Abstract
The chemistry at scale/metal interfaces was studied using scanning Auger microscopy after removal of the scale in ultra-high vacuum using an in situ scratching technique. Al2O3 and Cr2O3 scales formed between 900°C and 1100°C on Fe-18 wt.% Cr-5 wt.% Al and on Ni-25 wt.% Cr alloys, respectively, were investigated. The adhesion of these scales was determined qualitatively by way of micro-indentation and scratching on the surface oxide. All of the alumina scales fractured to the same degree to expose the metal surface, regardless of the oxidation temperature. The chromia-forming alloy on the other hand, developed more adherent scales at lower oxidation temperatures. About 20 at.% sulfur was found at the metal surface in all cases, and its presence was not only detected on interfacial voids, but also on areas where the scale was in contact with the alloy at temperature. Results from this study clearly demonstrated that sulfur as an alloying impurity does segregate to the scale/alloy interface. However, for alumina scales and chromia scales, the effect of this segregation on oxide adhesion is noticeably different.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
D. P. Whittle and J. Stringer,Phil. Trans. Roy. Soc. London A27, 309 (1979).
Y. Ikeda, K. Nii, and K. Yoshihara,Trans. Jpn. Inst. Met. Suppl. 24, 207 (1983).
A. W. Funkenbusch, J. G. Smeggil, and N. S. Bornstein,Metall. Trans. 16A, 1164–1165 (1985).
D. G. Lees,Oxid. Met. 27, 75 (1987).
K. L. Luthra and C. L. Briant,Oxid. Met. 26, 397–416 (1986).
J. L. Smialek and R. Browning, inHigh Temperature Materials Chemistry III, Z. A. Munir and D. Cubicciotti, eds. (The Electrochem. Soc., Pennington, NJ, 1986), pp. 258–272.
J. G. Smeggil and G. G. Peterson,Oxid. Met. 29, 103–119 (1988).
C. G. H. Walker and M. M. El Comati,Appl. Surf. Sci. 35, 164–172 (1988/89).
H. J. Grabke, D. Wiemer, and H. Viefhaus,Appl. Surf. Sci. 47, 243–250 (1991).
P. Y. Hou and J, Stringer, inMicroscopy of Oxidation, M. J. Bennett and G. W. Lorimer, eds. (Institute of Metals, 1991), p. 1345.
S. S. Chiang, D. B. Marshall, and A. G. Evans, inSurfaces and Interfaces in Ceramic and Ceramic-Metal Systems, J. Pask and A. G. Evans, eds. (Plenum, New York, 1981), pp. 603–617.
J. Valli,J. Vac. Sci. Technol. A4 (6), 3007–3014 (1986).
R. M. Cannon, R. M. Fisher, and A. G. Evans, inThin Films-Interfaces and Phenomena, Vol. 54, R. J. Nemanich, P. S. Ho, and S. S. Lau, eds. (MRS Symp. Proc. 1986), pp. 799–804.
P. Fox, D. G. Lees, and G. W. Lorimer,Oxid. Met. 36, 491–503 (1991).
J. Benard, ed.,Adsorption on Metal Surfaces—An Integrated Approach, Vol. 13 (Studies in Surface Science and Catalysis, Elsevier, 1983), pp. 55–97.
H. J. Grabke, W. Paulitschke, G. Tauber, and J. Viefhaus,Surf. Sci. 63, 377–389 (1977).
J. E. Harris,Acta Metall. 26, 1033–1041 (1978).
J. Stringer,Metall. Rev. 11, 113–128 (1966).
H. Hindam and D. P. Whittle,Oxid. Met. 18, 245–284 (1982).
J. G. Smeggil,Mater. Sci. Eng. 87, 261 (1987).
J. L. Smialek, inCorrosion and Particle Erosion at High Temperatures, V. Srinivasan and K. Vedula, eds. (TMS, 1989), pp. 425–457.
D. R. Sigler,Oxid. Met. 29, 23–43 (1988).
T. N. Rhys-Jones and H. J. Grabke,Mater. Sci. Tech. 4, 446–454 (1988).
I. Melas and D. G. Lees,Mater. Sci. Tech. 4, 455–456 (1988).
J. G. Smeggil,Corrosion and Particle Erosion at High Temperatures, V. Srinivasan and K. Vedula, eds. (TMS, 1989), pp. 403–424.
J. L. Smialek, inMicroscopy of Oxidation, M. J. Bennett and G. W. Lorimer, eds. (Institute of Metals, 1991), pp. 258–270.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hou, P.Y., Stringer, J. Oxide scale adhesion and impurity segregation at the scale/metal interface. Oxid Met 38, 323–345 (1992). https://doi.org/10.1007/BF00665658
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00665658