Abstract
Extractives were taken from the bark of Pinus halepensis, using water, 1% NaOH and 5% NaOH (with and without sulfonation), with resultant extract yields higher for the NaOH extracts than for those with water only. The NaOH extracts, however, showed lower reactivity. 30 days' storage in liquid or solid form had little influence on their viscosity, pH value and reactivity. At 33% concentration and pH's of 4 to 12 extracts done with water (with and without sulfonation) and with 1% NaOH solution (with sulfonation) showed high reactivity to formaldehyde. Extracts at pH 7 to 8 had short gelation times and longer ones at pH 4 (water extraction) and pH 10 (extraction with 1% NaOH solution, with sulfonation). The remaining three extracts proved unsuitable for further use as bonding agents, either due to their high viscosity or to their inability to cure. With the use of paraformaldehyde as hardener gelation times tended to become longer.
Zusammenfassung
Die Rinde von Pinus halepensis wurde mit Wasser, 1% NaOH und 5% NaOH (mit und ohne Sulfitierung) extrahiert, was zu höherer Extraktstoffausbeute führt als die reine Wasserextraktion. Die mit NaOH gewonnenen Extrakte zeigen jedoch niedrigere Reaktivitäten. Nach 30 Tagen Lagerung waren ihre Viskosität, pH-Wert und Reaktivität nur wenig verändert. Bei 33% Konzentration und pH 4 bis 12 zeigten die mit Wasser (mit und ohne Sulfitierung) und die mit 1% NaOH-Lösung (mit Sulfitierung) gewonnenen Extrakte hohe Reaktivität gegenüber Formaldehyd. Extrakte bei pH 7 bis 8 zeigten kurze, bei pH 4 (Extraktion mit Wasser) und bei pH 10 (Extraktion mit 1% NaOH-Lösung mit Sulfitierung) längere Gelierzeiten. Die übrigen drei Extrakte sind für eine weitere Verwertung als Bindemittel ungeeignet, entweder wegen ihrer hohen Viskosität oder ihrer Unfähigkeit, zu härten. Bei Verwendung von Paraformaldehyd als Härter werden die Gelierzeiten länger.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Literature
Anderson, B.A.; Breuer, J.R.; Nicholls, A.G. 1961: Bonding particle-boards with bark extracts. Forest Prod. J. 11:226–227
Ayla, C.; Weissmann, G. 1981: Verwendung der Polyphenole aus der Rinde von Pinus brutia Ten. zur Herstellung von Holzleimen. Holz Roh-Werkstoff 39:91–95
Chen, M.C. 1982a: Copolymer resins of bark and agricultural residue extracts with phenol and formaldehyde: 40 percent weight of phenol replacement. Forest Prod. J. 32:14–18
Chen, M.C. 1982b: Effects of extraction on the quantity of formaldehyde requirement in reaction of extractives of bark and agricultural residues with formaldehyde. Holzforschung 36:65–70
Dalton, L.K. 1950: Tannin-formaldehyde resins as adhesives for wood. Australian J. Appl. Sci. 1:54–70
Dalton, L.K. 1953: Resins from sulphited tannins as adhesives for wood. Australian J. Appl. Sci. 4:136–145
Dietrichs, H.H.; Garves, K.; Behrensdorf, D.; Sinner, M. 1978: Untersuchungen über die Kohlenhydrate der Rinden einheimischer Holzarten. Holzforschung 32:60–67
Dix, B.; Marutzky, R. 1983: Untersuchungen zur Gewinnung von Polyphenolen aus Nadelholzrinden. Holz Roh-Werkstoff 41: 45–50
Gnamm, H. 1949: Die Gerbstoffe und Gerbmittel. Stuttgart Wiss. Verlagsgesellschaft
Hall, B.R.; Leonard, H.J.; Nicholls, A.G. 1960: Bonding particle-boards with bark extracts. Forest Prod. J. 10:263–272
Herrick, W.F.; Conca, J.R. 1960: The use of bark extracts in cold-setting waterproof adhesives. Forest Prod. J. 10:361–398
Houwink, R.; Salomon, G. 1965: Adhesion and Adhesives. Vol. 1 Adhesives. London: Eslevier Publ. Co.
Liiri, H.; Sairanen, H.; Kilpeläinen, H.; Kivistö, A. 1982: Bark extractives from spruce as constituents of plywood bonding agents. Holz Roh-Werkstoff 40:51–60
Plomley, K.F.; Gottstein, W.J.; Hillis, E.W. 1957: Tannin-formaldehyde adhesives. C.S.I.R.O. (Australia), Forest Prod. Newsletter No 234, pp 6–8
Roffael, E. 1976: Die Bedeutung der Inhaltsstoffe der Rinde für ihre Verwendung in Spanplatten—1. Mittlg.: Einfluß der Inhaltsstoffe auf die Formaldehydabgabe von Rindenplatten. Holzforschung 30:9–14
Saayman, M.H.; Oatley, A.J. 1976: Wood adhesives from wattle bark extract. Forest Prod. J. 26:27–33
Steiner, R.P.; Chow, S. 1975: Factors influencing western hemlock bark extracts use as adhesives. Rep. VP-X-153. Western Forest Prod. Lab, Vancouver, B.C., Canada
Tišler, V.; Ayla, C.; Weissmann, G. 1983: Untersuchung der Rindenextrakte von Pinus halepensis Mill. Holzforsch. Holzverwert. 35:113–116
Tsoumis, G. 1980: Forest Utilization in Greece. Thessaloniki
Weissmann, G.; Ayla, C. 1980: Untersuchung der Rindenextrakte Pinus brutia Ten. Holz Roh-Werkstoff 38:307–312
Weissmann, G. 1981: Untersuchungen der Rindenextrakte von Picea abies. Holz Roh-Werkstoff 39:457–461
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Voulgaridis, E., Grigoriou, A. & Passialis, C. Investigations on bark extractives of Pinus halepensis Mill. Holz als Roh-und Werkstoff 43, 269–272 (1985). https://doi.org/10.1007/BF02608237
Issue Date:
DOI: https://doi.org/10.1007/BF02608237