Abstract
The oxidation kinetics of pure titanium and of Ti-6Al-4 V by water vapor were studied between 650 and 950°C and from 0.5 to 18 Torr. The results showed a marked similarity of the oxidation behavior for both the alloy and pure titanium. The rate curves had the same appearance. At low temperatures (below 750°C) they exhibited two stages. At high temperature the first of these stages was not observed. Scanning electron microscopy (SEM) and electron probe analyses of the scale showed that the structure of the scales was also similar over the temperature range 750–900°C: they consisted of two layers of rutile, and, in the case of the alloy, of a thin sublayer of alumina between the other two. Furthermore, SEM examination of the surface of oxidized specimens revealed the existence of whiskers.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
G. P. Lutschkin and G. G. Iljin,Fiz. Met. Metalloved. 2, 521 (1956).
K. Lohberg and H. W. Schleicher,Z. Phys. Chem. (Frankfurt) 15, 223 (1958).
F. Motte, thesis, Grenoble (in press).
P. Sarrazin and C. Coddet,Corros. Sci. 14, 83 (1974).
E. A. Garcia, X. Lucas, G. Beranger, and P. Lacombe,C. R. Acad. Sci., Ser. C 278, 837 (1974).
C. Coddet, P. Sarrazin, and J. Besson,J. Less-Common Met. (in press).
J. Stringer,Acta Metall. 8, 758 (1960).
J. Stringer,J. Electrochem. Soc. 112, 1083 (1965).
J. S. Sheasby, G. R. Wallwork, and W. W. Smeltzer,J. Electrochem. Soc. 113(12), 1255 (1966).
J. A. Roberson and R. A. Rapp,Trans. Am. Inst. Min. Metall. Pet. Eng. 239, 1327 (1967).
H. M. Flower and P. R. Swann,Acta Metall. 22, 1339 (1974).
T. Kameyama and S. Naka,J. Am. Ceram. Soc. 57(11), 499 (1974).
F. E. Wagstaff and K. J. Richards,J. Am. Ceram. Soc. 49(3), 118 (1966).
P. Kofstad,High Temperature Oxidation of Metals (John Wiley & Sons, New York, 1966), Chap. VI.
P. Kofstad, P. B. Anderson, and O. J. Krudtaa,J. Less-Common Met. 3, 89 (1961).
J. Yahia,Phys. Rev. 130(5), 1711 (1963).
E. H. Greene, F. J. Barone, and W. M. Hirthe,J. Am. Ceram. Soc. 48(12), 623 (1965).
J. B. Wachtman and L. R. Doyle,Phys. Rev. 135(1), 276 (1964).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Motte, F., Coddet, C., Sarrazin, P. et al. A comparative study of the oxidation with water vapor of pure titanium and of Ti-6Al-4V. Oxid Met 10, 113–126 (1976). https://doi.org/10.1007/BF00614241
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00614241