Styrene-acrylonitrile copolymer latex dispersions were prepared using hydrogen peroxide as an initiator by emulsion polymerization. Particle size distributions were determined by measuring the diameter of particles on electron micrographs. The chemical composition of the latex particles was determined by elemental analysis. The stability and electrophoretic behaviour of these latex dispersions against simple inorganic electrolyte has been investigated. The value of the critical coagulation concentration was found to increase with the decrease of the fraction of acrylonitrile in the polymer particles. The value ofStern potential calculated was found to be independent on the chemical composition of polymers. The difference present in the latex stability seems to be mainly due to the difference in the attractive energy between particles, i.e., theHamaker constant increases almost linearly with the increase of the content of acrelonitrile in the copolymer.
Zusammenfassung
Styrol-Acrylnitril-Mischpolymer-Latices wurden unter Verwendung von Wasserstoffperoxyd als Initiator von Emulsionspolymerisation hergestellt. Verteilungen der Partikelgrößen wurden durch !Messen des Teilchen-Durchmessers auf Elektronenmikrographien bestimmt. Die chemische Zusammensetzung der Latex-Teilchen wurde durch Elementar-Analyse festgestellt. Stabilität und elektrophoretische Beweglichkeit dieser Latex-Dispersionen gegen einfache inorganische Elektrolytlösungen wurden untersucht. Der Wert der kritischen Koagulationskonzentration nahm mit abnehmendem Anteil von Acrylnitril in den Polymer-Partikeln zu. Der Wert desStern Potentials war unabhängig von der chemischen Zusammensetzung der Polymere. Der Unterschied in der Stabilität scheint vorwiegend auf den Unterschied der Anziehungsenergie zwischen Partikeln zurückgeführt werden zu können, d. h. dieHamaker Konstante nimmt beinahe geradewegs mit der Zunahme des Gehaltes von Acrylnitril im Mischpolymer zu.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Ottewill, R. H. andD. J. Wilkins, Trans Faraday Soc.58, 608 (1962).
Johnson, G. A., J. Goldfarb andB. A. Pethica, Trans. Faraday Soc.61, 2321 (1965).
Ottewill, R. H. andJ. N. Shaw, Discussions Faraday Soc.42, 154 (1966).
Ottewill, R. H. andJ. N. Shaw, J. Colloid & Interface Sci.26, 110 (1968).
Kotera, A., K. Furusawa andK. Kudo, Kolloid-Z. u. Z. Polymere240, 837 (1970).
Ottewill, R. H. andT. Walker, Kolloid-Z. u. Z. Polymere227, 108 (1968).
Deželić, N., J. J. Petres andGj. Deželić, Kolloid-Z. u. Z. Polymere242, 1142 (1970).
Kerker, M., H. E. Bowman andE. Matijević, Trans. Faraday Soc.56, 1039 (1960).
Ono, H.,E. Jidai andK. Shihayama, to be published in Kolloid-Z. u. Z. Polymere.
Oster, G., J. Colloid Sci.2, 291 (1947).
Reerink H. andJ. Th. G. Overbeek, Discussions Faraday Soc.18, 74 (1954).
Visser, J., Advan. Colloid Interface Sci.3, 331 (1972).
Overheek, J. Th. G., Kolloid-Beih.54, 287 (1943).
Author information
Authors and Affiliations
Additional information
With 8 figures and 5 tables
Rights and permissions
About this article
Cite this article
Ono, H., Sato, F., Jidai, E. et al. Studies on the stability of styrene-acrylonitrile copolymer latex dispersions. Colloid & Polymer Sci 253, 538–543 (1975). https://doi.org/10.1007/BF01753957
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01753957