Abstract
The ageing behaviour of 3mol% Y2O3-ZrO2 at 100–500° C in a water-containing atmosphere was studied. A critical grain size of ∼ 0.37 μm and a lower temperature limit of ∼80°C for retaining the tetragonal symmetry were deduced from the kinetic study. An “ageing map” constructed on the grain size (G) against ageing temperature (T) plot is proposed to describe the low-temperature ageing behaviour of 3mol% Y2O3-ZrO2.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
T. Sato andM. Shimada,J. Amer. Ceram. Soc. 67 (1984) 212.
Idem, ibid. 68 (1985) 356.
M. Watanabe, S. Iio andI. Fukuura, in “Advances in Ceramics, Vol. 12, Science and Technology of Zirconia(II)”, (edited by N. Claussen, M. Ruhle and A. H. Heuer) American Ceramic Society, Columbus OH, (1984) pp. 391–398.
H. Y. Lu andS. Y. Chen,J. Amer. Ceram. Soc. 70 (1987) 537–41.
S. Y. Chen andH. Y. Lu,J. Mater. Sci. 23 (1988) 1195–1200.
F. F. Lange, G. L. Dunlop andD. I. Davies,J. Amer. Ceram. Soc. 69 (1986) 237.
M. Matsui, T. Soma andI. Oda, in “Advances in Ceramics, Vol. 12, Science and Technology of Zirconia(II)”, (edited by N. Claussen, M. Rhule and A. H. Heuer), American Ceramic Society, Columbus OH, (1984) pp. 371–381.
M. Ruhle, N. Claussen andA. H. Heuer, in “Advances in Ceramics, Vol. 12, Science and Technology of Zirconia(II)”, (edited by N. Claussen, M. Rhule and A. H. Heuer), American Ceramic Society, Columbus OH (1984) pp. 352–369.
H. Y. Lu, H. Y. Lin andS. Y. Chen, “Autocatalytic Effect and Microstructural Development During Ageing of 3 mol % Y2O3-TZP”,Ceram. Intl.,13 (1987) 207–214.
M. Yoshimura, T. Noma, K. Kawabata andS. Somiya,J. Mater. Sci. Lett. 6 (1987) 465–7.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Chen, S.Y., Lu, HY. Low-temperature ageing map for 3mol% Y2O3-ZrO2 . J Mater Sci 24, 453–456 (1989). https://doi.org/10.1007/BF01107426
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01107426