Abstract
In this paper the influence of molecular weight and molecular weight distribution on the tensile strength (tenacity) of melt spun and drawn linear polyethylene are investigated with the aim of outlining the requirements for a high strength fibre. The tenacity was investigated over the molecular weight average ¯M w range 60×103 to 330×103 with polydispersities ¯M w/¯M n ranging from 1.1 to 13.3. It was found that both molecular weight and its distribution affected tensile strength. The drawing conditions were also found to be important, a high draw temperature and a high draw ratio being needed for a high strength, high modulus fibre. By using a polymer of high ¯M w and low polydispersity, and drawing at the optimum conditions, strengths of 1.65 GPa and moduli of 85 GPa have been achieved for test temperatures of −55° C.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
G. Capaccio andI. M. Ward,Nature Phys. Sci. 243 (1973) 143.
Idem, Brit. Patent Appl. 10746 (filed 6 March 1973).
Idem, Polymer 15 (1974) 233.
A. Zwijnenberg andA. J. Pennings,J. Polym. Sci. Polym. Lett. Ed. 14 (1976) 339.
P. Smith andP. J. Lemstra,J. Mater. Sci. 15 (1980) 505.
I. M. Ward,Adv. Polym. Sci. 70 (1985) 1.
P. Smith andP. J. Lemstra,J. Polym. Sci. Polym. Phys. Ed. 19 (1981) 1007.
P. Smith, P. J. Lemstra andJ. P. L. Pijpers,ibid. 20 (1982) 2229.
W. Wu andW. B. Black,Polym. Eng. Sci. 19 (1979) 1163.
P. J. Flory,J. Amer. Chem. Soc. 67 (1945) 2048.
J. B. Smith, G. R. Davies andI. M. Ward,J. Polym. Sci. Polym. Phys. Ed. 13 (1975) 2331.
A. G. Gibson, G. R. Davies andI. M. Ward,Polymer 19 (1978) 683.
D. L. M. Cansfield, I. M. Ward, D. W. Woods, A. Buckley, J. M. Pierce andJ. L. Wesley,Polymer Commun. 24 (1983) 130.
P. L. Clarke, PhD thesis, Leeds (1981).
G. Capaccio, T. A. Crompton andI. M. Ward,J. Polym. Sci. Polym. Phys. Ed. 14 (1976) 1641.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hallam, M.A., Cansfield, D.L.M., Ward, I.M. et al. A study of the effect of molecular weight on the tensile strength of ultra-high modulus polyethylenes. J Mater Sci 21, 4199–4205 (1986). https://doi.org/10.1007/BF01106531
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01106531