Abstract
Particle segregation during transient liquid-phase bonding of aluminium-based metal matrix composite material using copper filler metal was investigated. Segregation was promoted by the slow movement of the solid-liquid interface during isothermal solidification and alumina particles with diameters less than 30 Μm were segregated when the copper foil thickness exceeded 5 and 15 Μm for the base metals examined. When bonding at 853 K, the liquid widths produced using these copper foil thiciknesses were almost identical to the median inter-particle spacing in the base metals investigated. When the amount of liquid formed at the bonding temperature decreased below a critical level, the test specimens broke apart immediately following the joining operation. The minimum film thickness of copper for satisfactory joint strength increased from 0.6 Μm to 2.4 Μm, when the heating rate to the bonding temperature decreased from 1 Ks−1 to 0.01 Ks−1.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
T. ENJO, K. IKEUCHI, Y. MURAKAMI and N. SUZUKI,Trans. JWRI 16 (1987) 285.
T. MOMONO, Private communication, Department of Materials Science and Engineering, Muroran Institute of Technology, Mizumoto, Japan (1993).
A. A. McFAYDEN, R. R. KAPOOR and T. W. EAGAR,Weld. J. 11 (1990) 399s.
K. SHINOZAKI, Private communication, Department of Welding and Production Engineering, Osaka University, Japan (1993).
D. M. STEFANESCU, B. K. DHINDAW, S. A. KACAR and A. MOITRA,Metall. Trans. 19A (1988) 2847.
D. SHANGGUAN, S. AHUJA and D. M. STEFACESCU,ibid. 23A (1992) 669.
H. KOKAWA, C. H. LEE and T. H. NORTH,22A (1991) 1627.
I. TUAH-POKU and T. B. MASSALSKSI,ibid. 19A (1988) 675.
K. SAIDA, Y. ZHOU and T. H. NORTH,J. Mater. Sci. 28 (1993) 1.
J. R. NIEMANN and R. A. GARRETT,Weld. J. 51 (1974) 175s.
J. R. CAHOON,Metall. Trans. 3 (1972) 1324.
T. B. MASSALSKI, (Ed.) “Binary Alloy Phase Diagrams” (ASM, Metals Park, OH, 1986).
K. IKEUCHI, Y. ZHOU, H. KOKAWA and T. H. NORTH,Metall. Trans. 21A (1992) 2905.
T. H. NORTH, K. IKEUCHI, Y. ZHOU and H. KOKAWA, TMS Symposium, “The Metal Science of Joining”, October 1991, Cincinatti, edited by M. Ciéslack (AIME) pp. 83–91.
H. NAKAGAWA, C.H. LEE and T. H. NORTH,Metall. Trans. 22A (1991) 543.
T. ENJO, K. IKEUCHI, M. ANDO and K. HAMADA,Trans. JWRI 14 (1985) 93.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Li, Z., Zhou, Y. & North, T.H. Counteraction of particulate segregation during transient liquid-phase bonding of aluminium-based MMC material. J Mater Sci 30, 1075–1082 (1995). https://doi.org/10.1007/BF01178448
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01178448