Abstract
The mutual influence of precipitation and recrystallisation was investigated in supersaturated and cold worked Cu-Co-alloys. For medium amounts of deformation (10 to 20% for 2.8 at. % Co) a discontinuous reaction was found that leads to simultaneous annihilation of dislocations and formation of rows of Co-particles. At lower amounts of deformation, recrystallisation is inhibited by particles, while recrystallisation is complete before precipitation starts at higher amounts of deformation.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
E. Hornbogen andH. Kreye, in “Textures in Research and Practice”, edited by J. Grewen and G. Wassermann (Springer, Berlin, 1969) p. 274.
V. A. Phillips,Trans AIME 230 (1964) 967.
I. W. Servi andD. Turnbull,Acta Met 14 (1966) 161.
J. D. Livingston,Trans AIME 215 (1959) 566.
C. A. MacKliet,Phys. Rev. 109 (1958) 1964.
C. Zener, quoted byC. S. Smith,Trans. AIME 175 (1948) 15.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kreye, H., Hornbogen, E. Recrystallisation of supersaturated copper-cobalt solid solutions. J Mater Sci 5, 89–95 (1970). https://doi.org/10.1007/BF00554625
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00554625