Abstract
Defects in mesophase pitch-based carbon fibres were studied by using scanning electron microscopy and energy dispersive X-ray analysis. A novel fractography technique permitted routine recovery of the primary fracture surfaces of filaments tested in tension. The carbon fibres included experimental monofilaments spun on laboratory equipment and multifilaments spun as a continuous fibre on production-type equipment. Carbon monofilaments and multifilaments from clean mesophase pitches were stronger than similarly prepared fibres from contaminated pitches. Reduction in the levels of contamination allowed fibres to be processed at high heat-treatment temperatures without sacrificing tensile strength. Results from a Weibull analysis of the tensile strength of clean multifilaments as a function of test gauge length were consistent with microscopy observations that strength-limiting surface flaws were closely spaced along the filaments.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
R. Moreton, Fibre Sci. Tech. 1 (1969) 273.
R. Moreton, W. Watt and W. Johnson, Nature 213 (1967) 690.
D. J. Thorne, ibid. 248 (1974) 754.
Idem, Third Conference on Industrial Carbons and Graphite (Society of Chemical Industry, London, 1971) p. 463.
R. Bacon and W. A. Schalamon, Appl. Polym. Symp. 9 (1969) 285.
S. Chwastiak, J. B. Barr and R. Didchenko, Carbon 17 (1979) 49.
P. E. Mcmahon, SAMPE Quarterly 6 (1974) 7.
R. J. Diefendorf and E. Tokarsky, Polym. Eng. Sci. 15 (1975) 150.
J. W. Johnson, Appl. Polym. Symp. 9 (1969) 229.
J. W. Johnson and D. J. Thorne, Carbon 7 (1969) 659.
J. V. Sharp and S. G. Burnay, “Carbon Fibres: Their Composites and Applications” (Plastics Institute, London, 1971) p. 68.
J. V. Sharp, S. G. Burnay, J. R. Matthews and E. A. Harper, “Carbon Fibres: Their Place in Modern Technology” (Plastics Institute, London, 1974), p. 25.
M. A. A. Jorro, W. R. Ladner and T. R. Rantell, Carbon 14 (1976) 219.
W. Watt and W. Johnson, Third Conference on Industrial Carbons and Graphite (Society of Chemical Industry, London) 1971, p. 417.
R. Moreton and W. Watt, Nature 247 (1974) 360.
J. B. Barr, S. Chwastiak, R. Didchenko, I. C. Lewis, R. T. Lewis and L. S. Singer, Appl. Polym. Symp. 29 (1976) 161.
J. V. Sharp and S. G. Burnay, “Carbon '72” (Bad Honnef, Deutsche Keramische Gesellschaft, 1972) p. 310.
E. Y. Robinson, University of California Report UCRL-5 06 22 (March 1969), (NSA 23 3 89 19).
A. Kelly, “Strong Solids” (Clarendon Press, Oxford, 1973) p. 172.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jones, J.B., Barr, J.B. & Smith, R.E. Analysis of flaws in high-strength carbon fibres from mesophase pitch. J Mater Sci 15, 2455–2465 (1980). https://doi.org/10.1007/BF00550747
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00550747