Abstract
This paper reports the results of a study exploring the possibility of employing unmodified Kraft (sulphate) lignin as a binder in particle boards manufactured using high frequency (27 MHz) heating. The mechanical parameters of the samples varied substantially with their density. For instance, the modulus of elasticity increased from 2.5 to 6.1 GPa when density changed from 700 to 1200 kg/m3. Similar results were obtained when replacing the lignin component with some thermoplastic binders (PVCAC, PVC, LDPE, PA 11, and an acrylic copolymer).
The water resistance of the samples was relatively low. For instance, a sample containing 20% lignin and having a density of 700 kg/m3 exhibited after 2 h exposure to water a thickness swelling of 40%. With a similar sample containing PVCAC as binder, the corresponding value was 13%. It was possible to reduce the degree of swelling with hydrophobizing additives or by using acetylated wood flakes. An addition of 5% of a polyethylene wax thus reduced the swelling of lignin bound samples to below 5%. Similar results were obtained with PVCAC as binder. Supplementary experiments were carried out with adding hollow microspheres (Expancel) to the material. Reduced swelling was recorded also in this case.
Predictions of the modulus values based on the Halpin-Tsai concept produced a fair degree of agreement with the experimental data, provided the density and the binder content were sufficiently high.
Zusammenfassung
Unmodifiziertes Lignin aus dem Kraft-(Sulfat)-Aufschluß wurde zur Herstellung von Spanplatten mit Hilfe einer Hochfrequenzerhitzung bei 27 MHz verwendet. Die mechanischen Eigenschaften der Proben variierten sehr stark entsprechend ihrer Dichte. Z.B stieg der E-Modul von 2,5 auf 6,1 GPa, wenn die Dichte von 700 auf 1200 kg/m3 erhöht wurde. Ähnliche Ergebnisse wurden erzielt, nachdem die Lignin-Komponente durch einige thermoplastische Harze wie PVCAC, PVC, LDPE, PA 11 und ein Acryl-Copolymer ersetzt wurden. Die Feuchtebeständigkeit der Proben war relativ gering. So wies eine Probeplatte mit 20% Ligninanteil und einer Dichte von 700 kg/m3 eine Dickenquellung von 40% auf. Bei einer ähnlichen Probe, die PVCAC als Bindemittel enthielt betrug die Dickenquellung nur 13%. Die Quellungseigenschaften konnten deutlich verbessert werden durch Zusatz von Hydrophobierungsmitteln. Die Zugabe von 5% Polyethylen- Wachs reduzierte die Quellung der ligninge-bundenen Platten auf unter 5%. Ähnliches gilt für PVCAC. Ergänzende Untersuchungen wurden unter Zugabe von Microballoons (Expancel) durchgeführt. Auch damit konnte die Quellung herabgesetzt werden. Die Berechnung der Festigkeits-eigenschaften nach dem Halpin-Tsai-Modell führte zu einer annehmbaren Übereinstimmung mit den experimentellen Daten, wenn die Dichte und Harzgehalt ausreichend hoch waren.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Cousins, W. J. 1976: Elastic modulus of lignin as related to moisture content. Wood Sci. Technol. 10: 9–17
Estep, H. M. 1954: The use of urea resins glues in radio frequency lumber edge gluing. J. Forest Prod. Res. Soc. June: 138–142
Fahey, D. J. 1976: High-frequency pressing of phenolic-bonded hardboards. Forest Prod. J. 26: 32–33
Halpin, J. C. 1969: Stiffness and expansion estimates for oriented short fiber composites. J. Comp. Mat. 3: 732–734
Halpin, J. C. 1984: Primer on composite materials: analysis. Technomic Publishing Co., Inc., Lancaster, Pennsylvania
Harris, R. A. 1977: Measuring particle alignment in particleboard and predicting selected mechanical properties of oriented boards. Virginia Polytech. Inst. and State Univ., Ph.D. Thesis
Hermans, J. J. 1967: Elastic properties of fiber reinforced materials when the fibers are aligned. Proc. Konigl. Nederl. Akad. van Weteschappen Amsterdam B 70 (1): 1–9
Hill, R. 1965: Theory of mechanical properties of fiber-strengthened material: III self consistent model. J. Mech. Phys. Solids 13: 189–198
Hunt, M. O. 1970: The prediction of the elastic constants of particle board by means of a structural analogy. North Carolina State Univ., Ph.D. Thesis
James, W. L. 1977: Dielectric behavior of Douglas-fir at various combinations of temperature, frequency, and moisture content. Forest Products J. 27: 44–48
Kollmann, J. 1955: Dielektrische Eigenschaften der Hölzer, in Landolt-Börnstein. 4: 205–212
Kröner, K.;Pungs, L. 1952: Zur dielektrischen Anisotropie des Naturholzes im grossen Frequenzbereich. Holzforschung 1: 13–16
Lee, W. K. 1977: Internal geometry of particleboard and its in-plane elastic constants. Univ. of Washington, Ph.D. Thesis
Lin, R. T. 1967: Review of the dielectric properties of wood and cellulose. Forest Prod. J. 17: 61–66
Lyon, D.;Short P. H.;Lehmann, W. F. 1980: Minimizing press time for radiofrequency-cured flakeboard. Forest Prod. J. 30: 33–38
Mackenzie, K. J. 1987: Encyclopedia of Polymer Sci. and Eng. 2 ed. vol. 15: 160
Mann, W. J. 1954: Some fundamentals of high frequency gluing. J. Forest Prod. Res. Soc. Dec.: 16–18
Menges, G.;Reichstein, H.;Beiss, K. 1980: Neue Verfahren zur Verarbeitung von Kunststoffen auf Basis der Mikrowellenerwärmung. Plastverarbeiter 31: 719–722
Miller, G. M.;Cole, T. J. S. 1957: The dielectric properties of resin glues for wood. Forest Products J. Oct.: 345–352
Miller D. G.;George, P. 1965: Causes of radio frequency burns in edge glued joints. ibid. Jan: 33–36
Nanassy, A. J. 1970: Overlapping of dielectric relaxation spectra in oven-dry yellow birch at temperatures from 20 to 100°C. Wood Sci. Techn. 4: 104–121
Stevens, R. R.;Woodson, G. E. 1977: High-frequency and hot-platen curing of medium-density fiberboards. Forest Prod. J. 27: 46–50
Swedish Pat. Appl. 78.0559-7, Swedish Pat Appl. 86.01453-7 DE-AS 21.13.763
Trapp, W.;Pungs, L., 1956: Einfluss von Temperatur und Feuchte auf das dielectrische Verhalten von Naturholz im grossen Frequenzbereich. Holzforschung. 5: 144–150
Tsai, S. W.;Pagano, N. J. 1968: Invariant properties of composite materials. Composite Materials Workshop, Tsai, S. W.; Halpin, J. C.; Pagano, N. J. (eds.): 233–253, Technomic Publishing Co., Stamford, CT
Yavorsky, J. M. 1954: The effects of moisture content and machining of wood on R.F. gluing processes. J. Forest Prod. Res. Soc. Feb.: 36–39
Venkateswaran, A. 1972: A comparison of the electrical properties of milled wood, milled wood cellulose, and milled wood lignin. Wood Science. 4: 248–253
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mathiasson, A., Kubát, D.G. Lignin as binder in particle boards using high frequency heating. Holz als Roh-und Werkstoff 52, 9–18 (1994). https://doi.org/10.1007/BF02615010
Issue Date:
DOI: https://doi.org/10.1007/BF02615010