Abstract
In recent scenarios, the development of nanotechnology with novel size, shape, and surface dependent properties has revealed incredible prospective for the treatment of environmental problems especially toxic heavy metals from contaminated water. As compared with traditional materials, a nanosized particle exhibits to a large extent efficiency and faster remediation rates in water treatment. Many kinds of nanomaterials such as carbon, nanometal/metal oxides, and polymer based have high selectivity and adsorption potential for the remediation of heavy metals/metalloids such as As5+, As3+, Pb2+, Cr3+, Cr6+, Hg2+, Co2+, Ni2+, Cd2+, and Cu2+ from contaminated water. This chapter gives a widespread analysis on the enduring research and progress activities in the field of remediation of toxic heavy metals/metalloids from contaminated water by using nanomaterials in order to achieve environmental detoxification, using adsorption process. We have also discussed the essential aspects of heavy metals problems on environment; their effects on human health through polluted water are reviewed.
Access provided by CONRICYT-eBooks. Download chapter PDF
Similar content being viewed by others
Keywords
3.1 Introduction
Water is the most valuable substance on this earth. All the life entities need water to survive. Without water then there would be no life on the earth. Drinking water quality is a common concern for people all over the world. We can survive days or even weeks without food, but cannot survive for long without water. Water quantity and quality is an important issue for public health. It is a well-known fact that clean drinking water is absolutely essential for healthy living. Water covered 326 million cubic miles on the Earth; however, only 3/10,000 is fresh water that can use for bathing, washing, cooking, and drinking. The rest percent is sheltered in oceans, icecaps glaciers, atmosphere, and ground water. But this 3% of water is also getting polluted by human deeds.
The contagion of water bodies such as oceans, rivers, aquifers, lakes, oceans, and groundwater is called water pollution. This water pollution occurs when pollutants are directly or indirectly discharged into natural water without proper treatment. Water pollution not only affects plants and animals but also affect the aquatic life. Approximately, the effect of water pollution is dangerous not only to human beings but also to the entire biosphere communities [1,2,3]. The problem of water pollution becoming severe day by day due to increase in population and increasing industrial activities. Many areas of surface water and groundwater are now contaminated with pathogens, harmful chemicals, and toxic heavy metals. Worldwide diseases like cancer, congenital malformation, and endocrine disturbances are associated with the contaminated drinking water.
Heavy metal toxicity is one of the leading problems in the current industrialized era. Wastewater from numerous industries, tanneries, battery manufacturing, metallurgical activities, electroplating, chemical manufacturing, and mining industries hold huge quantity of heavy metal ions [4, 5]. These wastewaters are discharged into water bodies directly, threatening not only the aquatic organisms, but also harming human and animals through their food chain. In numerous parts of the world, heavy metal concentration in drinking water is higher than the international guidelines values provided by the World Health Organization (WHO) and Bureau of Indian Standard (BIS).
Heavy metal is defining by the density of the metals in most of the cases. It is, thus, defined as those metals having a specific density in excess of 5 g/cm3 and toxic even in low concentration in contact with water and can have lethal effect on human bodies [6, 7]. It has been reported that about 1.6 million children die every year by consuming contaminated water. In the country like India, 80% of people are dying because of drinking toxic heavy metal contaminated water [6, 7]. The effects of these metals on human health are regularly reviewed by global bodies such as the World Health Organization [WHO]. Thus, the elimination of heavy metal ions from water bodies is vital to safeguard the environment and public health. To improve the quality of drinking water, the development of sustainable and robust technologies, chips, etc., has become of fundamental importance.
Several methods have been introduced to eradicate heavy metal ions from water such as chemical precipitation [8], membrane filtration [9], ion exchange [10], reverse osmosis [11], extraction [12], electrochemical treatment techniques [13], irradiation [14], coagulation [15], and adsorption [16]. But adsorption [17] shows most potential method to eliminate heavy metal ions from water as compared to others due to being inexpensive and extremely flexible. Carbon, zeolites, clay minerals, and chitosan have been explored for the adsorption of heavy metals by numerous researchers but the less adsorption ability and elimination competence restricts its application.
Current advancement in nanotechnology provides a hopeful way to resolve the environmental problems and offers protective dealings for future problems resulting from the exchanges of energy and resources with the environment [18, 19]. The most important environmental applications of nanotechnology could be elimination of toxic heavy metals ions from polluted water.
The major demerits of traditional sorbents in removal of heavy metals from wastewater could be solved by nanostructured materials. These nanomaterials have size ranging from 1 to 100 nm. As compared with traditional materials, nanomaterials show advanced effectiveness and quicker adsorption rates of heavy metals due to its novel size, large surface area, and shape dependent properties resulting in high reactivity to various heavy metals ions.
3.2 Heavy Metals/Metalloids and Their Sources
Water pollution caused by hazardous heavy metals and metalloids can occur from both natural as well as anthropogenic sources [20, 21]. Commonly known natural sources of heavy metals are mainly volcanic activities, rocks, ore minerals that are hidden in the crust, forest fires, etc., [21]. Anthropogenic sources of heavy metals pollution are increasing due to industrial waste, use of fertilizers, pesticides, sewage sludge, mining, combustion of coal and other fossil fuels. The toxic waste occurs due to both industrial production and end-used products landing into water bodies. Many industries like metal smelting, leather tanning, semiconductor, chemical manufacturing, etc., directly discharge heavy metal ions contaminated wastewater into natural water without adequate treatment [20, 21]. Thus, industrialized countries are more often faced with the impact of toxic heavy metals. Table 3.1 provides the anthropogenic sources of heavy metal pollutants provided by Dr. Gautam SP, CPCB New Delhi [22].
As discussed above about the sources of pollution by toxic heavy metals into the environment, mining is yet another such major source. There are many reports in this regard. For example, the effluents released in water bodies from Zawar mines in Udaipur district found to have higher levels of hazardous zinc and lead [23] causing toxicity of water. In another study by Shulka [24] of the water samples of northeast coalfield region of Chhattisgarh, it was found that level of cadmium, lead, iron, zinc, chromium, copper in the water was beyond the permissible limit. Hu et al. [25] have reported extensively in their study on the pollution of heavy metals in China. Their study suggests mining is one of the prime reasons of the heavy metal pollution in China. In gold mining, mercury (Hg) is used for amalgamation of gold. Most of the mercury is removed in this process and reused; however, some of the mercury enters in the river system. The gold mining activity is prime reason for the Amazon basin system to pollute [26].
Since ages, the agriculture has remained a prime economic activity for human beings to survive. Because of the ever increasing population, the demand for food is increasing at rapid rate, therefore, need to produce more is need of hour. In order to produce more, the increase in use of fertilizers and pesticides have taken place. For healthy growth of crops, heavy metals like Cu, Zn, Mo, Ni, Fe, Mn, and Co are also essential apart from macronutrient like N, P, K, etc. The compounds via which these elements are supplied also contain some amount of Cd and Pb, which upon prolonged use are deposited in the soil [27]. These metals enter the ground water via interconnection between soil and groundwater and hence causing water pollution [26].
Biosolid waste is another source of heavy metal contamination to the soil and hence the groundwater and water bodies. Biosolids like livestock manure, sewage sludge, etc., contain heavy metals such as Sb, Cr, Cd, and As. When these solids are used over the land in the activities such as agriculture, then over a period of time they could accumulate and hence may contaminate water [23].
3.3 Effects of Heavy Metals/Metalloid in Human Health
Heavy metals are very dangerous for both human health and aquatic life, if, it crosses the maximum permissible limit because heavy metals are inclined to bioaccumulate [28]. Bioaccumulation indicates an increase of a chemical in living bodies eventually, compared to the concentration of chemicals in the environment [28]. Accumulation of heavy metals in living things is faster in rate than the substance is lost by catabolism and excretion. Five most common heavy metals that are very toxic to both human and aquatic life even at low concentration and reviewed by WHO many times which are discussed in brief are: lead, cadmium, chromium, mercury, and arsenic [29, 30]. Severe exposures to heavy metals have been known and it continues to grow unabated in many parts of the world. Particularly, the exposure is increasing in less developed countries like Pakistan, India, and Bangladesh [22]. Too much of heavy metal consumption can damage different systems of the body together with the reproductive system, nervous, kidneys and it can cause cancer, high blood pressure, and anemia [30, 31]. The symptoms consist of headache, abdominal pain, irritability, confusion, and in severe cases it can cause coma, seizures, and death [5, 31, 32].
Arsenic is classified as a heavy metal but it is actually a metalloid. It is abundant in our environment with both natural and anthropogenic sources [33, 34]. In water, arsenic has leading forms of inorganic species such as arsenate [As5+] and arsenite [As3+] [33, 34]. Maximum permissible limit of arsenic in drinking water set by the WHO and BIS is at 0.01 mg/L [35, 36]. Arsenic consumption is mostly due to intake of seafood and drinking water. Its long-standing exposure enhances risk of skin cancer, lesions, hyperkeratosis, and pigmentation changes [37, 38]. Results show occasional exposure to arsenic can have risk of lung cancer [38].
Lead is a poisonous heavy metal that is dangerous to human health. In contact with water, lead is colorless, odorless, and tasteless. In drinking water, the maximum permissible limit of lead set by the WHO and the BIS is 0.01 mg/L [35, 36]. In child, the high level of lead exposure can result with neurological damage, coma, organ failure, and ultimately death [39]. The exposure in low level can affect learning disabilities; inhibit growth, and hearing loss [31, 39]. The symptoms show poor appetite, vomiting, sleep disorder, cramps, irritability, fatigue, and constipation [39]. It can easily accumulate within the body for a long time, i.e., bioaccumulate [21], which possibly is stored in the kidney, bones, brain, and other main organs. Lead can also store in the blood and bones of child’s for several decades [31, 39].
Mercury is exceptionally toxic heavy metals and it must be handled properly. The permissible limit of mercury in drinking water set by the WHO and the BIS is at 0.006 mg/L and 0.001 mg/L, respectively [35, 36]. The exposure of mercury can harm the nervous system, impair hearing, speech, vision and gait, involuntary muscle movements, corrodes skin, and mucous membranes. It can also cause the problem of chewing and swallowing of food [40]. In India, the general population is exposed to mercury due to intake of seafood and drinking contaminated water [41]. The pregnant women need to avoid a high intake of seafood, such as fish, shark, tuna, and swordfish, taken from polluted waters [40].
The maximum permissible limit of cadmium in drinking water set by the WHO and BIS is at 0.003 mg/L [35, 36]. It was first reported in Japan that extended exposure of cadmium might give rise to dangerous bone disease, called itai-itai (“ouch-ouch”). It was first reported from the Jinzu river basin in Japan [29, 31]. Cadmium exposure can also lead to harmful effects such as renal damage, emphysema, chronic disorders, and skeletal malformation in fetus, hypertension, kidney damage, and testicular atrophy [29]. Cadmium is also considered as carcinogenic reported by the International Agency for Research on Cancer (IARC, 1993). The IARC’s study was based on occupationally exposed workers [31]. In India, many people have already exceeding cadmium exposure levels, and the edge is very thin. Therefore, proper treatment should be taken to decrease the cadmium hazard to diminish the unpleasant health effects.
In contact with water, chromium forms two stable oxidation states, Cr3+ and Cr6+ [42]. Cr6+ is far more poisonous than Cr3+ to living things for its carcinogenicity, toxicity, and high aqueous solubility. Currently, the WHO has set a permissible limit for chromium in drinking water at 0.1 mg/L and the BIS at 0.05 mg/L [35, 36]. The exposures to Cr6+ occasinally raises the risk of cancers in the respiratory system. Zhang and Li [43] recently reported that in China (resident in the Liaoning), the death due to stomach cancers increased. The reasons behind this are drinking water in resident Liaoning was greatly contaminated with Cr6+ which are released by the ore smelting industries.
Copper is a reddish metal and is a crucial element for all the living organisms. It is vital in diet to assure good health. On the other hand, too much absorption of copper can be root of adverse health effects, including stomach cramps, nausea, vomiting, diarrhea, etc., [44]. It has also been reported that too much exposure of copper can cause liver and kidney damage [31]. In drinking water, the maximum permissible limit of copper set by the WHO is at 2 mg/L and by the BIS is at 0.05 mg/L [35, 36]. Therefore, removal of these heavy metals is very necessary for clean and healthy environment. Table 3.2 provides the maximum permissible limits of heavy metals set by the WHO and BIS in drinking water (Sources provided by the WHO and BIS). Figure 3.1 shows the six hazardous heavy metals in drinking water.
3.4 Nanomaterials as Adsorbent for Heavy Metals/Metalloids
Nanomaterials as sorbents for elimination of heavy metals/metalloids ions from wastewater should have following criteria. The nanosorbents should be nontoxic and have high sorption capacities. The adsorbed metal ions could be detached easily from the surface of the nanoadsorbents and could be infinitely recycled [29]. So far, a varieties of nanomaterials such as carbon, metal and metal oxides, and polymer supported nanoadsorbents have been studied for the removal of heavy metal from water, and the results indicate that highest explored nanoadsorbents were carbon, nanozero-valent iron and iron oxide-based nanoadsorbents due to their large surface area volume ratio, low cost, easy availability, nontoxic, and recyclable [29, 45]. Few metal oxide nanoadsorbents such as TiO2, CeO, MnO, and AlO were also explored for the removal of heavy metals from water [46]. Polymer supported nanoadsorbents have also been explored by the researcher in this field [47]. Figure 3.2 shows the pie chart of explored utilization of different nanomaterials as sorbents for heavy metal remediation from water.
3.4.1 Carbon-Based Nanomaterials
Undoubtedly, carbon-based nanomaterials are the most admired and broadly used adsorbent for the applications in wastewater treatment all over the world. In recent decades, carbon-based adsorbent [48] is extensively used for the removal of heavy metals from waste water due to its nontoxic, low-cost, and high sorption capacities [6]. Firstly, activated carbon was used as sorbents for heavy metal remediation but have demerits to remove heavy metals at ppm [parts per million (mg/L)] level [6]. To overcome these demerits, nanotechnology recently designs graphene, carbon nanotubes, and fullerene used as nanosorbents for the remediation of heavy metals [6, 48].
Lijima was the first who discovered carbon nanotubes (CNTs). Owing to their exclusive structural, mechanical, optoelectronic, semiconducting, electronic, chemical, and physical properties, CNTs have been used extensively to eliminate heavy metals from wastewater [6]. CNTs have two forms, single-walled carbon nanotubes (SWCNTs) and multi-walled carbon nanotubes (MWCNTs). Many studies have revealed that CNTs have outstanding adsorption capacity and have high adsorption effectiveness for various heavy metals as compared with other adsorbent [49, 50]. Li et al. [49] have reported CTNs have excellent adsorption capacity for Pb2+ from water. Li et al. [50] again reported thermodynamics studies of Pb2+ adsorption on carbon nanotubes in a range of temperatures; 280, 298, and 321 K and calculate all the thermodynamic constant such as equilibrium constant, standard entropy change, and standard-free energy. The desorption result also reveals that Pb2+ can be removed easily from CNTs by varying the solution pH using HNO3 and HCl, which signifies that CNTs can be reused again. Hu et al. [51] reported chromium removal using oxidized MWCNTs. The result indicates that chromium adsorption mostly depends on the redox reaction of Cr6+ ions on the surface of oxidized MWCNTs to form Cr3+, and ensuing Cr3+ sorption on MWCNTs appears as the foremost mechanism for the uptake of chromium on MWCNTs.
Pillay et al. [52] reported the adsorption capabilities of Cr6+ using three carbon-based adsorbents that are: activated carbon, functionalized MWCNTs, and unfunctionalized MWCNTs. The results revealed that unfunctionalized MWCNTs showed the highest adsorption capability with up to 98% out of 100 mg/L of Cr6+ solution being adsorbed. Pyrzyńska and Bystrzejewski [53] reported comparative study of heavy metals ion Co2+ and Cu2+ adsorption onto activated carbon, carbon nanotubes, and carbon-encapsulated magnetic nanoparticles. The results indicate CNTs have less sorption capacity as compared with carbon nanomaterials. In the meantime, Stafiej and Pyrzynska [54] reported solution pH, including metal ions concentrations, could affect the adsorption distinctiveness of CNTs, and the experimental data agreed well with the Freundlich adsorption isotherm model. Kosa et al. [55] reported modified carbon nanotubes with 8-hydroxyquinoline and used it for the removal of Cu2+, Pb2+, Cd2+, and Zn2+. The results revealed that the modification of CNTs with 8-hydroxyquinoline improved the removal efficiency of heavy metals.
Graphene is an additional parts of carbon nanomaterials, having one or more atomic layered graphite. It has two-dimensional structure having excellent thermal and mechanical properties. Zhao et al. [56] reported synthesis of few-layered graphene oxide nanosheets using modified Hummers method and used these graphene nanosheets as sorbents for the elimination of Cd2+ and Co2+ ions from water. The results signify that sorption of heavy metal on graphene nanosheets is dependent on solution pH, ionic strength, and the abundant oxygen-containing functional groups on the surfaces of graphene oxide nanosheets. Zhang et al. [57] reported composites graphene oxide/magnetite (GO/Fe3O4) synthesized via a copper catalyzed azidealkyne cyclo addition reaction. Further, GO/Fe3O4 was modified with polyacrylic acid (PAA) to obtain PAA/GO/Fe3O4 which was used for the removal of Cu2+, Cd2+, and Pb2+ ions from water. It is found that the PAA/GO/Fe3O4 nanocomposite shows extraordinary removal effectiveness for Cu2+, Cd2+, and Pb2+ ions. Chandra et al. [58] reported a size of 10 nm magnetite-graphene adsorbents for the removal of As3+ and As5+ from water. The outcome signifies the high uptake of arsenic as a result of the increased adsorption sites in composite of graphene. Yang et al. [59] reported aggregation of Graphene oxide (GO) by Cu2+ in aqueous solution, indicates enormous Cu2+ absorption capacity. The study characterized by atomic force microscopy and confocal microscopy reported that Cu2+ ions folded GO sheets and creates large aggregation along with increased adsorption sites. The results demonstrate 10 times adsorption capacity then activated carbon. Table 3.3 shows the carbon-based nanoadsorbents explored for the remediation of heavy metals from water. Figure 3.3 shows the different shapes of carbon-based nanoadsorbents.
3.4.2 Nanosized Metal and Metal Oxides
Recently, metal and metal oxide nanoadsorbents (NMO) such as nanosized zero-valent iron (NZVI), ferric oxides, titanium oxides, cerium oxides, manganese oxides, aluminum oxides were explored as the most gifted adsorbent for the remediation of heavy metals from water [45, 46, 60,61,62,63,64]. The motivation behind this is due to their large surface areas and high adsorption capacity caused by the size-quantization effect [65, 66]. The study reported that NMOs show evidence of very favorable sorption to heavy metals in terms of high capacity and selectivity. On the other hand, the surface energy increases as the size of NMOs decreases from micrometer to nanometer levels, which reduces their stability. Therefore, NMOs can easily aggregate due to Van der Waals forces and other interactions [66], which very much decreases the high adsorption capacity and selectivity of NMOs. Additionally, NMOs have poor mechanical strength and too much pressure drops which leads to unfeasible in fixed beds. To overcome this all problems, many researchers have impregnated NMOs into porous supports to obtain composite nanoadsorbents [47], which include amino acids, polymers, activated carbon, natural materials, etc. Above and beyond as compared with all traditional NMOs, magnetic nanoadsorbents create a center of attention because of their large surface area, ecofriendly, availability, low cost and it can be simply separated from water applying magnetic field [60, 61]. Furthermore, magnetic composite adsorbents can easily be regenerated or recycled [61], which reduces the cost of wastewater management (Fig. 3.3).
3.4.2.1 Iron-Based Nanoparticles as Nanoadsorbents for Heavy Metals
The exploitation of iron-based nanoadsorbents have been acknowledged to a great extent in the field of heavy metals remediation from water due to their exceptional properties, for instance small size, high surface area to volume ratio, ecofriendly, excellent magnetic properties, and great ability of surface modification.
Zero-Valent Iron: Among all the metal/metal oxide nanomaterials, nanoscale zero-valent iron (NZVI) has distinguished itself by its unique properties that include low cost, low toxicity, ecofriendly, larger surface to volume ratio, diminish the chemicals consumption, no secondary pollutant, strong adsorption ability, and easy separation under external magnetic field [60, 67]. Therefore, these properties make NZVI as the excellent adsorbent for the treatment of heavy metals from water. Ponder et al. [67] reported quick removal of Cr6+ and Pb2+ from aqueous solution using supported NZVI (“Ferragels”). The result indicates supported NZVI, while oxidizing the Fe to goethite (R-FeOOH) reduced the Cr to Cr3+ and the Pb to Pb0. Kanel et al. [33, 34] reported that NZVI rapidly removes As3+ and As5+ from groundwater. The maximum adsorption capacity of As3+ obtained from Freundlich adsorption model was 3.5 mg/g. Boparai et al. [68] investigated NZVI for the removal of Cd2+ (conc. range 25–450 mg/L). The results recommend the competent removal of Cd2+ from contaminated water. Zhang et al. [69] reported that NZVI has limitation to remediate contaminated groundwater due to lack of durability and mechanical strength. To overcome these problems, NZVI was loaded onto kaolinite as a support material (K-NZVI) and used for the remediation of Pb2+ from water. The results show 96% of Pb2+ was removed within 30 min using 10 g/L K-NZVI in 500 mg/L Pb2+. Kim et al. [70] reported the Zeolite supported NZVI for the removal of Pb2+ from aqueous water and the results designated immense potential of Pb2+ elimination from water. Su et al. [71] reported the removal of NZVI to the co-contaminants Cd2+ and nitrates. The result indicates increase in solution pH and negative charge of NZVI increases the removal of Cd2+ from 40 to 188 mg/g with nitrate present and 30% of nitrate was reduced by NZVI within 2 h. Liu et al. [43] reported NZVI supported on pumice (P-NZVI) successfully removed Hg2+ and Cr6+ from wastewater. The maximum uptake of Hg2+ and Cr6+ onto P-NZVI was 332.4 and 306.6 mg/g, respectively. Table 3.4 shows the NZVI adsorbents for the removal of heavy metals from water.
Iron Oxide-based nanoadsorbents exist in various forms in nature such as Goethite (γ-FeOOH), Maghemite (γ-Fe2O3), Hematite (α-Fe2O3), and Magnetite (Fe3O4) [72]. Recently, the majority of research for the applications of wastewater treatment has focused on iron oxide nanoadsorbents [72, 73]. Nasser [73] reported the maximum adsorption capacity for Pb2+ ions was obtained as 36.0 mg/g by Fe3O4 NPs, which was much higher than that of reported low-cost adsorbents. The small size of Fe3O4 NPs was favorable for the diffusion of metal ions from solution on to the active sites of the adsorbents surface. The result indicates that Fe3O4 nanosorbents were effective and economical adsorbents for rapid removal and recovery of metal ions from wastewater effluents. Sarkar and Sarkar [74] investigated the applicability of polyethylene glycol (PEG-4000) coated Fe3O4 magnetic nanoparticles for the selective removal of toxic Pb2+ ion from wastewater. The result indicates maximum adsorption of Pb2+ at optimum pH 6, and the equilibrium contact time is 10 min. Wang et al. [75] reported synthesized water-soluble Fe3O4 NPs through a hydrothermal method and found excellent removal of Pb2+ and Cr6+ ions from waste water. The result indicates more than 90% of Pb2+ and Cr6+ ions were removed within 2 min.
Xin et al. [76] reported amine-functionalized mesoporous Fe3O4 NPs (AF-Fe3O4) used for the removal of Pb2+, Cd2+, and Cu2+ ions from water. The result indicates the adsorption of these heavy metals agreed well with Langmuir isotherm model and the maximum adsorption capacities for Pb2+, Cd2+, and Cu2+ from 369.0 to 523.6 mg/g, which is superior to other reported work. Liu et al. [77] reported Humic acid (HA) coated Fe3O4 NPs (Fe3O4/HA) successfully removed toxic heavy metals Hg2+, Pb2+, Cd2+, and Cu2+ from water. The maximum removal efficiency of the heavy metals reached equilibrium within 15 min, and agreed well with Langmuir isotherm adsorption with maximum uptake from 46.3 to 97.7 mg/g. The result indicates 99% removal of Hg2+, Pb2+, and almost 95% of Cd2+, and Cu2+. Bagbi et al. [78] reported monodispersed Fe3O4 NPs synthesized by chemical co-precipitation and used for successful removal of Pb2+ from water (Fig. 3.4). The result indicated 100% removal of Pb2+ within 30 min. Pseudo-second-order rate equation shows better fitted data. Spent Fe3O4 NPs were regenerated using 0.005 M HNO3. Grossl et al. [79] investigate Cu2+ adsorption/desorption studies using goethite (a-FeOOH) NPs applying pressure-jump relaxation technique. The relaxations rate of Cu2+ decreased with an increase in pH. The results indicate that the rate of adsorption of divalent metal cations on goethite was directly related to the rate of removal of a water molecule from the primary hydration sphere of a particular divalent metal cation. Chen et al. used Goethite and hematite nanoadsorbents for the removal of Cu2+. It was reported that both the nanoadsorbents show high adsorption uptake of Cu2+ [80]. The obtained maximum adsorption capacity of Cu2+ is 149.25 and 84.46 mg/g for goethite and hematite nanoadsorbents, respectively. It also indicates that adsorption of Cu2+ was fitted well with Langmuir adsorption isotherm as compared with Freundlich model. Hu et al. [81] investigated maghemite NPs for the removal of Cr6+ from waste water. The removal of heavy metal was very fast and within 15 min adsorption equilibrium reached. The adsorption data were analyzed and fitted well by Freundlich isotherm. Cr6+ adsorption capacity of maghemite nanoparticles was compared favorably with other adsorbents like activated carbon and clay. Regeneration studies of maghemite underwent six successive adsorption desorption processes. Hu et al. [82] reported the applicability of maghemite (γ-Fe2O3) NPs for the removal of Cr6+, Cu2+, and Ni2+ from electroplating wastewater. The result indicated adsorption of heavy metals reached equilibrium rapidly within 10 min and Langmuir adsorption isotherm fitted well. Regeneration studies of γ-Fe2O3 NPs adsorption desorption processes undergo successfully retained metal removal capacity.
3.4.2.2 Nanosized Titanium Oxides
Titanium dioxide (TiO2) was recently explored as the adsorbent for the application of heavy metals remediation from water. It has three different crystal structures such as anatase, rutile, and brookite. The brookite type cannot be used in industries due to its low stability at room temperature and rutile type is easily coagulated at room temperature and its band gap energy is larger than that of anatase type [83]. Therefore, anatase-type TiO2 used as an adsorbent to investigate the photo adsorption effect was selected. It was reported that bulk and nanoparticle TiO2 anatase exhibit different chemical behavior, catalytic reactivity, and surface acidity based on their different surface planes [83, 84]. Engates and Shipley [45] investigated adsorption of metals (Pb2+, Cd2+, Cu2+, Ni2+, Zn2+) using TiO2 nanoparticles and bulk particles. The result indicates successful removal of multiple metals (Pb2+, Cd2+, Cu2+, Ni2+, Zn2+) at solution pH 8 and spiked San Antonio tap water.
Liang et al. [85] investigated new method using TiO2 nanoadsorbents as solid-phase extractant coupled with Flame atomic absorption spectrometry (FAAS) was proposed for preconcentration and determination of trace Zn2+ and Cd2+. The removal of Zn2+ and Cd2+ at different pH, contact time, elution solution and interfering ions was investigated. Kim et al. [83] performed an experiment for the removal of Cu2+ using suspended anatase-type titanium dioxide nanoadsorbents. The adsorption amount increased rapidly with an increasing solution pH and temperature. The obtained adsorption equilibrium constant (Kads) was 0.854 and adsorption isotherm of Cu2+ adsorption fitted well to Langmuir adsorption isotherm. Skubal et al. (2002) reported removal of aqueous Cd2+ from waste water using TiO2 nanoadsorbents [86]. More than 90% of Cd2+ was removed by both adsorption and reduction processes onto the TLA-modified TiO2. These removal and reduction processes were catalytic in nature.
3.4.2.3 Nanosized Cerium Oxides
Nano cerium oxides (CeO2) have been explored as the excellent nanoadsorbents for heavy metals removal from water due to specific surface area, less toxicity, good catalytic activity [87], blue shift in absorption spectra [88], lattice expansion [88], phase transformation [89], and photovoltaic response [90]. Cao et al. [91] developed, hollow ceria nanospheres via microwave assisted hydrothermal method. These ceria hollow nanospheres then were examined for the removal of As5+ and Cr6+ from water. The obtained maximum adsorption capacity for As5+ is 22.4 mg/g and 15.4 mg/g Cr6+, and these values were extremely higher than other ceria nanostructures reported in data. Recillas et al. [92] investigated suspended CeO2 NPs stabilized with hexamethylenetetramine and used for the removal of dissolved chromium (VI) from water. Several concentrations of adsorbent and adsorbate were tested, trying to cover a large range of possible real conditions. These results can be used to propose this treatment sequence for a clean and simple removal of drinking water or wastewater reuse when a high toxicity heavy metal such as Cr6+ is responsible for water pollution. Di et al. [93] synthesized CeO2 NPs supported on aligned carbon nanotubes (ACNTs) nanoadsorbents and investigated these for the removal of Cr6+ from drinking water. The result indicated that CeO2/ACNTs nanoadsorbents show excellent adsorption of Cr6+ and the maximum adsorption capacity obtained as 30.2 mg/g. These studies put forward that CeO2/ACNTs have enormous prospective applications in water treatment.
Haron et al. [94] developed cerium modified zeolite P (CeZP) nanoadsorbents and used these for the removal of As5+ from aqueous solution. The sorption capacity increased with increasing temperature 25–90 °C. The adsorption of As5+ onto CeZP follows Langmuir model and the obtained maximum sorption capacity was 8.72 mg/g (25 °C) and increased to 23.42 mg/g (90 °C), indicating an endothermic process. The results show that nanoadsorbents’ CeZP has excellent removal efficiency of As5+ from wastewater (wood treatment industry).
3.4.2.4 Nanosized Magnesium Oxides
Recently, numerous works have focused on the synthesis of nanosized magnesium oxides (MgO) of various morphologies for the removal of heavy metals from water. Gao et al. (2008) reported a facile method to fabricate MgO of different morphologies and investigated their influence on the removal of Cr6+ and the result indicates excellent adsorption of Cr6+. Also the flowerlike morphology of mesoporous MgO was synthesized and investigated for the adsorption capabilities of Cd2+ and Pb2+ [95]. The concentration of Cd2+ and Pb2+ decreased from 100 to 0.007 and 0.05 mg/L, respectively (at equilibrium time: 120 min). It shows that removal of Cd2+ and Pb2+ using flowerlike MgO was much lower than the Pollutant Dischargeable Standard in China (Cd2+ < 0.01 mg/L, Pb2+ < 0.1 mg/L). Koivula et al. [96] reported the used of Cryptomelane type MnO for the removal of Cu2+ from wastewaters. The cryptomelane has ion exchange properties for weak acidic ion exchangers that show high-quality selectivity toward transition metals. This shows obtained capacity of 1.3 m mol/g for Cu2+ and distribution coefficient as high as ∼104 ml/g, promising future application for the removal of metal ions from water. Pakarinen et al. [97] reported two tunnel-structured oxides of nanoporous manganese oxides (OMS-1 and OMS-2) using hydrothermal method for the removal of metals ions and acid using kinetic measurements at different metal ion concentrations. This results show that OMS materials selectively adsorb Cu2+, Ni2+, and Cd2+ in the presence of Ca and Mg. The study shows that both the nanoadsorbents were stable and their maximum Cu2+ uptake capacity was obtained as 0.9–1.3 m mol/g.
3.4.2.5 Nanosized Aluminum Oxides
Recently, alumina (Al2O3) has been explored as the adsorbent for heavy metals, and α-Al2O3 is anticipated to be more adsorptive active than Al2O3 [98,99,100]. Its chemical or physical modification of γ-Al2O3 nanoparticles with certain functional groups shows donor atoms such as oxygen, nitrogen, sulfur, and phosphorus and is expected to improve their sorption toward heavy metals [100, 101]. Fan et al. [102] reported hydrous amorphous nanoadsorbents Al (HAO), Fe (HFO), and Mn (HMO) oxides show high affinity for heavy metal ions. These nanoadsorbents then have been investigated for the removal of Pb2+ from water, the results show excellent removal efficiency. Pu et al. [103] reported fixing γ-mercaptopropyl-trimethoxysilane (γ-MPTMS) on the surface of γ-Al2O3 improve its selectivity toward Cu, Hg, Au, and Pd ions rather than other ions. The mechanism responsible for the selectivity adsorption of metal ions was through the affinity of -SH group, the hydrolyzation of metal ions, and electrostatic adsorption. The result shows the obtained adsorption capacity of modified γ-Al2O3 nanoadsorbents were found as 10.4, 16.3, 15.3, and 17.4 mg/g for Hg, Cu, Au, and Pd, respectively. Furthermore, Afkhami et al. [104] reported nanoγ-Al2O3-coated sodium dodecyl sulfate modified with 2, 4-dinitrophenylhydrazine (DNPH) was used as adsorbent for removal of heavy metals Pb2+, Cr3+, Cd2+, Ni2+, Co2+, and Mn2+. The result indicates that Freundlich isotherms sorption model fitted well for the adsorption of Mn2+, Pb2+, Cr3+, and Cd2+, ions whereas, Langmuir model fitted well for Ni2+ and Co2+ ions. The obtained maximum Langmuir adsorption capacity values for Pb2+, Cr3+, and Cd2+ ions were 100, 83.33 and 100 mg/g, respectively. Table 3.5 shows various nanoadsorbents for the removal of heavy metals/metalloids from water.
3.5 Polymer and Amino Acid Supported Nanomaterials for Heavy Metals/Metalloid
The fast adsorption and high uptake of heavy metals of nanoadsorbents mainly depend on functional groups and large surface area [47, 105]. Metal and metal oxide and carbon-based nanomaterials have high surface area but don’t have to adsorb functional group. To overcome these problems, organic polymer, polyphenylenediamine, holds a large amount of polyfunctional groups (amino and imino groups) can effectively adsorb heavy metal ions, whereas their small specific area and low adsorption rate limit their application [47]. Therefore, new sorbents with both polyfunctional groups and high surface area are still expected. The development of hybrid sorbents has opened up the new opportunities of their application in fast removal of heavy metals from water [47, 106]. Chen et al. [107] prepared magnetite coated 3-aminopropyl trimethoxysilane (APTES). Then, the modified nanoparticles further grated by different heterocyclic groups (HCG) (Fe3O4@SiO2-NH-HCGs). This Fe3O4@SiO2-NH-HCGs were used for the removal of heavy metal cations such as Cu2+, Hg2+, Pb2+, and Cd2+. The result shows 96% removal of heavy metals within 20 min at normal temperature and has good stability and reusability.
Huang and Chen [108] investigated magnetic nanoadsorbent by the covalent binding of polyacrylic acid (PAA) on the surface of Fe3O4 nanoparticles and then followed amino-functionalization using diethylenetriamine (DETA) via carbodiimide activation. This amino-functionalized magnetic nano-adsorbent shows excellent capability for the rapid and efficient adsorption of metal cations and anions from aqueous solutions via the chelation or ion exchange mechanisms. The maximum adsorption capacities and Langmuir adsorption constants were 12.43 mg/g and 0.06 L/mg for Cu2+ and 11.24 mg/g and 0.0165 L/mg for Cr6+, respectively.
Cai et al. [109] used polyacrylic acid stabilized amorphous calcium carbonate nanoparticles and used it for the application of heavy metal removal from water. The maximum removal capacities for Cd2+, Pb2+, Cr3+, Fe3+, and Ni2+ ions were found to be 514.62, 1028.21, 258.85, 320.5, and 537.2 mg/g, respectively.
Pavlidou and Papaspyrides [110] reported a review on recent advances in the field of polymer-layered silicate nanocomposite. These nanocomposites have attracted both academic and industrial attention because they exhibited dramatic improvement in properties at very low filler contents.
Liu et al. [111] reported hybrid polymers from the ring-opening polymerization of pyromellitic acid dianhydride (PMDA) and phenylaminomethyl trimethoxysilane (PAMTMS) and used it for the removal of Cu2+ and Pb2+ from water. The result indicates excellent removal efficiency due to novel size and shape dependent properties of nanoparticles. Table 3.6 shows the polymer-based nanoadsorbents.
3.6 Conclusion
Recent development in nanotechnology has provided much more opportunities to develop nontoxic, cost-effective and environmentally friendly water treatment technology. Nanomaterials have blessed with a numerous numbers of physicochemical properties that make them attractive for wastewater purification. Many researchers have investigated nanomaterials as sorbents and reported that it is best tools for heavy metal removal, due to their small size unique structure and surface modification. These nanomaterials rapidly remove heavy metals/metalloids ions even at low concentration, with high selectivity and adsorption capacity. The exploitation of new efficient adsorption materials is essential and will continue infinitely, the future of nanomaterials in removal heavy metal ions in wastewater treatment is fairly bright.
References
X. Qu, P.J. Alvarez, Q. Li, Applications of nanotechnology in water and wastewater treatment. Water Res. 47(12), 3931–3946 (2013)
T. Rajeswari, N. Sailaja, Impact of heavy metals on environmental pollution. J. Chem. Pharm. Sci. 42(3), 175–181 (2014)
R. Kundra, R. Sachdeva, S. Attar, M. P, Studies on the removal of heavy metal ions from industrial waste water by using titanium electrodes. J Curr. Chem. Pharm. Sc. 2(1), 11 (2012)
M. Jamil, M.S. Zia, M. Qasim, Contamination of agro-ecosystem and human health hazards from wastewater used for irrigation. J. Chem. Soc. Pak. 32(3), 370–378 (2010)
S. Khan, Q. Cao, Y. Zheng, Y. Huang, Y. Zhu, Health risks of heavy metals in contaminated soils and food crops irrigated with wastewater in Beijing. China. Environ. pollut. 152(3), 686–692 (2008)
M.S. Mauter, M. Elimelech, Environmental applications of carbon-based nanomaterials. Environ. Sci. Technol. 42(16), 5843–5859 (2008)
F. Fu, Q. Wang, Removal of heavy metal ions from wastewaters: a review. J. Environ. Manage. 92(3), 407–418 (2011)
L.K. Wang, Y.-T. Hung, N.K. Shammas, Physicochemical treatment processes (Springer, 2005)
M.E. Ersahin, H. Ozgun, R.K. Dereli, I. Ozturk, K. Roest, J.B. van Lier, A review on dynamic membrane filtration: materials, applications and future perspectives. Biores. Technol. 122, 196–206 (2012)
Y. Xing, X. Chen, D. Wang, Electrically regenerated ion exchange for removal and recovery of Cr (VI) from wastewater. Environ. Sci. Technol. 41(4), 1439–1443 (2007)
A. Bodalo-Santoyo, J. Gómez-Carrasco, E. Gomez-Gomez, F. Maximo-Martin, A. Hidalgo-Montesinos, Application of reverse osmosis to reduce pollutants present in industrial wastewater. Desalination 155(2), 101–108 (2003)
I. Rykowska, W. Wasiak, J. Byra, Extraction of copper ions using silica gel with chemically modified surface. Chem. Pap. 62(3), 255–259 (2008)
F.C. Walsh, G.W. Reade, Electrochemical techniques for the treatment of dilute metal-ion solutions. Stud. Environ. Sci. 59, 3–44 (1994)
G. Batley, Y. Farrar, Irradiation techniques for the release of bound heavy metals in natural waters and blood. Anal. Chim. Acta 99(2), 283–292 (1978)
P. Zhang, H.H. Hahn, E. Hoffmann, Different behavior of iron (III) and aluminum (III) salts to coagulate silica particle suspension. Acta Hydrochim. Hydrobiol. 31(2), 145–151 (2003)
V. Srivastava, C. Weng, V. Singh, Y. Sharma, Adsorption of nickel ions from aqueous solutions by nano alumina: kinetic, mass transfer, and equilibrium studies. J. Chem. Eng. Data 56(4), 1414–1422 (2011)
D. Zamboulis, E.N. Peleka, N.K. Lazaridis, K.A. Matis, Metal ion separation and recovery from environmental sources using various flotation and sorption techniques. J. Chem. Technol. Biotechnol. 86(3), 335–344 (2011)
J. Lee, S. Mahendra, P.J. Alvarez, Nanomaterials in the construction industry: a review of their applications and environmental health and safety considerations. ACS Nano 4(7), 3580–3590 (2010)
I. Ali, New generation adsorbents for water treatment. Chem. Rev. 112(10), 5073–5091 (2012)
H. Pekey, D. Karakaş, M. Bakoglu, Source apportionment of trace metals in surface waters of a polluted stream using multivariate statistical analyses. Mar. Pollut. Bull. 49(9), 809–818 (2004)
R. Verma, P. Dwivedi, Heavy metal water pollution-A case study. Recent Res. Sci. Technol. 5(5) (2013)
B.Z. Marg, in Hazardous metals and minerals pollution in India: Sources, toxicity and management, (A position paper, Indian National Science Academy, New Delhi, 2011)
S.K. Agarwal, Heavy metal pollution (APH publishing, India, 2009)
A.K. Shukla, Toxicity of heavy metals in the water samples of North-Eastern coal field region of Chhattisgarh. Dermatitis 5(25), 20 (2014)
H. Hu, Q. Jin, P. Kavan, A study of heavy metal pollution in China: Current status, pollution-control policies and countermeasures. Sustainability 6(9), 5820–5838 (2014)
H. Bradl, Heavy metals in the environment: Origin, interaction and remediation (Academic Press, 2005)
R.A. Wuana, F.E. Okieimen, Heavy metals in contaminated soils: a review of sources, chemistry, risks and best available strategies for remediation. Isrn Ecol. (2011)
N. Pourang, Heavy metal bioaccumulation in different tissues of two fish species with regards to their feeding habits and trophic levels. Environ. Monit. Assess. 35(3), 207–219 (1995)
X. Wang, Y. Guo, L. Yang, M. Han, J. Zhao, X. Cheng, Nanomaterials as sorbents to remove heavy metal ions in wastewater treatment. J. Environ. Anal. Toxicol. (2012)
X. Wang, T. Sato, B. Xing, S. Tao, Health risks of heavy metals to the general public in Tianjin, China via consumption of vegetables and fish. Sci. Total Environ. 350(1), 28–37 (2005)
L. Järup, Hazards of heavy metal contamination. Br. Med. Bull. 68(1), 167–182 (2003)
J. Pronczuk, M. Bruné, F. Gore, Children’s environmental health in developing countries. Encycl. Environ. Health. 601–610 (2011)
S.R. Kanel, J.-M. Greneche, H. Choi, Arsenic (V) removal from groundwater using nano scale zero-valent iron as a colloidal reactive barrier material. Environ. Sci. Technol. 40(6), 2045–2050 (2006)
S.R. Kanel, B. Manning, L. Charlet, H. Choi, Removal of arsenic (III) from groundwater by nanoscale zero-valent iron. Environ. Sci. Technol. 39(5), 1291–1298 (2005)
W.H. Organization, Guidelines for drinking-water quality (World Health Organization, Geneva, 2011) 2011
(BIS) BOIS. Indian standard drinking water speciation. New Delhi 110002 (2012)
P. Smedley, D. Kinniburgh, A review of the source, behaviour and distribution of arsenic in natural waters. Appl. Geochem. 17(5), 517–568 (2002)
T.S. Choong, T. Chuah, Y. Robiah, F.G. Koay, I. Azni, Arsenic toxicity, health hazards and removal techniques from water: an overview. Desalination 217(1), 139–166 (2007)
R.A. Goyer, Lead toxicity: current concerns. Environ. Health Perspect. 100, 177 (1993)
H.E. Ratcliffe, G.M. Swanson, L.J. Fischer, Human exposure to mercury: a critical assessment of the evidence of adverse health effects. J. Toxicol. Environ. Health 49(3), 221–270 (1996)
M. Castro-González, M. Méndez-Armenta, Heavy metals: implications associated to fish consumption. Environ. Toxicol. Pharmacol. 26(3), 263–271 (2008)
X. Lv, J. Xu, G. Jiang, X. Xu, Removal of chromium (VI) from wastewater by nanoscale zero-valent iron particles supported on multiwalled carbon nanotubes. Chemosphere 85(7), 1204–1209 (2011)
T. Liu, Z.-L. Wang, X. Yan, B. Zhang, Removal of mercury (II) and chromium (VI) from wastewater using a new and effective composite: pumice-supported nanoscale zero-valent iron. Chem. Eng. J. 245, 34–40 (2014)
F. Pizarro, M. Olivares, R. Uauy, P. Contreras, A. Rebelo, V. Gidi, Acute gastrointestinal effects of graded levels of copper in drinking water. Environ. Health Perspect. 107(2), 117 (1999)
K.E. Engates, H.J. Shipley, Adsorption of Pb, Cd, Cu, Zn, and Ni to titanium dioxide nanoparticles: effect of particle size, solid concentration, and exhaustion. Environ. Sci. Pollut. Res. 18(3), 386–395 (2011)
M. Hua, S. Zhang, B. Pan, W. Zhang, L. Lv, Q. Zhang, Heavy metal removal from water/wastewater by nanosized metal oxides: a review. J. Hazard. Mater. 211, 317–331 (2012)
B. Pan, B. Pan, W. Zhang, L. Lv, Q. Zhang, S. Zheng, Development of polymeric and polymer-based hybrid adsorbents for pollutants removal from waters. Chem. Eng. J. 151(1), 19–29 (2009)
J. Ruparelia, S. Duttagupta, A. Chatterjee, S. Mukherji, Potential of carbon nanomaterials for removal of heavy metals from water. Desalination 232(1), 145–156 (2008)
Y.-H. Li, S. Wang, J. Wei, X. Zhang, C. Xu, Z. Luan et al., Lead adsorption on carbon nanotubes. Chem. Phys. Lett. 357(3), 263–266 (2002)
Y.-H. Li, Z. Di, J. Ding, D. Wu, Z. Luan, Y. Zhu, Adsorption thermodynamic, kinetic and desorption studies of Pb2+ on carbon nanotubes. Water Res. 39(4), 605–609 (2005)
J. Hu, C. Chen, X. Zhu, X. Wang, Removal of chromium from aqueous solution by using oxidized multiwalled carbon nanotubes. J. Hazard. Mater. 162(2), 1542–1550 (2009)
K. Pillay, E. Cukrowska, N. Coville, Multi-walled carbon nanotubes as adsorbents for the removal of parts per billion levels of hexavalent chromium from aqueous solution. J. Hazard. Mater. 166(2), 1067–1075 (2009)
K. Pyrzyńska, M. Bystrzejewski, Comparative study of heavy metal ions sorption onto activated carbon, carbon nanotubes, and carbon-encapsulated magnetic nanoparticles. Colloids Surf., A 362(1), 102–109 (2010)
A. Stafiej, K. Pyrzynska, Adsorption of heavy metal ions with carbon nanotubes. Sep. Purif. Technol. 58(1), 49–52 (2007)
S.A. Kosa, G. Al-Zhrani, M.A. Salam, Removal of heavy metals from aqueous solutions by multi-walled carbon nanotubes modified with 8-hydroxyquinoline. Chem. Eng. J. 181, 159–168 (2012)
G. Zhao, J. Li, X. Ren, C. Chen, X. Wang, Few-layered graphene oxide nanosheets as superior sorbents for heavy metal ion pollution management. Environ. Sci. Technol. 45(24), 10454–10462 (2011)
W. Zhang, X. Shi, Y. Zhang, W. Gu, B. Li, Y. Xian, Synthesis of water-soluble magnetic graphene nanocomposites for recyclable removal of heavy metal ions. J. Mater. Chem. A. 1(5), 1745–1753 (2013)
V. Chandra, J. Park, Y. Chun, J.W. Lee, I.-C. Hwang, K.S. Kim, Water-dispersible magnetite-reduced graphene oxide composites for arsenic removal. ACS Nano 4(7), 3979–3986 (2010)
S.-T. Yang, Y. Chang, H. Wang, G. Liu, S. Chen, Y. Wang et al., Folding/aggregation of graphene oxide and its application in Cu 2 + removal. J. Colloid Interface Sci. 351(1), 122–127 (2010)
F. Fu, D.D. Dionysiou, H. Liu, The use of zero-valent iron for groundwater remediation and wastewater treatment: a review. J. Hazard. Mater. 267, 194–205 (2014)
J.E. Van Benschoten, B.E. Reed, M.R. Matsumoto, P. McGarvey, Metal removal by soil washing for an iron oxide coated sandy soil. Water Environ. Res. 66(2), 168–174 (1994)
F. Zhang, Q. Jin, S.-W. Chan, Ceria nanoparticles: size, size distribution, and shape. J. Appl. Phys. 95(8), 4319–4326 (2004)
A. Agrawal, K. Sahu, Kinetic and isotherm studies of cadmium adsorption on manganese nodule residue. J. Hazard. Mater. 137(2), 915–924 (2006)
J.A. Coston, C.C. Fuller, J.A. Davis, Pb2+ and Zn2+ adsorption by a natural aluminum-and iron-bearing surface coating on an aquifer sand. Geochim. Cosmochim. Acta 59(17), 3535–3547 (1995)
A. Henglein, Small-particle research: physicochemical properties of extremely small colloidal metal and semiconductor particles. Chem. Rev. 89(8), 1861–1873 (1989)
M.A. El-Sayed, Some interesting properties of metals confined in time and nanometer space of different shapes. Acc. Chem. Res. 34(4), 257–264 (2001)
S.M. Ponder, J.G. Darab, T.E. Mallouk, Remediation of Cr (VI) and Pb (II) aqueous solutions using supported, nanoscale zero-valent iron. Environ. Sci. Technol. 34(12), 2564–2569 (2000)
H.K. Boparai, M. Joseph, D.M. O’Carroll, Kinetics and thermodynamics of cadmium ion removal by adsorption onto nano zerovalent iron particles. J. Hazard. Mater. 186(1), 458–465 (2011)
X. Zhang, S. Lin, Z. Chen, M. Megharaj, R. Naidu, Kaolinite-supported nanoscale zero-valent iron for removal of Pb2+ from aqueous solution: reactivity, characterization and mechanism. Water Res. 45(11), 3481–3488 (2011)
S.A. Kim, S. Kamala-Kannan, K.-J. Lee, Y.-J. Park, P.J. Shea, W.-H. Lee et al., Removal of Pb (II) from aqueous solution by a zeolite–nanoscale zero-valent iron composite. Chem. Eng. J. 217, 54–60 (2013)
Y. Su, A.S. Adeleye, Y. Huang, X. Sun, C. Dai, X. Zhou et al., Simultaneous removal of cadmium and nitrate in aqueous media by nanoscale zerovalent iron (nZVI) and Au doped nZVI particles. Water Res. 63, 102–111 (2014)
P. Xu, G.M. Zeng, D.L. Huang, C.L. Feng, S. Hu, M.H. Zhao et al., Use of iron oxide nanomaterials in wastewater treatment: a review. Sci. Total Environ. 424, 1–10 (2012)
N.N. Nassar, Rapid removal and recovery of Pb (II) from wastewater by magnetic nanoadsorbents. J. Hazard. Mater. 184(1), 538–546 (2010)
Z. Khayat Sarkar, F. Khayat Sarkar, Selective removal of lead (II) ion from wastewater using superparamagnetic monodispersed iron oxide (Fe3O4) nanoparticles as a effective adsorbent. Int. J. Nanosci. Nanotechnol. 9(2), 109–114 (2013)
L. Wang, J. Li, Q. Jiang, L. Zhao, Water-soluble Fe3 O4 nanoparticles with high solubility for removal of heavy-metal ions from waste water. Dalton Trans. 41(15), 4544–4551 (2012)
X. Xin, Q. Wei, J. Yang, L. Yan, R. Feng, G. Chen et al., Highly efficient removal of heavy metal ions by amine-functionalized mesoporous Fe3O4 nanoparticles. Chem. Eng. J. 184, 132–140 (2012)
J.-F. Liu, Zhao Z-s, Jiang G-b, Coating Fe3O4 magnetic nanoparticles with humic acid for high efficient removal of heavy metals in water. Environ. Sci. Technol. 42(18), 6949–6954 (2008)
Y. Bagbi, A. Sarswat, D. Mohan, A. Pandey, P.R. Solanki, Lead (Pb2+) adsorption by monodispersed magnetite nanoparticles: Surface analysis and effects of solution chemistry. J. Environ. Chem. Eng. 4(4), 4237–4247 (2016)
P.R. Grossl, D.L. Sparks, C.C. Ainsworth, Rapid kinetics of Cu (II) adsorption/desorption on goethite. Environ. Sci. Technol. 28(8), 1422–1429 (1994)
Y.-H. Chen, F.-A. Li, Kinetic study on removal of copper (II) using goethite and hematite nano-photocatalysts. J. Colloid Interface Sci. 347(2), 277–281 (2010)
J. Hu, G. Chen, I.M. Lo, Removal and recovery of Cr (VI) from wastewater by maghemite nanoparticles. Water Res. 39(18), 4528–4536 (2005)
J. Hu, G. Chen, I.M. Lo, Selective removal of heavy metals from industrial wastewater using maghemite nanoparticle: performance and mechanisms. J. Environ. Eng. 132(7), 709–715 (2006)
M.-S. Kim, K.-M. Hong, J.G. Chung, Removal of Cu (II) from aqueous solutions by adsorption process with anatase-type titanium dioxide. Water Res. 37(14), 3524–3529 (2003)
M.-S. Kim, J.G. Chung, A study on the adsorption characteristics of orthophosphates on rutile-type titanium dioxide in aqueous solutions. J. Colloid Int. Sci. 233(1), 31–37 (2001)
P. Liang, T. Shi, J. Li, Nanometer-size titanium dioxide separation/preconcentration and FAAS determination of trace Zn and Cd in water sample. Int. J. Environ. Anal. Chem. 84(4), 315–321 (2004)
L. Skubal, N. Meshkov, T. Rajh, M. Thurnauer, Cadmium removal from water using thiolactic acid-modified titanium dioxide nanoparticles. J. Photochem. Photobiol., A 148(1), 393–397 (2002)
S. Carrettin, P. Concepción, A. Corma, J.M. Lopez Nieto, V.F. Puntes, Nanocrystalline CeO2 increases the activity of Au for CO oxidation by two orders of magnitude. Angew. Chem. Int. Ed. 43(19), 2538–2540 (2004)
S. Tsunekawa, T. Fukuda, A. Kasuya, Blue shift in ultraviolet absorption spectra of monodisperse CeO2 − x nanoparticles. J. Appl. Phys. 87(3), 1318–1321 (2000)
Z. Wang, S. Saxena, V. Pischedda, H. Liermann, C. Zha, In situ x-ray diffraction study of the pressure-induced phase transformation in nanocrystalline CeO2. Phys. Rev. B. 64(1), 012102 (2001)
A. Corma, P. Atienzar, H. Garcia, J.-Y. Chane-Ching, Hierarchically mesostructured doped CeO2 with potential for solar-cell use. Nat. Mater. 3(6), 394–397 (2004)
C.-Y. Cao, Z.-M. Cui, C.-Q. Chen, W.-G. Song, W. Cai, Ceria hollow nanospheres produced by a template-free microwave-assisted hydrothermal method for heavy metal ion removal and catalysis. J. Phys. Chem. C. 114(21), 9865–9870 (2010)
S. Recillas, J. Colón, E. Casals, E. González, V. Puntes, A. Sánchez et al., Chromium VI adsorption on cerium oxide nanoparticles and morphology changes during the process. J. Hazard. Mater. 184(1), 425–431 (2010)
Z.-C. Di, J. Ding, X.-J. Peng, Y.-H. Li, Z.-K. Luan, J. Liang, Chromium adsorption by aligned carbon nanotubes supported ceria nanoparticles. Chemosphere 62(5), 861–865 (2006)
M.J. Haron, F. Ab Rahim, A.H. Abdullah, M.Z. Hussein, A. Kassim, Sorption removal of arsenic by cerium-exchanged zeolite P. Mater. Sci. Eng., B 149(2), 204–208 (2008)
C. Gao, W. Zhang, H. Li, L. Lang, Z. Xu, Controllable fabrication of mesoporous MgO with various morphologies and their absorption performance for toxic pollutants in water. Cryst. Growth Des. 8(10), 3785–3790 (2008)
R. Koivula, J. Pakarinen, M. Sivenius, K. Sirola, R. Harjula, E. Paatero, Use of hydrometallurgical wastewater as a precursor for the synthesis of cryptomelane-type manganese dioxide ion exchange material. Sep. Purif. Technol. 70(1), 53–57 (2009)
J. Pakarinen, R. Koivula, M. Laatikainen, K. Laatikainen, E. Paatero, R. Harjula, Nanoporous manganese oxides as environmental protective materials—Effect of Ca and Mg on metals sorption. J. Hazard. Mater. 180(1), 234–240 (2010)
J. Li, Y. Shi, Y. Cai, S. Mou, G. Jiang, Adsorption of di-ethyl-phthalate from aqueous solutions with surfactant-coated nano/microsized alumina. Chem. Eng. J. 140(1), 214–220 (2008)
M. Hiraide, J. Iwasawa, S. Hiramatsu, H. Kawaguchi, Use of surfactant aggregates formed on alumina for the preparation of chelating sorbents. Anal. Sci. 11(4), 611–615 (1995)
G. Chang, Z. Jiang, T. Peng, B. Hu, Preparation of high-specific-surface-area nanometer-sized alumina by sol-gel method and study on adsorption behaviors of transition metal ions on the alumina powder with ICP-AES. Acta Chim. Sin. Chin. Ed. 61(1), 100–103 (2003)
S. Dadfarnia, A.H. Shabani, H.D. Shirie, Determination of lead in different samples by atomic absorption spectrometry after preconcentration with dithizone immobilized on surfactant-coated alumina. Bull. Korean Chem. Soc. 23(4), 545–548 (2002)
M. Fan, T. Boonfueng, Y. Xu, L. Axe, T.A. Tyson, Modeling Pb sorption to microporous amorphous oxides as discrete particles and coatings. J. Colloid Interface Sci. 281(1), 39–48 (2005)
X. Pu, Z. Jiang, B. Hu, H. Wang, γ-MPTMS modified nanometer-sized alumina micro-column separation and preconcentration of trace amounts of Hg, Cu, Au and Pd in biological, environmental and geological samples and their determination by inductively coupled plasma mass spectrometry. J. Anal. At. Spectrom. 19(8), 984–989 (2004)
A. Afkhami, M. Saber-Tehrani, H. Bagheri, Simultaneous removal of heavy-metal ions in wastewater samples using nano-alumina modified with 2, 4-dinitrophenylhydrazine. J. Hazard. Mater. 181(1), 836–844 (2010)
M.-R. Huang, S.-J. Huang, X.-G. Li, Facile synthesis of polysulfoaminoanthraquinone nanosorbents for rapid removal and ultrasensitive fluorescent detection of heavy metal ions. J. Phys. Chem. C. 115(13), 5301–5315 (2011)
X. Zhao, L. Lv, B. Pan, W. Zhang, S. Zhang, Q. Zhang, Polymer-supported nanocomposites for environmental application: a review. Chem. Eng. J. 170(2), 381–394 (2011)
D. Chen, T. Awut, B. Liu, Y. Ma, T. Wang, I. Nurulla, Functionalized magnetic Fe3O4 nanoparticles for removal of heavy metal ions from aqueous solutions. e-Polymers (2016)
S.-H. Huang, D.-H. Chen, Rapid removal of heavy metal cations and anions from aqueous solutions by an amino-functionalized magnetic nano-adsorbent. J. Hazard. Mater. 163(1), 174–179 (2009)
G.-B. Cai, G.-X. Zhao, X.-K. Wang, S.-H. Yu, Synthesis of polyacrylic acid stabilized amorphous calcium carbonate nanoparticles and their application for removal of toxic heavy metal ions in water. J. Phys. Chem. C. 114(30), 12948–12954 (2010)
S. Pavlidou, C.D. Papaspyrides, A review on polymer–layered silicate nanocomposites. Prog. Polym. Sci. 33(12), 1119–1198 (2008). doi:http://dx.doi.org/10.1016/j.progpolymsci.2008.07.008
J. Liu, Y. Ma, T. Xu, G. Shao, Preparation of zwitterionic hybrid polymer and its application for the removal of heavy metal ions from water. J. Hazard. Mater. 178(1–3), 1021–1029 (2010). doi:http://dx.doi.org/10.1016/j.jhazmat.2010.02.041
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 Springer Nature Singapore Pte Ltd.
About this chapter
Cite this chapter
Bagbi, Y., Pandey, A., Solanki, P.R. (2018). Role of Nanostructured Materials Toward Remediation of Heavy Metals/Metalloids. In: Khan, Z. (eds) Nanomaterials and Their Applications. Advanced Structured Materials, vol 84. Springer, Singapore. https://doi.org/10.1007/978-981-10-6214-8_3
Download citation
DOI: https://doi.org/10.1007/978-981-10-6214-8_3
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-10-6213-1
Online ISBN: 978-981-10-6214-8
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)