Abstract
From the results of the bending strength and Weibull modulus of the joints of silicon nitride ceramics brazed using aluminium-silicon and aluminium-magnesium alloy filler metals at a temperature of 1073 K for 0.9 ksec in a vacuum of 1.3 × 10−3 Pa, silicon, especially, present in a small amount in the filler metals, was found to be effective in improving the bond strength, while magnesium in the filler metals was harmful to the joining. This can result in the formation of a thick stable alumina layer on the surfaces of the filler metals containing magnesium during brazing which prevented contact of the filler metals with the silicon nitride ceramics.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
K. Suganuma, T. Okamoto, K. Koizumi and M. Shimada, J. Mater. Sci. 22 (1987) 1359.
A. Kohno, T. Yamada and K. Yokoi, Nippon Kinzoku-Gakkaishi 49 (1985) 876.
M. Naka, M. Kubo and I. Okamoto, J. Mater. Sci. 22 (1987) 4417.
M. Morita, K. Suganuma and T. Okamoto, J. Mater. Sci. Lett. 6 (1987) 474.
X. S. Ning, K. Suganuma, M. Morita and T. Okamoto, Phil. Mag. Lett. 55 (1987) 93.
X. S. Ning, K. Suganuma, T. Okamoto, A. Koreeda and Y. Miyamoto, J. Mater. Sci., 24 (1989) 2879.
X. S. Ning, T. Okamoto, Y. Miyamoto, A. Koreeda and K. Suganuma, ibid., 24 (1989) 2865.
I. M. Low and R. McPherson, ibid. 24 (1989) 926.
W. Hehn and E. Fromm, Aluminium 64 (1988) 180.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ning, X.S., Okamoto, T., Miyamoto, Y. et al. Bond strength and interfacial structure of silicon nitride joints brazed with aluminium-silicon and aluminium-magnesium alloys. J Mater Sci 26, 2050–2056 (1991). https://doi.org/10.1007/BF00549166
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00549166