, and R. K. Wild:Corros. Sci., 1976, vol. 16, p. 551.
C. T. H. Stoddart and E. D. Hondros:Nat. Phys. Sci., 1972, vol. 237, p. 90.
G. Betz, G. J. Wehner, and L. Toth:J. Appl. Phys., 1974, vol. 45, p. 5312.
L. E. Davis, N. C. MacDonald, P. W. Palmberg, G. E. Riach, and R. E. Weber:Handbook of Auger Electron Spectroscopy, Physical Electronics Industries, Eden Prairie, 1976.
G. Ertl and K. Wandett:Surf. Sci., 1975, vol. 50, p. 479.
G. C. Allen and R. K. Wild:J. Electron. Spectres. Relat. Phenom., 1974, vol. 5, p. 409.
M. Seo, J. B. Lumsden, and R. W. Staehle:Surf. Sci., 1975, vol. 50, p. 541.
T. B. Reed:Free Energy of Formation of Binary Compounds, MIT, Cambridge, MA, 1971.
R. K. Wild:Corros. Sci., 1974, vol. 14, p. 575.
L. J. Weirick: SCL-DC-7220091, Sandia Laboratories, Livermore, CA, 1973.
M. Warzee, J. Hennaut, M. Maurice, C. Sonnen, and J. Waty:J. Electrochem. Soc, 1975, vol. 112, p. 670.
V. R. Howes:Corros. Sci, 1970, vol. 10, p. 99.
J. Webber:Corros. Sci., 1976, vol. 16, p. 499.
R. K. Wild:Corros. Sci., 1977, vol. 17, p. 87.
V. R. Howes:Corros. Sci., 1968, vol. 8, p. 729.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Baer, D.R., Merz, M.D. Differences in oxides on large-and small-grained 304 stainless steel. Metall Trans A 11, 1973–1980 (1980). https://doi.org/10.1007/BF02655116
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02655116