The sintering behaviour of powders of two calcium phosphates, namely hydroxyapatite (HA) and dicalcium phosphate (DCP), were studied at various temperatures and in various environments. The density, flexural strength and Knoop hardness of HA sintered in air for 4 h initially increased with the sintering temperature, reaching maxima at around 1150°C, and then decreased due to decomposition of HA into tri- (TCP) and tetracalcium phosphates. Sintering in vacuum caused decomposition of HA at lower temperatures, and consequently the mechanical properties were poorer than those of HA sintered in air. The densification and mechanical properties of DCP sintered in air and vacuum showed similar behaviour to those of HA. In air DCP underwent phase transformation from γ- to β- and to α-phases. In vacuum DCP started to decompose into tricalcium phosphate at 1000°C. To reduce dehydroxylation, HA powder was sintered in moisture at various temperatures up to 1350°C and X-ray diffraction study did not indicate any decomposition at the highest sintering temperature. The density, flexural strength and hardness of HA sintered in moisture increased with the sintering temperature and eventually reached plateaux at about 1300°C, but below 1200°C they were lower than those of HA sintered in air at corresponding temperatures. Thus, it is seen that dehydroxylation did not hinder sintering of HA. On the other hand, decomposition obstructed sintering of both HA and DCP.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
J. R.VAN WAZER, “Phosphourous and Its Compounds”, Vols I and II (Interscience, New York, 1958).
J. S. HANKER and B. L. GIAMMARA, Science 242 (1988) 885.
M. JARCHO, Clin. Orthopaed. Related Res. 157 (1981) 259.
C. LAVERNIA and J. M. SCHOENUNG, Ceram. Buli. 70 (1991) 95.
H. DENISSEN, C. MANGANO and G. VENINI, “Hydroxylapatite Implants” (Piccin Nuova Libraria, SPA, Padua, 1983) p. 19.
M. WINTER, P. GRISS, K.DE GROOT, H. TAGAI, G. HEIMKE, H. J. A. V. DIJK and K. SAWAI, Biomaterials 2 (1981) 159.
R. E. HOLMES and S. M. ROSER, Int. J. Oral Maxillofae. Surg. 16 (1987) 718.
J. W. FRAME, P. G. J. ROUT and R. M. BROWNE, Int. J. Oral. Maxillofae.Surg. 18 (1989) 142.
C. CHANG, V. J. MATUKAS and J. E. LEMONS, Int. J. Oral Maxillofae Surg. 41 (1983) 729.
G. L.DE LANGE, C.DE PUTTER, K.DE GROOT and F. H. BURGER. J. Dent. Res. 68 (1989) 509.
S.-Y. CHAO and C. K. POON, J. Oral Maxillofac. Surg. 45 (1987) 339.
D. G. PAGE and D. LASKIN, J. Oral Maxillofac. Surg. 45 (1987) 356.
K.DE GROOT, Biomaterials 1 (1980) 47.
J. C. TROMBE and G. MONTEL, J. Inorg. Nucl. Chem. 40 (1978) 15.
T. KIJIMA and M. TSUTSUMI, J. Amer. Ceram. Soc. 62 (1979) 455.
W.VAN RAEMDONCK, P. DUCHEYNE and P.DE MEESTER, in “Metal and Ceramic Biomaterials”, Vol. 2, edited by P. DUCHEYNE and W. HASTING (CRC Press, Boca Raton, Florida, 1984) p. 149.
H. NEWESELY, J. Oral Rehab. 4 (1977) 97.
K. YAMASHITA, H. OWADA, H. NAKAGAWA, T. UMEGAKE and T. KANAZAWA, J. Amer. Ceram. Soc. 69 (1986) 590.
M. JARCHO, C. H. BOLEN, M. B. THOMAS, J. BOBICK, J. F. KAY and R. H. DOREMUS, J. Mater. Sci. 11 (1976) 2027.
A. GEE and V. R. DEITZ, Analyt. Chem. 25 (1953) 1320.
Military Standard MIL-STD-1942 (MR): “Flexural Strength of High Performance Ceramics at Ambient Temperature” (Department of the Army, Washington, DC, 1983).
P. W. RANBY, D. H. MASH and S. T. HENDERSON, Brit. J. Appl. Phys. 8 (1957) S18.
W. L. HILL, G. T. FAUST and D. S. REYNOLDS, Amer. J. Sci. 242 (1944) 457.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Wang, P.E., Chaki, T.K. Sintering behaviour and mechanical properties of hydroxyapatite and dicalcium phosphate. J Mater Sci: Mater Med 4, 150–158 (1993). https://doi.org/10.1007/BF00120384
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00120384