Abstract
The spheroidization of cementite lamellae in high-carbon steel wires could be achieved in a short time by drawing at elevated temperatures below theA 1 temperature. The rapid spheroidization was attributed mainly to shearing or fracturing of cementite plates into smaller particles. Sharp edges of the fractured particles were thought to be blunted by the diffusion of iron and carbon atoms. The diffusion rate in the case of drawing at elevated temperatures was very rapid compared with that in the case of static annealing, due to continuous regeneration of dislocations and vacancies during the drawing. However, the mechanical properties of the spheroidized wires were deteriorated by internal voids formed during the drawing. Such a disadvantage could be circumvented by many cold-drawing passes followed by a final single drawing pass at an elevated temperature.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
C. M. Sellar,Metallography 10 (1977) 89.
A. H. Holtzman, J. C. Danko andR. D. Stout,Trans. Met. Soc. AIME 212 (1958) 475.
J. Leeder, P. Payson andW. L. Hodapp,Trans. ASM 28 (1940) 306.
O. E. Cullen,Met. Progr. 64 (1953) 78.
J. L. Robbins, O. C. Shepard andO. D. Sherby,J. Iron Steel Inst. 202 (1964) 804.
O. D. Sherby, M. J. Harrigan, L. Shamag andC. Sauve,Trans. ASM 21 (1969) 578.
E. A. Chojnowski andW. J. McG. Tegart,Met. Sci. J. 2 (1968) 14.
A. G. Martin andC. M. Sellar,Metallography 3 (1970) 259.
D. F. Lupton andD. H. Warrington,Met. Sci. J. 6 (1972) 200.
S. Chattopadhyay andC. M. Sellars,Acta Metall. 30 (1982) 157.
S. E. Nam andD. N. Lee,J. Korean Inst. Met. 19 (1981) 143.
Idem, in “Strength of Metals and Alloys”, edited by H. J. McQueen, J.-P. Bailon, J. I. Dickson, J. J. Jonas and M. G. Akben (Pergamon, Oxford, 1985) p. 1061.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Nam, S.E., Lee, D.N. Accelerated spheroidization of cementite in high-carbon steel wires by drawing at elevated temperatures. J Mater Sci 22, 2319–2326 (1987). https://doi.org/10.1007/BF01082110
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01082110