Abstract
An exact theory is developed to describe the evolution of fibre fragmentation in a single-filament composite test as a function of the underlying fibre statistical strength and fibre/matrix interfacial shear stress, τ. The fragment distribution is a complicated function of fibre strength and τ because the stress around breaks which do occur recovers to the applied value, σ, over a length δ(σ) determined by τ. Therefore, no other breaks can occur within δ (σ) of an existing break. To account for this effect, the fibre fragment distribution is decomposed into two parts; fragments formed by breaks separated by more than δ (σ) at stress σ, and fragments smaller than δ (σ) which were formed at some prior stress σ′ < σ when a smaller δ(σ′) < δ(σ) prevailed. The distribution of fragments larger than δ (σ) is identical to that of a fibre with a unique non-statistical strength σ and is known exactly. The distribution of fragments smaller than δ(σ) can then be determined from the distribution of the longer fragments. Predictions of the theory are compared to simulations of fibre fragmentation for several common models of stress recovery around fibre breaks with excellent agreement obtained. The present theory can be utilized to thus derive both thein situ fibre strength at short gauge lengths ≃ δ and the τ from experimentally obtained fragment distributions, and an unambiguous inversion procedure is briefly discussed. The application of the theory to other multiple-cracking phenomena in composites is also discussed.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
R. Gulino andS. L. Phoenix,J. Mater. Sci., in press.
A. N. Netravali, R. B. Henstenburg, S. L. Phoenix andD. Schwartz,Polym. Compos. 10 (1989) 226.
R. B. Henstenburg andS. L. Phoenix,ibid. 10 (1989) 226.
B. Widom,J. Chem. Phys. 44 (1966) 3888.
A. Kelly andW. R. Tyson,J. Mech. Phys. Solids 13 (1965) 329.
A. C. Kimber andJ. G. Keer,J. Mater. Sci. Lett. 1 (1982) 353.
W. A. Fraser, F. H. Ancker, A. T. DiBenedetto andB. Elbirli,Polym. Compos. 4 (1983) 238.
L. T. Drzal, M. J. Rich andP. F. Lloyd,J. Adhesion 16 (1982) 1.
L. T. Drzal, M. J. Rich, M. F. Koenig andP. F. Lloyd,ibid. 16 (1983) 133.
S. H. Own, R. V. Subramanian andS. C. Saunders,J. Mater. Sci. 21 (1986) 3912.
A. Kelly andN. H. MacMillan, “Strong Solids”, 3rd Edn (Clarendon Press, Oxford, 1986) Ch. 6.
H. Scher, private communication.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Curtin, W.A. Exact theory of fibre fragmentation in a single-filament composite. J Mater Sci 26, 5239–5253 (1991). https://doi.org/10.1007/BF01143218
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01143218