Oxygen transport during oxide growth on (110), (111), and (100) Al crystals at 550°C is investigated by18O/SIMS combined with kinetic measurements and SEM and TEM observations. Starting with an electropolished surface, the experimental evidence suggests oxide growth by oxygen anion transport via local pathways through an outer amorphous Al2O3 layer and oxygen incorporation at the periphery of the underlying laterally growing γ-Al2O3 islands. The kinetics, island morphology and epitaxy are sensitive to substrate orientation. This oxide growth behavior is compared with oxide formation on a sputter-cleaned and annealed (111) Al surface.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P. E. Doherty and R. S. Davis,J. Appl. Phys. 34, 619 (1963).
J. J. Randall and W. J. Bernard,J. Appl. Phys. 35, 1317 (1964).
H. M. Hindam and W. W. Smeltzer,Oxid. Met. 14, 337 (1980).
M. J. Dignam and W. R. Fawcett,J. Electrochem. Soc. 7, 663 (1966).
K. Shinohara, T. Seo, and H. Kyogoku,Z. Metallk. 73, 774 (1982).
R. K. Hart and J. K. Maurin,Surf. Sci. 20, 285 (1970).
A. F. Beck, M. A. Heine, E. J. Caule, and M. J. Pryor,Corros. Sci. 7, 1 (1967).
H. J. van Beek and E. J. Mittemeijer,Thin Solid Films 122, 131 (1984).
G. M. Scamans and E. P. Butler,Metall. Trans. A6, 2055 (1975).
K. Thomas and M. W. Roberts,J. Appl. Phys. 32, 70 (1961).
E. W. A. Young and J. H. W. De Wit,Solid State Ionics 16, 39 (1985).
D. F. Mitchell, R. J. Hussey, and M. J. Graham,J. Vacuum Sci. Technol. A1, 1006 (1983).
I. P. Batra and L. Kleinman,J. Electron Spect. Rel. Phenom. 33, 175 (1984).
R. M. Henry, B. W. Walker, and P. C. Stair,Solid State Commun. 42, 23 (1982).
C. Ocal, B. Basurco, and S. Ferrer,Surf. Sci. 157, 233 (1985).
A. Csanady, A. Barna, and P. B. Barna,Oxid. Met. 13, 245 (1979).
M. J. Graham and M. Cohen,J. Electrochem. Soc. 119, 879 (1972).
J. I. Eldridge, R. J. Hussey, D. F. Mitchell, and M. J. Graham, inProceedings of the Symposium on Fundamental Aspects of High Temperature Corrosion-II, D. A. Shores and G. J. Yurek, eds., Vol. 86–9 (Electrochemical Society, Pennington, New Jersey, 1986), p. 226.
P. B. Sewell, D. F. Mitchell, and M. Cohen,Dev. Appl. Spect. 7A, 61 (1969).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Eldridge, J.I., Hussey, R.J., Mitchell, D.F. et al. Thermal oxidation of single-crystal aluminum at 550°C. Oxid Met 30, 301–328 (1988). https://doi.org/10.1007/BF00659003
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00659003