Abstract
The compression behaviour of a series of polyester resins of various compositions and in different states of cure has been investigated. Their mechanical characteristics having been established, the same range of resins was then used as a matrix material for a series of composites reinforced with carbon, glass and aromatic polyamide fibres. The composites were unidirectionally reinforced, having been manufactured by pultrusion, and were compression tested in the fibre direction after a series of experiments to assess the validity of a simple testing procedure. “Rule of Mixtures” behaviour occurred in glass-polyester composites up to limiting volume fractions (V f) of 0.31 for strength and 0.46 for elastic modulus, the compression modulus being equal to the tensile modulus, and the apparent fibre strength being in the range 1.3 to 1.6 GPa at this limiting V f. At a V f of 0.31 the strengths of reinforced polyesters were proportional to the matrix yield strength, σ my, and their moduli were an inverse exponential function of σ my. For the same matrix yield strength a composite with an epoxy resin matrix was stronger than polyester based composites. At V f=0.30, Kevlar fibre composites behaved as though their compression modulus and strength were much smaller than their tensile modulus and strength, while carbon fibre composites were only slightly less stiff and weaker in compression than in tension. The compression strengths of the polyester resins were found to be proportional to their elastic moduli.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
P. D. Ewins, RAE TR, 71217 (1971).
A. Kelly in “Strong Solids” 2nd edn. (Clarendon Press, Oxford, 1973) pp. 170–1.
E. Moncunill De Ferran and B. Harris, J. Comp. Mater. 4 (1970) 62.
M. R. Piggott and P. Wilde, J. Mater. Sci., in press.
T. Hayashi and K. Koyama, Proceedings of the International Conference on the Mechanical behaviour of Materials, Kyoto, Soc. Mater. Sci. Japan 5 (1971) 104.
N. L. Hancox, J. Mater. Sci. 10 (1975) 234.
B. W. Rosen, “Fibre Composite Materials” (American Society for Metals, Metals Park, Ohio) Ch. 3, 1964.
J. H. Greenwood and P. G. Rose, J. Mater. Sci. 9 (1974) 1809.
C. R. Chaplin, J. Mater. Sci. 12 (1977) 347.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Piggott, M.R., Harris, B. Compression strength of carbon, glass and Kevlar-49 fibre reinforced polyester resins. J Mater Sci 15, 2523–2538 (1980). https://doi.org/10.1007/BF00550757
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00550757