Abstract
Fatigue tests have been conducted on polystyrene in air at different mean stress conditions and also over the temperature range−60 to 60°C using notched specimens. In addition, some tests were performed with the specimens immersed in a detergent and in a corn oil. The data were first represented on a conventional log ΔK-log da/dN plot to determine the Paris law parameters and how these varied with mean stress, temperature and environment. Considerable variations were noted but no useful pattern could be discerned. The data were then analysed using a recently proposed two-stage line plastic zone model so that a crack tip zone stress and a fatigue damage factor could be found. These stresses were found to be very high in air and to increase with increasing mean stress, and this is attributed to a high degree of constraint at the crack tip. There was an abrupt change in σc at about 20° C which, it is suggested, is caused by the onset of crazing due to the presence of a loss peak. Associated changes in K c were also noted. In environments, the stresses were much smaller and agreed with those obtained in static fracture, suggesting that crazes are formed in environments prior to, and not during, fatigue crack growth. The stress reduction factor, α, remained constant at about 0.2 with both temperature and environment.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
S. Arad, J. C. Radon and L. E. Culver, Polymer. Eng. Sci. 12 (1972) 193.
Idem, ibid 9 (1969) 339.
R. W. Hertzberg, H. Nordberg and J. A. Manson, J. Mater. Sci. 5 (1970) 521.
B. Mukherjee and D. J. Burns, Exp. Mech. 11 (1971) 433.
J. G. Williams, J. Mater. Sci. 12 (1977) 2525.
G. P. Marshall, L. E. Culver and J. G. Williams, Int. J. Fract. 9 91973) 295.
R. J. Bird, G. Rooney and J. Mann, Polymer 12 (1971) 742.
J. Murray and D. Hull, ibid 10 (1969) 451.
J. P. Berry, J. Polymer Sci. 50 (1961) 313.
D. Hull, J. Mater. Sci 5 (1970) 357.
S. Rabinowitz, A. R. Krause and P. Beardmore, ibid 8 (1973) 11.
V. Havlicek and V. Zilvar, J. Macromol. Sci. B5 (1971) 317.
M. D. Skibo, R. W. Hertzberg and J. A. Manson, J. Mater. Sci. 11 (1976) 479.
J. A. Manson and R. W. Hertzberg, CRC Rev. Macromol. Sci. 1 (1973) 433.
W. F. Brown Jun and J. E. Srawley, ASTM, STP 410 (1966).
S. A. Sutton, Eng. Fract. Mech. 6 (1974) 587.
J. C. Radon, S. Arad and L. E. Culver, ibid 6 (1974) 195.
N. G. McCrum, B. E. Read and G. Williams, “Anelastic and Dielectric Effects in Polymeric Solids” (Wiley, London, 1967).
M. Parvin and J. G. Williams J. Mater. Sci. 11 (1976) 2045.
J. C. Radon, J. Polymer Sci. 13 (1975) 383.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mai, Y.W., Williams, J.G. Temperature and enviromental effects on the fatigue fracture in polystyrene. J Mater Sci 14, 1933–1940 (1979). https://doi.org/10.1007/BF00551034
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00551034