Swelling effects of carbon tetrachloride on the mechanical relaxations in the crystal mat and the melt-crystallized samples of high density polyethylene were studied using a torsion pendulum. A very strongα-relaxation peak appears by swelling at the low temperature side of the originalα-relaxation for the crystal mat. It was shown that this strongα-relaxation originates from the slippage between the highly swollen lamellae. For the melt-crystallized sample, theα-relaxation peak is decreased by swelling, but its temperature is unchanged. This behavior suggests that theα-relaxation in the melt-crystallized sample originates mainly from deformation process of intermosaic block region. The swelling effect onγ-relaxation was also discussed.
Zusammenfassung
Quellungseffekte von Tetrachlorkohlenstoff auf das mechanische Relaxationsverhalten in Einkristall-Matten und schmelzkristallisierten Proben von linearem Polyäthylen wurden mit den Torsionspendeln untersucht. Ein sehr starkesα-Maximum tritt durch die Quellung bei tieferen Temperaturen als der derα-Relaxation in den nicht gequollenen Einkristall-Matten auf. Es wird gezeigt, daß diese starkeα-Relaxation auf das Gleiten der ausreichend gequollenen Lamellen zurückzuführen ist. Bei schmelzkristallisierten Proben wird dasα-Maximum durch die Quellung erniedrigt, seine Temperaturlage wird jedoch nicht verändert. Dies zeigt, daß dieα-Relaxation in der schmelzkristallisierten Probe hauptsäcblich auf Deformations-Prozessen in den Blöcken beruht. Auch die Quellungseffekte auf dieγ-Relaxationen wurden diskutiert.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
For example,J. A. Sauer, J. Polym. Sci. Symp., No.32, 69 (1971).
Hideshima, T., Prog. Polym. Phy. Japan9, 279 (1965).
Illers, K. H., Kolloid-Z. u. Z. Polym.231, 622 (1969).
Inamura, I., H. Ochiai, H. Yamaura, J. Polym. Sci., Polym. Phys. Ed.12, 2267 (1974).
Sinnott, K. M., J. Appl. Phys.37, 3385 (1966).
Takayanagi, M., Kogyo Kagaku Zasshi73, 1277 (1970), and Pure and Appl. Chem. 15, 555 (1967).
Hoffman, J. D., G. Williams, E. Passaglia, J. Polym. Sci.14, 173 (1966).
Pechhold, W., S. B. Blasenbrey, S. Waerner, Kolloid-Z.189, 14 (1963).
Nakayasu, H., M. Markovitz, D. J. J. Plazek, Trans. Soc. Rheology5, 261 (1961).
Iwayanagi, S., H. Nakane, Abstr. Int. Cong. Rheol. 40 (Kyoto 1968).
McCrum, N. G., E. L. Morris, Proc. Roy. Soc., Ser. A292, 506 (1960).
Hideshima, T., Abstr. Int. Cong. Rheol. 325 (Kyoto 1968).
Wada, Y., K. Tsuge, J. Appl. Phys.1, 64 (Japan 1962).
Kuriyama, I., H. Arai, to be published elsewhere.
Bead, B. E., G. Williams, Trans. Faraday Soc.57, 1979 (1961).
Off, H. G., A. Peterlin, Kolloid-Z. u. Z. Poly.215, 97 (1967).
Udagawa, Y., A. Keller, J. Polym. Sci.,A-2 9, 437 (1971).
Fischer, E. W., A. Peterlin, Makromol. Chem.74, 1 (1964).
Kajiyama, T., T. Okada, A. Sakoda, M. Takayanagi, J. Makromol. Sci., Phys.B 7, 583 (1973).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Arai, H., Kuriyama, I. Swelling effect onα-relaxation in high density polyethylene. Colloid & Polymer Sci 254, 967–971 (1976). https://doi.org/10.1007/BF01516912
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF01516912