Abstract
The influence of blend morphology on mechanical behaviour of rubber-toughened polymers was investigated. Diglycidyl ether of bisphenol A epoxies toughnened by core-shell rubber particles were employed as the model systems. The blend morphology was varied by changing the composition of the shell of particles, the curing agent, and the extent of agitation prior to casting. It is shown that the most uniform dispersion of particles is obtained when the shell of the modifiers contains reactive groups. In the absence of the reactive groups and when a slow curing agent is employed, however, a highly connected microstructure is obtained. It was found that a blend with a connected microstructure provides significantly higher fracture toughness compared to a similar blend containing uniformly dispersed particles. The reason for this observation is that the connected morphology enables the shear bands to grow further from the crack tip and thus consume more energy before fracture occurs. Also, the yield strength in uniaxial tensile testing is significantly lower in the blend with the connected morphology. Therefore, it should contribute to a larger plastic zone size.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
C. B. BUCKNALL, “Toughened Plastics” (Applied Science, London, 1977).
J. N. SULTAN, R. C. LIABLE and F. J. MCGARRY, Polym. Symp. 16 (1971) 127.
A. C. GARG and Y. W. MAI, Compos. Sci. Technol. 31 (1988) 179.
R. A. PEARSON and A. F. YEE, J. Mater. Sci. 26 (1991) 3828.
V. V. KOZII and B. A. ROZENBERG, Polym. Sci. 34 (1992) 919.
R. J. M. BORGGREVE and R. J. GAYMANS, Polymer 29 (1988) 1441.
E. A. FLEXMAN, D. D. HUANG and H. L. SNYDER, in “Polymer Preprints 29, edited by C. K. Riew and A. J. Kinloch (ACS, Washington, 1988) p. 189.
K. YAMANAKA, Y. TAKAGI and T. INOUE, Polymer 30 (1989) 1839.
H. S. Y. HSICH, Polym. Eng. Sci. 30 (1990) 493.
H. J. SUE, E. I. GARCIA-MEITIN, D. M. PICKELMAN and P. C. YANG, in “Toughened Plastics”, Advances in Chemistry Series, Vol. 233, edited by C. K. RIEW and A. J. KINLOCH (ACS, Washington, 1993) p. 259.
K. YAMANAKA and T. INOUE, Polymer 30 (1989) 662.
B. G. MIN, J. H. HODGKIN and Z. H. STACHURSKI, J. Appl. Polym. Sci. 50 (1993) 1065.
A. MUKRAMI, D. SAUNDERS, K. OOISHI and T. YOSHIKI, J. Adhes. 39 (1992) 227.
T. IIJIMA, S. MIURA, W. FUKUDA and M. TOMOI, Eur. Polym. J. 29 (1993) 1103.
P. A. MATAGA, Acta Metall. 37 (1989) 3349.
Y. HUANG and A. J. KINLOCH, J. Mater. Sci. Lett. 11 (1992) 484.
R. A. PEARSON and A. F. YEE, J. Mater. Sci. 24 (1989) 2571.
R. BAGHERI, PhD dissertation, Lehigh University, Bethlehem, PA (1995).
H. J. SUE, R. A. PEARSON, D. S. PARKER, J. HUANG and A. F. YEE, ACS Div. Polym. Chem. Polym. Prep. 29 (1988) 147.
Rohm and Haas scientists, private communication (1993).
C. M. GOMEZ and C. B. BUCKNALL, Polymer 34 (1993) 2111.
S. REICH, Phys. Lett. 114A (1986) 90.
M. CARPINETI and M. GIGLIO, Phys. Rev. Lett. 68 (1992) 3327.
D. J. ROBINSON and J. C. EARNSHAW, ibid. 71 (1993) 715.
I. C. HUANG, PhD dissertation, University of Michigan, Ann Arbor, MI (1994).
G. R. IRWIN, Appl. Mater. Res. 3 (1964) 65.
S. WU, Polym. Eng. Sci. 30 (1990) 753.
A. LAZZERI and C. B. BUCKNALL, J. Mater. Sci. 28 (1993) 6799.
C. CHENG, A. HILTNER, E. BAER, P. R. SOSKEY and S. G. MYLONAKIS, ibid. 30 (1995) 587.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Bagheri, R., Pearson, R.A. Role of blend morphology in rubber-toughened polymers. JOURNAL OF MATERIALS SCIENCE 31, 3945–3954 (1996). https://doi.org/10.1007/BF00352655
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00352655