Abstract
Two types of Nicalon SiC fibres having different structures have been examined. Their mechanical properties and their microstructures have been studied up to 1300° C. The fall in strength above 1000° C has been shown to be due to the microcrystallization of the fibre structure. Under low loads this change in structure led to a shrinkage of the fibre. The fibres were found to creep at temperatures above 1000° C when loads greater than a threshold level were applied. The creep of the fibres has been shown to be controlled by the changes which occur to the fibre structure. Degradation of the fibres on heating in air or argon has been shown to depend on SiO2 and free carbon, which have been shown to exist in the fibre.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
G. Simon andA. R. Bunsell,J. Mater. Sci. 19 (1984) 3649.
E. Fitzer andR. Ebi, in “Silicon Carbide 1973”, edited by R. C. Marshall, J. W. Faust Jr and C. E. Ryan (University of South Carolina Press, Columbia, 1973) p. 320.
M. F. Ashby andR. A. Verrall,Acta Metall. 21 (1973) 149.
M. F. Ashby,Scripta Metall. 3 (1969) 837.
R. N. Ghoshtagore andR. L. Coble,Phys. Rev. 143 (1966) 623.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Simon, G., Bunsell, A.R. Creep behaviour and structural characterization at high temperatures of Nicalon SiC fibres. J Mater Sci 19, 3658–3670 (1984). https://doi.org/10.1007/BF02396938
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02396938