Abstract
A series of heat treatments were performed to study the sensitization and the stress corrosion cracking (SCC) behavior of INCONEL Alloy 690. The microstructural evaluation and the chromium depletion near grain boundaries were carefully studied using analytical electron microscopy (AEM). The measured chromium depletion profiles were matched well to the calculated results from a thermodynamic/kinetic model. The constant extension rate test (CERT) was performed in the solution containing 0.001 M sodium thiosulfate (Na2S2O3) to study the SCC resistance of this alloy. The Huey test was also performed in a boiling 65 pct HNO3 solution for 48 hours to study the intergranular attack (IGA) resistance of this alloy. Both tests showed that INCONEL 690 has very good corrosion resistance. It is believed that the superior IGA and SCC resistances of this alloy are due to the high chromium concentration (≈30 wt pct). It is concluded in this study that INCONEL 690 may be a better alloy than INCONEL 600 for use as the steam generator (S/G) tubing material for pressurized water reactors (PWR's)
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
O.S. Tatone:Nucl. Eng. Int. (NEL), June 1986, pp. 81–83.
A.J. Sedricks, J.W. Schultz, and M.A. Cordovi:Boshoku Gijutsu (Corros. Eng.), 1979, vol. 28, pp. 82–95.
P.H. Berge and J.R. Donati:Nucl. Technol., 1981, vol. 55, pp. 88–104.
G.P. Airey, A.R. Vaia, and R.G. Aspden:Nucl. Technol., 1981, vol. 55, pp. 436–48.
T. Yonezawa, K. Onimura, T. Kusakabe, H. Nagano, K. Yamanaka, M. Inoue, N. Sassaguri, and T. Minami: Mitsubishi Heavy Industries, Ltd., and Sumitomo Metal Industries, Ltd., Takasago, Japan, unpublished research, 1985.
R.A. Page and A. McMinn:Metall. Trans. A, 1986, vol. 17A. pp. 877–87.
B.P. Miglin and C.E. Shoemaker:Corrosion/86, 1986, paper no. 255.
Inconel Alloy 690, Huntington Alloys, Inc., Huntington, WV. 1980.
G. Cliff and G.W. Lorimer:Proc. 5th Europ. Cong. on Electron Microscopy, Institu of Physics, Bristol, U.K., 1992, p. 140.
J.J. Goldstein: inIntroiduction to analytical Electron microcopy. J.J. Hern, J.I. Goldstein, and D.C. Joy, eds., Plenum Press, New York, NY, 1979, ch. 3, pp. 83–120.
N.J. Zaluzec: inIntroduction to Analytical Electron Microcopy. J.J. Hren, J.I. Goldstein, and D.C. Joy, eds., Plenum Press, New York, NY, 1979, ch. 4, opp. 121–67.
J.J. Kai, C.H. Tsai, T.A. Huang, and M.N. Liu:Metall Trans. A., 1989, vol. 20A, pp. 1077–88.
L.H. Wang and T.A. Huang: Department of Nuclear Engineering, National Tsing Hua University, Hsinchu, Taiwan, Republic of China, private communication. 1989.
G.S. Was and R.M. Kruger:Acta Metall., 1985, vol. 33, (5), pp. 841–54.
S.C. Yao and M.N. Liu: Department of Nuclear Engineering. National Tsing Hua Unversity, Hsinchu, Taiwan, Republic of China, private communication, 1987.
G.S. Was, H.H. Tischner, and P.M. Latanision:Metall. Trans. A. 1981, vol. 12A, pp. 1379–408.
E.L. Hall and C.L. Briant:Metall. Trans. A., 1985, vol. 16A, pp. 1225–36.
E.L. Hall and C.L. Briant: Metall. Trans. A. 1984, vol. 15A, pp. 793–811.
C.H. Tsai, J.J. Kai, G.P. Yu, and S.S. Hsu: Department of Nuclear Engineering, National Tsing Hua University, Hsinchu, Taiwan, Republic of China, unpublished research, 1987.
V.B. Rajan and G.S. Was:Corrosion/86, 1986, paper no. 252
J.J. Kai, C.H. Tsai and T.A. Huang,Trans. Am. Nucl. Soc., 1988, vol. 56, pp. 247–49.
R.C. Scarberry, W. Mankins, and M. Pothovey: EPRI Workshop on Thermally Treated Alloy 690 Tubes for Nuclear Steam Generatiors, EPRI, Palo Alto, CA, 1985.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kai, J.J., Yu, G.P., Tsai, C.H. et al. The effects of heat treatment on the chromium depletion, precipitate evolution, and corrosion resistance of INCONEL alloy 690. Metall Trans A 20, 2057–2067 (1989). https://doi.org/10.1007/BF02650292
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02650292