Abstract
The effect of temperature and strain-rate on the fracture behaviour during high strain-rate (∼ 103 sec−1) impact of two highly filled polymeric composite propellants (containing segmented polyurethanes based on hydroxy-term inated polybutadiene (HTPB) or glycidyl azide polymer (GAP) filled with ammonium perchlorate (AP) particles) and a plasticized thermoplastic (cast double base (CDB) nitrocellulose-nitroglycerine) propellant have been examined over a wide temperature range encompassing the ⋊ittle-ductile” transition. In the “elastic” region of the loaddisplacement curve, the yield stress and fracture toughness is highest for GAP/AP and lowest for HTPB/AP. In the “elastic” and post-yield “ductile” regions CDB is more fracture-resistant than GAP/AP and HTPB/AP over the temperature range −20 to 50° C, but below −40° C, where both CDB and GAP/AP are brittle, GAP/AP is more fracture-resistant than CDB (as observed in the “elastic” region). Although all the propellants are known to develop small cracks in the “elastic” and post-yield “ductile” regions of the load-displacement curve, the overall fracture behaviour is largely governed by viscoelastic properties (because the cracks close up in compression). The good mechanical properties of CDB, above the “brittle-ductile” transition temperature, can be attributed to the presence of a largeβ-transition loss peak. In the composites, the fracture behaviour is also influenced to a lesser extent by the degree of filler-binder interactions. Dynamic mechanical analysis indicates that GAP/AP has a slightly higher degree of filler-binder interactions than HTPB/AP. A temperature-strain rate reduction has been obtained for the yield stress and the composite curve can be expressed by the equation σy =K 1 +K 2 log (Ġea T ) whereK 1 andK 2 are constants anda T is a shift factor.K 2 is a material constant which reflects the temperature and strain-rate sensitivity.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
C. W. Fong andR. C. Warren,J. Mater. Sci. 20 (1985) 3101.
K. G. Hoge,Appl. Polym. Symp. 5 (1967) 19.
J. Heijboer,J. Polym. Sci.: C 16 (1968) 3755.
P. I. Vincent,Polymer 13 (1972) 558.
P. Kendall,Br. Polym. J. 10 (1978) 35.
G. T. Wulf andG. T. Richardson,J. Phys. E: Sci. Instrum. 7 (1973) 167.
S. Y. Ho andC. W. Fong,Polymer in press.
R. F. Boyer,Polym. Eng. Sci. 8 (3) (1968) 161.
P. I. Vincent,Polymer 15 (1974) 111.
B. L. Lee andL. E. Nielsen,J. Polym. Sci: Polym. Phys. Edn 15 (1977) 683.
L. E. Nielsen andB. L. Lee,J. Comp. Mater. 6 (1972) 136.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ho, S.Y., Fong, C.W. Temperature dependence of high strain-rate impact fracture behaviour in highly filled polymeric composite and plasticized thermoplastic propellants. J Mater Sci 22, 3023–3031 (1987). https://doi.org/10.1007/BF01086508
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01086508