Abstract
The oxidation behavior of iron-nickel-aluminum alloys containing 0–40 wt.% nickel and 0–30 wt.% aluminum has been investigated at 600 and 800° C. Through the construction of “oxide maps” it can be shown that three possible oxide morphologies may exist: Alloys containing less than approximately 5 wt.% aluminum form scales consisting of predominantly Fe2O3 and spinel; alloys with between 5 and 10 wt.% aluminum form Al2O3 scales interspersed by Fe2O3 nodules, and alloys with greater than 10 wt.% aluminum form predominantly γ-Al2O3 scales.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
R. T. Foley,J. Electrochem. Soc. 109(12), 1202 (1962).
G. L. Wulf, T. J. Carter, and G. R. Wallword,Corros. Sci. 9, 689 (1969).
I. A. Menzies and J. Lubkiewicz,Oxid. Met. 3(1), 41 (1971).
Croll, J., Ph.D. thesis, University of New South Wales (1971).
I. A. Menzies and J. Lubkiewicz,J. Electrochem. Soc. 117(2), 1539 (1970).
W. E. Boggs,J. Electrochem. Soc. 118(6), 906 (1971).
F. Saegusa and L. Lee,Corrosion 22, 168 (1966).
W. C. Hagel,Corrosion 22(10), 316 (1956).
T. Nakayama and K. Kaneko,Corrosion 26(7), 187 (1970).
G. J. Bateman and R. Rolls,Br. Corros. J. 5(5), 122 (1970).
G. R. Wallwork and M. B. McGirr, inStress Effects and the Oxidation of Metals, J. V. Cathcart, ed. (Met. Soc. of A.I.M.E., New York, 1975) p. 263.
R. E. Grace and A. U. Seybolt,J. Electrochem. Soc. 105(10), 582 (1958).
T. Nakayama, Report of Castings Research Laboratory, Waseda University,9, 71 (1958).
G. S. Viktorovich and D. I. Lisovskii,Tsvetn. Met. 7(11), 49 (1966).
R. H. Condit, M. J. Brabers, and C. E. Birchenall,Trans. Am. Inst. Min. Metall. Pet. Eng. 218, 768 (1960).
F. H. Stott, G. C. Wood, and M. G. Hobby,Oxid. Met. 3(2), 103 (1971).
G. C. Wood,Corros. Sci. 2, 255 (1962).
D. P. Whittle and G. C. Wood,J. Electrochem. Soc. 114(10), 986 (1967).
M. G. C. Cox, B. McEnaney, and V. D. Scott,Phil. Mag. 31(2), 331 (1975).
V. R. Howes,Corros. Sci. 8, 221 (1968).
J. F. Tien and F. S. Pettit,Metall. Trans. 3(6), 1587 (1972).
J. D. Kuenzly and D. L. Douglass,Oxid. Met. 8(3), 139 (1974).
F. A. Golightly, F. H. Stott, and G. C. Wood,Oxid. Met. 10(3), 163 (1976).
F. N. Rhines and J. S. Wolf,Metall. Trans. 1, 1701 (1970).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sakiyama, M., Tomaszewicz, P. & Wallwork, G.R. Oxidation of iron-nickel aluminum alloys in oxygen at 600–800° C. Oxid Met 13, 311–330 (1979). https://doi.org/10.1007/BF00609303
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00609303