Abstract
Fabrication characteristics of hybrid thin film components are investigated. Lead zirconate titanate (PZT) films, thickness 10 μm, are fabricated by using laser ablation on the Ag electrode (about 1 μm thick) which is deposited on 200 μm Si substrates by evaporation. Composition close to the target material is obtained in PZT films even in air and without substrate heating. Low surface energy in the Ag−Si system causes spheroidization of the Ag layer on the fresh Si substrate, but the surface can be modified by grinding and oxidization. Only some cavities exist at the interface. The interface between the Ag electrode and PZT layer is physically continuous, as revealed by electron microscopy. After annealing at 750°C for 2 h, the PZT layer consists of the rhombohedral perovskite phase with a fraction of the pyrochlore phase. Detrimental interdiffusion between Pb and Si occurs during annealing if the PZT thin film is directly on the Si substrate. This is retarded by the presence of the Ag layer.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
N. Tsuda,JEE 64 (January 1987).
M. Noble and D. W. Kuntz,Laser & Optronics March, 65 (1989).
R.E. Aldlich,Ferroelectrics 27, 19 (1980).
K. Mizumura, Y. Kurihara, H. Ohashi, S. Kumamoto and K. Okuno,Jpn. J. Appl. Phys. 30 (9B) 2271 (1991).
P.M. Leung,Ferroelectrics 28, 355 (1980).
L.T. Li, Y.J. Yao, and Z.N. Mu,Ferroelectrics 28, 40 (1980).
S. Bouwstra, F.R. Blom, T.S.J. Lammerink, H. Yntema, P. Schrap, J.H.J. Fluitman and M. Elwenspoek,Sensors and Actuators 17, 219 (1989).
T. Nakagawa, J. Yamaguchi, T. Usuki, Y. Matsui, M. Okuyalla and Y. Hamakawa,Jpn. J. Appl. Phys. 18, (5), 897 (1979).
T. Hase and T. Shiosaki,Jpn. J. Appl. Phys. 30 (9B) 2159, (1991).
M. Okada, K. Tominaga, T. Araki, S. Katayama and Y. Sakashita,Jpn. J. Appl. Phys. 29 (4), 718 (1990).
G. J. Yi, Y. J. Wu and M. Sayer,J. Appl. Phys. 64 (5) 2717 (1988).
K. Sreenivas and M. Sayer,J. Appl. Phys. 64 (3) 1484 (1988).
S.B. Krupanidhi, N. Maffei, M. Sayer and K. EI-Assal,J. Appl. Phys. 54 (11) 6601 (1983).
R.N. Castellano, and L.G. Feinstein,J. Appl. Phys. 50 (69) 4406 (1979).
A. Okada,J. Appl. Phys. 48 (7) 2905 (1977).
T. Okamura, M. Adachi, T. Shiosaki and A. Kawabata,Jpn. J. Appl. Phys. 30 (5) 1034 (1991).
M. Adachi, T. Matsuzaki, T. Yamada, T. Shiosaki and A. Kawahata,Jpn. J. Appl. Phys. 26 (4) 550 (1987).
R. Takayama and Y. Tomita,J. Appl. Phys. 65 (4) 1666 (1989).
S. Otsubo, T. Maeda, T. Minamikawa, Y. Yonezawa, A. Morimoto and T. Shimizu,Jpn. J. Appl. Phys. 29 (1) L133 (1990).
D. Roy, S.B. Krupanidhi and J.P. Dougherty,J. Appl. Phys. 69(11) 7930 (1991).
L.D. Madsen and L. Weaver,J. Electron. Mater. 21 (1) 93 (1992).
N. Okada, K. Ishikawa, T. Nomura, K. Murakami, S. Fukuoka, N. Nishino and U. Kihara,Jpn. J. Appl. Phys. 30 (9B) 2267 (1991).
Y. Kondoh and T. Ono,Jpn. J. Appl. Phys. 30 (9B) 2260 (1991).
H.X. Zhang, H. Moilanen, A. Uusimäki S. Leppävuori and R. Rautioaho,J. Electron. Mater. 22 (4) 419 (1993).
S. Otsubo, T. Minamikawa, Y. Yonezawa, A. Morimoto and T. Shimizu,Jpn. J. Appl. Phys. 29, (1) L73 (1990).
H. Moilanen, H.X. Zhang, J. Frantti, A. Uusimäki, R. Rautioaho and S. Leppävuori,Actuator (92),Proc. 3rd Int. Conf. New Actuators (June 1992), Bremen, p. 191.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhang, HX., Karjalainen, P., Uusimäki, A. et al. Evaluation of PZT thin films on Ag coated Si substrates. J. Electron. Mater. 23, 1279–1284 (1994). https://doi.org/10.1007/BF02649891
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02649891