The oxidation behavior of iron-chromium-nickel alloys containing 0–30% chromium has been determined for oxidation at 1000°C in static pure oxygen atmospheres. Particular emphasis has been placed on the correlation between the kinetics of oxidation and the morphologies and compositions of the scales produced. Maximum oxidation resistance was associated with the formation of chromic oxide scales on alloys containing greater than 20% chromium. The loss of an oxide species from these scales by volatilization may limit the usefulness of alloys protected by chromic oxide scales to a temperature less than 1000°C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J. E. Croll and G. R. Wallwork,Oxid. Metals 1, 55 (1969).
H. J. Yearian, E. C. Randell, and T. A. Longo,Corrosion 12, 515 t (1956).
G. L. Wulf, M. B. McGirr, and G. R. Wallwork,Corr. Sci. 9, 739 (1969).
G. C. Wood and D. P. Whittle,JISI 202, 979 (1964).
C. S. Tedmon,J. Electrochem. Soc. 114, 788 (1967).
G. C. Wood,Corr. Sci. 2, 255 (1961).
E. J. Felten,J. Electrochem. Soc. 108, 490 (1961).
V. R. Howes,Corr. Sci. 8, 221 (1968).
P. K. Footner, D. R. Holmes, and D. Mortimer,Nature 216, 54 (1967).
G. C. Wood,Corr. Sci. 2, 173 (1961).
G. C. Wood, T. Hodgkiess, and D. P. Whittle,Corr. Sci. 6, 129 (1966).
G. C. Wood,Oxid. Metals 2, 11 (1970).
B. Chattopadhyay and G. C. Wood,Oxid. Metals 2, 373 (1970).
A. U. Seybolt,J. Electrochem. Soc. 107 147 (1960).
G. C. Wood and T. Hodgkiess,J. Electrochem. Soc. 113, 319 (1966).
R. A. Rapp,Corrosion 21, 382 (1965).
R. T. Foley,J. Electrochem. Soc. 109, 1202 (1962).
G. L. Wulf, T. J. Carter, and G. R. Wallwork,Corr. Sci. 9, 689 (1969).
A. Dalvi, Research Report, Dept. of Met. and Mat. Sci., McMaster University, Hamilton, Ontario (1968).
G. S. Viktorovich, V. A. Gutin, and D. I. Lisovski,Tsvetn. Metall. 7, 54 (1966).
H. J. Yearian, H. E. Boren, and R. E. Warr,Corrosion 12, 561 t (1956).
J. E. Croll, Ph.D. Thesis, University of New South Wales, Australia (1971).
C. S. Giggins and F. S. Pettit,Trans. AIME 245, 2495 (1969).
P. Schafmeister and R. Ergang,Arch. Eisenhuttenw 12, 459 (1939).
C. H. M. Jenkins, E. H. Bucknall, C. R. Austin, and G. A. Mellor,JISI 136, 187 (1937).
C. S. Tedmon,J. Electrochem. Soc. 113, 766 (1966).
R. Kosak, Ph.D. Thesis, Ohio State University (1969).
G. R. Wallwork and A. Z. Hed,Oxid. Metals 3, 171 (1971).
C. Wagner, “Atom Movements” A.S.M. Cleveland, Ohio (1951), p. 153.
W. C. Hagel,Trans. ASM 56, 583 (1963).
Author information
Authors and Affiliations
Additional information
Research supported by the Broken Hill Proprietary Co., Ltd., Postgraduate Research Scholarship.
Unless otherwise specified, all compositions referred to in this paper are in weight percent.
Rights and permissions
About this article
Cite this article
Croll, J.E., Wallwork, G.R. The high-temperature oxidation of iron-chromium-nickel alloys containing 0–30% chromium. Oxid Met 4, 121–140 (1972). https://doi.org/10.1007/BF00613088
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF00613088