Abstract
The mechanisms of plastic fracture (dimpled rupture) in high-purity and commercial 18 Ni, 200 grade maraging steels and quenched and tempered AISI 4340 steels have been studied. Plastic fracture takes place in the maraging alloys through void initiation by fracture of titanium carbo-nitride inclusions and the growth of these voids until impingement results in coalescence and final fracture. The fracture of AISI 4340 steel at a yield strength of 200 ksi (1378 MN/mm2) occurs by nucleation and subsequent growth of voids formed by fracture of the interface between manganese sulfide inclusions and the matrix. The growth of these inclusion-nucleated voids is interrupted long before coalescence by impingement, by the formation of void sheets which connect neighboring sulfide-nucleated voids. These sheets are composed of small voids nucleated by the cementite precipitates in the quenched and tempered structures. The sizes of non-metallic inclusions are an important aspect of the fracture resistance of these alloys since the investigation demonstrates that void nuclea-tion occurs more readily at the larger inclusions and that void growth also proceeds more rapidly from the larger inclusions. Using both notched and smooth round tensile specimens, it was demonstrated that the level of tensile stress triaxiality does not effect the void nu-cleation process in these alloys but that increased levels of triaxial tension do result in greatly increased rates of void growth and a concomitant reduction in the resistance to plastic fracture.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. R. Low, Jr.:Prog. Mater. Sci., 1963,vol. 12, no. l, pp. 1–96.
C. P. Sullivan:Welding Research Council Bulletin No. 122,1967.
B. I. Edelson and W. M. Baldwin, Jr.:Trans. ASM, 1962, vol. 55, pp. 230–50.
A. G. Franklin and W. J. McG. Tegart:J. Iron Steel Inst., 1964, vol. 202, pp. 588–92.
A. J. Birkle, R. P. Wei, and G. E. Pellissier:Trans. ASM, 1966, vol. 59, pp. 981- 90.
R. Kiessling and N. Lange:Non-Metallic Inclusions in Steel, Part II, p. 97, Iron and Steel Institute, London, 1966.
T. Boniszewski and E. Boniszewski:J. Iron Steel Inst., 1966, vol. 204, pp. 360- 65.
R. T. DeHoff and F. N. Rhines:Quantitative Microscopy, p. 128, McGraw- Hill, New York, 1968.
R. T. DeHoff and F. N. Rhines:Trans. TMS-AIME, 1961, vol. 221, pp. 975–82.
F. C. Hull and W. J. Houk:Trans. AIME, 1953, vol. 197, pp. 565–72.
A. J. Baker, F. J. Lauta, and R. P. Wei:ASTM STPNo. 370, 1965, pp. 3-28.
A. W. Dana, E. L. Aul, and G. Sachs:NACA Tech. Note No. 1830, Cleveland, Ohio, 1949.
S. Floreen and H. W. Hayden:Met. Sci. J., 1970, vol. 4, pp. 77–80.
W. Weibull:Igeniors Vetenskaps Akademien, Hondlinger No. 151, Stockholm, 1939.
P. W.Bridgman:Large Plastic Flow and Fracture, p. 9, McGraw-Hill, New York, 1952.
H. C. Chao and L. H. Van Vlack:Trans. TMS-AIME, 1965, vol. 233, pp. 1227- 31.
H. C. Chao and L. H. Van Vlack:Mat. Res. Stan., 1965, vol. 5, pp. 611–13.
L. E. Wood and L. H. Van Vlack:Trans. ASM, 1963, vol. 56, pp. 770–72.
H. C. Chao, L. Thomassen, and L. H. Van Vlack:Trans. ASM, 1964, vol. 57, pp. 386–98.
C. Zener:Elasticity and Anelasticity, p. 133, University of Chicago Press, Chicago, 1948.
E. E. Underwood:Quantitative Stereology, p. 29, Addison-Wesley, Reading, Mass., 1970.
S. Floreen and H. W. Hayden:Scripta Met., 1970, vol. 4, pp. 87–94.
H. Darlington:Ductile Fracture Under Axisymmetric Stresses in Electrolytic Iron and Spheroidized Low-Carbon Steel, Ph.D. Thesis, Lehigh University, 1971.
J. Gurland and J. Plateau:Trans. ASM, 1963, vol. 56, pp. 442–54.
P. Feltham and A. S. Beyron:Phil. Mag., 1966, vol. 13, pp. 311–16.
J. R. Rice and D. M. Tracey:J. Mech. Phys. Solids, 1969, vol. 17, pp. 201–17.
F. A. McClintock:Ductility, p. 255, ASM, Metals Park, Ohio, 1968.
F. A. McClintock:J Appl. Mech., 1968, vol. 35, pp. 363–71.
H. C. Rogers:Trans. TMS-AIME, 1960, vol. 218, pp. 498–506.
L. Roesch and G. Henry:ASTM STP453, 1969, pp. 3-35.
J. J. Hauser and M. G. H. Wells: Air Force Mat. Lab. Tech. Rep. AFML-TR- 69-339, 1970.
J. J. Hauser, M. G. H. Wells, and I. Perlmutter:J. Vac. Sci. Tech., 1972, vol. 9, p. 1339.
L. F. Porter:J. Vac. Sci. Tech., 1972, vol. 9, pp. 134044.
M. J. May and D. J. Latham:Toward Improved Ductility and Toughness, p. 157, Climax Molybdenum Development Company, Japan, 1971.
R. A. Grange:Trans. ASM, 1966, vol. 59, pp. 2648.
D. Broek:Eng. Fract. Mech., 1970, vol. 1, pp. 691–95.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Cox, T.B., Low, J.R. An investigation of the plastic fracture of AISI 4340 and 18 Nickel-200 grade maraging steels. Metall Trans 5, 1457–1470 (1974). https://doi.org/10.1007/BF02646633
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF02646633