Summary
The possibility of using microtomed longitudinal sections of wood for the study of longitudinal shrinkage has been investigated using hoop pine (Araucaria cunninghamii Ait.). Cutting of the sections was shown to distort them and to affect their subsequent shrinkage. However, by increasing the inclination angle of the microtome knife, sections could be cut without change in longitudinal dimensions. The longitudinal shrinkage behaviour of such sections more than 80 μm thick was little different from that of thicker sawn specimens.
Measurements of longitudinal shrinkage using this technique showed that very thin sections (40 μm) had greater longitudinal shrinkage than sawn wood. Partial delignification with sodium chlorite also increased longitudinal shrinkage. The longitudinal shrinkage was reproducible over successive cycles of moisture content change but not reversible, the length of a specimen at a given moisture content being less during desorption than at the same moisture content during adsorption. It is considered likely that the longitudinal shrinkage of wood is markedly affected by stresses which develop within the cell wall as the wood dries.
Zusammenfassung
Die Möglichkeit, Mikrotom-Längsschnitte zur Prüfung der Längsschwindung zu verwenden, wurde an Hoop Pine (Araucaria cunninghamii Ait.) geprüft. Dabei zeigte sich, daß die Längsschnitte beim Schneiden verschoben werden, was die nachfolgende Schwindung beeinflußt. Nachdem der Schnittwinkel des Mikrotommessers vergrößert worden war, konnten die Schnitte ohne Veränderung der Längsabmessungen abgetrennt werden. Das Längsschwindungs-Verhalten solcher Schnitte von über 80 μm Dicke unterschied sich nur wenig von demjenigen dickerer, gesägter Proben.
Messungen der Längsschwindung mit Hilfe des beschriebenen Verfahrens zeigten, daß sehr dünne Schnitte (40 μm) eine größere Längsschwindung aufweisen als gesägte Schnitte. Die teilweise Delignifizierung mit Natrium Chlorit erhöhte ebenfalls die Längsschwindung. Die Längsschwindung blieb während aufeinanderfolgender zyklischer Feuchtigkeitsänderungen reproduzierbar, war aber nicht umkehrbar. Die Länge einer Probe war, bei gleichem Feuchtigkeitsgehalt während der Desorption geringer als während der Adsorption. Es darf als wahrscheinlich angesehen werden, daß die Längsschwindung des Holzes deutlich durch Spannungen beeinflußt wird, die sich beim Trocknen des Holzes innerhalb der Zellwand entwickeln.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Christensen, G. N.: The Rate of Sorption of Water Vapour by Wood and Pulp. APPITA Vol.13 (1959) p. 112–123.
—: Kinetics of Sorption of Water Vapour by Wood, I. Effect of Sample Thickness. Aust. J. Appl. Sci. Vol.11 (1960) No. 2, p. 295/304.
—: The Use of Small Specimens for Studying the Effect of Moisture Content Changes on the Deformation of Wood under Load. Aust. J. Appl. Sci. Vol.13 (1962) No. 4, p. 242/256.
—, u. K. E. Kelsey: Die Geschwindigkeit der Wasserdampfsorption durch Holz. (The Rate of Sorption of Water Vapour by Wood.) Holz als Roh- und Werkstoff Vol.17 (1959) p. 178/188.
Clarke, S. H.: The Differential Shrinkage of Wood. Forestry Vol.4 (1930) No. 2, p. 93.
Greenhill, W. L.: Shrinkage of Australian Timbers, Pt. 1. Coun. Sci. Ind. Res., Aust., Pamphlet No.67 (1936).
Grzeczynski, T.: Einfluß der Erwärmung im Wasser auf vorübergehenden und bleibende Formänderungen frischen Rotbuchenholzes. Holz als Roh- und Werkstoff Vol.20 (1962) No. 6, p. 210/216.
Halse, D. M.: Determination of Cellulose and Wood Fibre in Paper. Papir Journalen Vol.10 (1926) p. 121
Kelsey, K. E.: A Critical Review of the Relationship between the Shrinkage and Structure of Wood. C.S.I.R.O. Aust., Div. For. Prod. Tech. Pap. No. 28 (1963).
Kishima, T., andS. Hayashi: Dimensional Variation of Wood Sections Caused in the Process of Making Slides. Wood Research (Kyoto Univ.) No. 22 (1959) p. 35/42.
Koehler, A.: Longitudinal Shrinkage of Wood. Trans. Amer. Soc. Mech. Engrs. Vol.53 (1931) p. 17.
Koehler, A.: Longitudinal Shrinkage of Wood. U.S. For. Serv., For. Prod. Lab. Rep. No. 1093 (1946).
Kübler, H.: Studien über Wachstumsspannungen des Holzes, 3. Mitt.: Längenänderungen bei der Wärmebehandlung frischen Holzes. Holz als Roh- und Werkstoff Vol.17 (1959) No. 3, p. 77/86.
Kühne, H., andJ. Vodoz: Über das Schwinden und Quellung einiger Schweizerischer Hölzer. (Shrinkage and Swelling of some Swiss Wood Species.) Ber. Eidgenöss. Mat. Prüf. Anst. No. 179 (1951).
Lawniczak, M., K. Nowak and W. Dregier: Badania nad pecznieniem mikroskopowych preparatow drewna. (Investigation of the swelling of thin sections of wood.) Sylwan Vol.100 (1956) No. 3, p. 89/96.
Lindsay, F. W., and L. Chalk: Influence of Rays on the Shrinkage of Wood. Forestry Vol.27 (1954) No. 1, p. 16/24.
MacLean, J. D.: Effect of Temperature on the Dimensions of Green Wood. Proc. Amer. Wood. Press. Assoc. Vol.48 (1952) p. 136/157.
Siimes, F. E.: Suomalaisen mantypuun rakenteellisista ja fysikalisista ominaisuuksista. (On the Structural and Physical Properties of Finnish Pine Wood, especially the Phenomenon of Shrinking and Swelling Affected by Changing the Moisture Content of Wood.) Publ. Found. For. Prod. Res. Finnl. No. 29 (1938).
Vodoz, J.: Le retrait et le gonflement du bois. (Shrinkage and Swelling of Wood.) J. For. Suisse No. 10 (1953) p. 508/516.
Yokota, T., and H. Tarkow: Hygrothermal Properties of Wood. J. Jap. Wood Res. Vol.7 (1961) No. 5, p. 217/222.
—: Changes in Dimension on Heating Green Wood. For. Prod. J. Vol.12 (1962) p. 43/45.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Sadoh, T., Christensen, G.N. Longitudinal shrinkage of wood — Part I: Longitudinal shrinkage of thin sections. Wood Sci.Technol. 1, 26–44 (1967). https://doi.org/10.1007/BF00592254
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00592254