Abstract
Experiments are reported in which indigenous sulfur, present at low levels within a substrate alloy, is sufficient to produce oxide scale exfoliation effects. The amount of sulfur commonly found at levels less than approximately 50 ppm by weight in normally prepared alloys is sufficient to produce exfoliation. The reduction of such sulfur either through the use of high purity, i.e. low sulfur starting materials or the use of active element additions, is sufficient to produce adherent scales. By reacting with indigenous sulfur to form refractory sulfides, active element, e.g. yttrium, additions effectively reduce the amount of sulfur available to segregate to and weaken the crucial scale-metal interfacial bond.
Pores are frequently observed on substrate surfaces when oxide scales exfoliate. These pores have commonly been attributed to Kirkendall effects. By reacting with and annihilating vacancies resulting from Kirkendall effects at the scale-metal interface, active element oxides at the scale-metal interface have been suggested to promote scale adherence. Studies conducted here have shown that without active element additions small pores few in number are associated with exfoliation effects. Despite adherent scales, similar pores occur at the scale-metal interface. Hence the relationship between porosity at the scale-metal interface and protective scale adherence is unclear.
In a series of experiments involving implanted species that would be little soluble at elevated temperatures, exfoliating scales were produced despite the presence of yttrium in a Ni – 20 wt% Cr – 12 wt% Al alloy. Pores in exfoliated regions of such implanted specimens had all the characteristics normally associated with scale exfoliation effects in unimplanted materials. Hence it is suggested that the porosity commonly observed at surfaces of conventionally produced alloy substrates is rather due to the expulsion of contaminant levels, i.e. low ppm levels, of little soluble elements, e.g. argon, present at low levels.
Experimental results which have led to these conclusions are presented.
Access this chapter
Tax calculation will be finalised at checkout
Purchases are for personal use only
Preview
Unable to display preview. Download preview PDF.
Similar content being viewed by others
References
D.P. Whittle and J. Stringer: Philos. Trans. R. Soc. London, 1980, Ser., A295, 309–32.
J.G. Smeggil: “The Effect of Indigenous Sulfur on the Adherence of Chromia Scales” presented at the spring 1988 ASM-AIME meeting, Las Vegas, Nevada, submitted for publication in conference proceedings.
J.G. Smeggil: Mater Sci. and Eng., 1987, 87, 261–266.
J.G. Smeggil, N.S. Bornstein and M.A. DeCrescente: Oxid. of Metals, 1988, 30, 259–266.
J.G. Smeggil and G.G. Peterson: Oxid. of Metals, 1988, 29, 103–119.
J.G. Smeggil, E.L. Paradis, A.J. Shuskus and N.S. Bornstein: J. Vac. Sci. Technol., A., 1985, 3, 2269–73.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 1989 ECSC, EEC, EAEC. Brussels and Luxembourg
About this chapter
Cite this chapter
Smeggil, J.G., Shuskus, A.J., Bornstein, N.S., DeCrescente, M.A. (1989). The Role of Sulfur in the Growth and Adhesion of Oxide Scales. In: Lang, E. (eds) The Role of Active Elements in the Oxidation Behaviour of High Temperature Metals and Alloys. Springer, Dordrecht. https://doi.org/10.1007/978-94-009-1147-5_17
Download citation
DOI: https://doi.org/10.1007/978-94-009-1147-5_17
Publisher Name: Springer, Dordrecht
Print ISBN: 978-94-010-7009-6
Online ISBN: 978-94-009-1147-5
eBook Packages: Springer Book Archive