Abstract
Unidirectionally reinforced graphite/copper composites have been fabricated using a pressure infiltration casting procedure. T300 and T650 graphite fibers have been used to reinforce copper and copperchromium alloys. The effects of the chromium level in the copper matrix on the tensile strength, stiffness, and thermal expansion behavior of the composites have been evaluated through tensile and three-point bend testing, and thermal cycling. At the 0.5 wt% alloying level, chromium increases the stiffness and optimizes the thermal expansion behavior of graphite/copper composites. The longitudinal tensile strengths of these composites are above 1606 MPa, whereas the transverse tensile strengths are lower than 40 MPa due to incomplete infiltration during processing. Scanning electron microscopy analyses reveal that the unalloyed copper matrix composites experienced extensive fiber/matrix debonding under tensile loading. The addition of chromium to the copper increases the level of matrix bonding to the graphite fibers, as evidenced by observations of fractured tensile specimens. Auger electron spectroscopy analyses indicate that a chromium carbide phase present at the interface is responsible for the improved bonding.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
F. Weitzcr, K. Remschnig, J.C. Schuster, and P. Rogl, Phase Equilibria and Structural Chemistry in the Ternary M-Si-N and M-B-N,J. Muter. Res., Vol 5. 1990, p 2152
D.L. McDanels and J.O. Diaz, “Exploratory Feasibility Studies of Graphite Fiber Reinforced Copper Matrix Composites for Space Power Radiator Panels,” NASA TM-102328, Sep 1989, NASA Lewis Research Center, Cleveland
S.M. De Vincent, “Development of Graphite/Copper Composites Utilizing Engineered Interfaces,” NASA CR-187143, June 1991, NASA Lewis Research Center, Cleveland
M.H. Hural and B.K. Min, The Effects of Matrix Plasticity on the Thermal Deformation of Continuous Fiber Graphite/Metal Com- posites.J. Comp. Mater, Vol 18. 1984. p 519
A. Bartlett and A.G. Evans, Residual Stress Cracking of Met- al/Ceramic Bonds.Acta Metall. Mater, Vol 39, 1991, p 1579
M. Y. He and A.G. Evans, The Strength and Fracture of Metal/Ce- ramic Bonds,Acta Metall. Mater, Vol 39, 1991, p 1587
A. Gupta, A.S. Argon and J.A. Cornie. Interfaces with Controlled Toughness as Mechanical Fuses to Isolate Fibers from Damage,J. Mater. Sci., Vol 24, 1984, p 2031
S.I. Dement’ev, A.A. Zabolotskii. I.V. Romanovich, S.A. Prokof ’ev, and S.E. Salibekov, Reaction of Carbon Fibers with Magnesium, Translated fromPorosh. Metall., Vol 3, 1977, p 50
A.J. Cook and P.S. Werner, Pressure Infiltration Casting of Metal Matrix Composites,Mater. Sci. Eng., Vol A144, 1991, p 189
ASTM D 2344, “Standard Test Method for Apparent Interlaminar Shear Strength of Parallel Fiber Composites by Short-Beam Method,”Annual Book of ASTM Standards, 15.03, American So- ciety for Testing and Materials, 1991, p 43
Wood Handbook: Wood as an Engineering Material, Agriculture Handbook No. 72, 8-2, U.S. Forest Products Laboratory, 1974
S.M. DeVincent and G.M. Michal, Reaction Layer Formation at the Graphite/Copper-Chromium Alloy Interface,Metall. Trans., Jan 1993, in press
“Thermal Expansion—Nonmetallic Solids,”Thermophysical Properties of Matter, Vol 13, IFI/Plenum Press, 1977, p 77–79
“Thermal Expansion—Nonmetallic Solids,”Thermophysical Properties of Matter, Vol 13, IFI/Plenum Press, 1977, p 845–847
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
DeVincent, S.M., Michal, G.M. Improvement of thermal and mechanical properties of graphite/copper composites through interfacial modification. JMEP 2, 323–331 (1993). https://doi.org/10.1007/BF02648818
Issue Date:
DOI: https://doi.org/10.1007/BF02648818