Abstract
The effects of slip character and grain size on the intrinsic material and extrinsic closure contributions to fatigue crack growth resistance have been studied for a 7475 aluminum alloy. The alloy was tested in the underaged and overaged conditions with grain sizes of 18 μm and 80 μm. The fracture surface exhibited increased irregularity and planar facet formation with increased grain size, underaging, and tests in vacuum. These changes were accompanied by an increased resistance to fatigue crack growth. In air the 18 μm grain size overaged material exhibited relatively poor resistance to fatigue crack growth compared with other microstructural variants, and this was associated with a lower stress intensity for closure. All materials exhibited a marked improvement in fatigue crack growth resistance when tested in vacuum, with the most significant difference being ˜1000× at a ΔK of 10 MPa m1/2 for the 80 μm grain size underaged alloy. This improvement could not be accounted for by either an increase in closure or increased crack deflection and is most likely due to increased slip reversibility in the vacuum environment. The intrinsic resistance of the alloy to fatigue crack growth was microstructurally dependent in vacuum, with large grains and planar slip providing the better fatigue performance.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. E. Shigley:Mechanical Engineering Design, 1977, McGraw-Hill, New York, NY, p. 179.
R. A. Smith: inFatigue Thresholds, Fundamentals and Engineering Applications, J. Bäcklund, A. F. Blom, and C. J. Beevers, eds., Engineering Materials Advisory Services, Ltd., West Midlands, UK, 1981, vol. I, p. 33.
P. Stenvall: inFatigue Thresholds, Fundamentals and Engineering Applications, J. Bäcklund, A. F. Blom, and C. J. Beevers, eds., Engineering Materials Advisory Services, Ltd., West Midlands, UK, 1981, vol. II, p. 931.
W. Elber.Eng. Fracture Mech., 1970, vol. 2, p. 37.
T. C. Lindley and C. E. Richards:Mat. Sci. Eng., 1974, vol. 14, p. 381.
R. O. Ritchie, S. Suresh, and C. M. Moss:J. Eng. Mat. and Tech., Trans. ASME Series H, 1979, vol. 102, p. 293.
N. Walker and C. J. Beevers:Fat. of Eng. Mat. and Struct., 1979, vol. 1, p. 135.
R. O. Ritchie and S. Suresh:Metall. Trans. A, 1978, vol. 9A, p. 291.
J. Lindigkeit, G. Terlinde, A. Gysier, and G. Lütjering:Acta Metall., 1979, vol. 27, p. 1717.
Fu-Shiong Lin and E. A. Starke, Jr.:Mat. Sci. Eng., 1980, vol. 43, p. 65.
Fu-Shiong Lin and E. A. Starke, Jr.:Mat. Sci. Eng., 1980, vol. 45, p. 153.
Fu-Shiong Lin and E. A. Starke, Jr.: inHydrogen in Metals, A. W. Thompson and I.M. Bernstein, eds., TMS-AIME, Warrendale, PA, 1981, p. 485.
John A. Wert, N. E. Paton, C. H. Hamilton, and M.W. Mahoney:Metall. Trans. A, 1981, vol. 12A, p. 1267.
Edgar A. Starke, Jr.:Strength of Metals and Alloys (ICSMAG), R. C. Gifkins, ed., Pergamon Press, Oxford, 1983, vol. 3, p. 1025.
J. Petit, B. Bouchet, C. Goss, and J. de Fouguet:Fracture, Proc. 4th Int. Conf. on Fracture (ICF4), D. M. R. Taplin, ed., University of Waterloo Press, Waterloo, Canada, 1977, vol. 2, p. 867.
M. D. Holliday and C. J. Beevers:Int. J. of Fracture, 1979, vol. 15, p. R27.
A. K. Vasudévan and S. Suresh:Metall. Trans. A, 1982, vol. 13A, p. 2271.
B. R. Kirby and C. J. Beevers:Fatigue of Eng. Mat. and Structures, 1979, vol. 1, p. 203.
S. Suresh:Metall. Trans. A, 1983, vol. 14A, p. 2375.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Carter, R.D., Lee, E.W., Starke, E.A. et al. The effect of microstructure and environment on fatigue crack closure of 7475 aluminum alloy. Metall Trans A 15, 555–563 (1984). https://doi.org/10.1007/BF02644980
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02644980