Abstract
A combined theoretical and experimental investigation was conducted to assess the suitability of the 10-deg off-axis tensile-test specimen for the intralaminar-shear characterization of unidirectional composites. Composite mechanics, a combined-stress failure criterion and a finiteelement analysis were used to determine theoretically the stress-strain variation across the specimen width and the relative stress and strain magnitudes at the 10-deg plane. Strain gages were used to measure the strain variation across the specimen width at specimen midlength and near the end tabs. Specimens from Mod-I/epoxy. T-300/epoxy, and S-glass/epoxy were used in the experimental program. It was found that the 10-deg off-axis tensile-test specimen is suitable for intralaminar-shear characterization and it, is recommended that it should be considered as a possible standard test specimen for such a characterization.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Abbreviations
- E :
-
normal modulus; subscripts define direction
- F :
-
combined-stress failure-criterion function
- G :
-
shear modulus—intralaminar
- K :
-
coupling coefficient in combined-stress failure-criterion function
- S :
-
uniaxial fracture stress; subscripts define direction
- x, y, z :
-
structural-axes orthogonal coordinate system withx taken along load direction
- 1, 2, 3:
-
material-axes orthogonal coordinate system with 1 taken along fiber direction
- ε:
-
strain; subscripts define type, plane and direction
- θ:
-
orientation angle between structural and material axes measured positive counterclockwise
- θ g :
-
orientation angle locating strain gage from load direction
- σ:
-
stress; subscripts define type, plane and direction
- C :
-
compression
- c :
-
structural-axes property
- g :
-
strain-gage reading
- ℓ:
-
ply (unidirectional composite) property
- S :
-
shear, symmetric
- T :
-
tension
- x, y, z :
-
structural-axes directions
- 1, 2, 3:
-
material-axes directions
References
Bert, C.W., “Experimental Characterization of Composites,”Comp. Mats.,8 Part 2,Chamis,C. C.,ed.,Academic Press,New York,73–133 (1975).
Daniel, I.M. and Liber, T., “Lamination Residual Stresses in Fiber Composites,” ITT Res. Inst. Rep. IITRI-D6073-1 (1975); also NASA CR-134826.
Chamis, C.C., “Failure Criteria for Filamentary Composites,” NASA TN D-5367 (1969).
Chami, C.C., “Failure Criteria for Filamentary Composites”STP 460. Composite Materials: Testing and Design, ASTM, New Orleans, 336–351 (1972).
“Transverse Sensitivity Errors,” Micro-Measurements, Tech. Note 137.
Chamis, C.C., Kring, J.F. and Sullivan, T.L., “Automated Testing Data Reduction Computer Program,” NASA TM X-68050 (1972).
Chamis, C.C. and Sullivan, T.L., “Combined-Load Stress-Strain Relationships of Fiber Composite Laminates,” NASA TM X-71825 (1976).
Daniel, I.M. and Liber, T., “Strain Rate Effects on Mechanical Properties of Fiber Composites,” IIT Res. Inst. Rep. IITRI-D6073-IV (1976); also NASA CR-135087.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chamis, C.C., Sinclair, J.H. Ten-deg off-axis test for shear properties in fiber composites. Experimental Mechanics 17, 339–346 (1977). https://doi.org/10.1007/BF02326320
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02326320