Abstract
This investigation deals with some flexural fatigue and abrasion studies of Kevlar-29, glass and carbon fibres. The test methods included in the study are fatigue by pure flexing, buckling and rotation over a wire, and abrasion by rubbing against a rotating rod. Kevlar-29 fibres were found to perform well in these tests because they could survive the relatively high bending strains by yielding in axial compression. Carbon and glass fibres, although unable to survive at these high strains, did perform well when very low bending strains and tensions were used. Kevlar-29 fibres were found to be less abrasion-resistant than glass fibres, probably because of their low radial strength. The fracture morphologies of Kevlar-29 fibres in nearly all these tests showed axial splitting, confirming indications of low strength in the fibre perpendicular to its axis.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
A. R. Bunsell,J. Mater. Sci. 10 (1975) 1300.
J. W. S. Hearle andL. Konopasek, to be published.
B. C. Jariwala, Ph.D. Thesis, University of Manchester, 1974.
M. M. Schoppee andJ. Skelton,Textile Res. J. 44 (1974) 968.
S. F. Calil, Ph.D. Thesis, University of Manchester, 1977.
J. W. S. Hearle andB. S. Wong,J. Phys. E. to be published.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hearle, J.W.S., Wong, B.S. Flexural fatigue and surface abrasion of Kevlar-29 and other high-modulus fibres. J Mater Sci 12, 2447–2455 (1977). https://doi.org/10.1007/BF00553932
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00553932