Effect of minor Gd addition on the microstructure, mechanical properties and wear behavior of as-cast Mg–5Sn-based alloy was investigated by means of OM, XRD, SEM, EDS, a super depth-of-field 3D system, standard high-temperature tensile testing and dry sliding wear testing. Minor Gd addition has strong effect on changing the morphology of the Mg–5Sn binary alloy. Gd addition benefits the grain refinement of the primary α-Mg phase, as well as the formation and homogeneous distribution of the secondary Mg2Sn phase. The mechanical properties of the Mg–5Sn alloys at ambient and elevated temperatures are significantly enhanced by Gd addition. The wear behavior of the Mg–5Sn alloy is also improved with minor Gd addition. The alloy with 0.8% Gd addition exhibits the best ultimate tensile strength and elongation as well as the optimal wear behavior. Additionally, the worn surface of the Mg–5Sn–Gd becomes smoother in higher Gd-containing alloys. The best wear behavior of alloy was exhibited when Gd addition was up to 0.8%, showing a much smoother worn surface than that of control sample. The improvement of tensile properties is mainly attributed to the refinement of microstructure and the increasing amount and uniform distribution of Mg2Sn phase. The larger amount of Mg2Sn phase uniformly distributed at the grain boundary of Mg–Sn–Gd alloys act as a lubrication during sliding, and combined with smaller grain size improve wear behavior of the binary alloy.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Razavi, S.M., Foley, D.C., Karaman, I., Hartwig, K.T., Duygulu, O., Kecskes, L.J., Mathaudhu, S.N., and Hammond, V.H., Effect of grain size on prismatic slip in Mg–3Al–1Zn alloy, Scr. Mater., 2012, vol. 67, no. 5, p. 439.
Kashefi, N. and Mahmudi, R., The microstructure and impression creep behavior of cast AZ80 magnesium alloy with yttrium additions, Mater. Des., 2012, no. 39, p. 200.
Chen, Y.A., Li, J., Yu, S., Liu, H., and Ye, R.Y., Effect of Zn on microstructure and mechanical property of Mg–3Sn–1Al alloys, Mater. Sci. Eng. A, 2014, no. 612, p. 96.
Shi, Z.Z., The crystallography of lath-shaped Mg2Sn precipitates in a Mg–Sn–Zn–Mn alloy, J. Alloys Compd., 2013, no. 559, p. 158.
Terbush, J.R., Stanford, N., Nie, J.F., and Barnett, M.R., Na partitioning during thermomechanical processing of an Mg–Sn–Zn–Na alloy, Metall. Mater. Trans. A, 2013, vol. 44, no. 11, p. 5216.
Huang, X.F. and Zhang, W.Z., Characterization and interpretation of interfacial structure of the Mg2Sn laths in an Mg–Sn–Mn–Ag–Zn alloy, Philos. Mag. Lett., 2014, vol. 94, no. 4, p. 251.
Gibson, M.A., Fang, X., Bettles, C.J., and Hutchinson, C.R., The effect of precipitate state on the creep resistance of Mg–Sn alloys, Scr. Mater., 2010, vol. 63, no. 8, p. 899.
Poddar, P., Das, A., and Sahoo, K.L., Dry sliding wear characteristics of gravity die-cast magnesium alloys, Metall. Mater. Trans. A, 2014, vol. 45, no. 4, p. 2270.
Kang, D.H., Park, S.S., and Kim, N.J., Development of creep resistant die cast Mg–Sn–Al–Si alloy, Mater. Sci. Eng. A, 2005, vol. 413–414, p. 555.
Liu, H., Chen, Y., Tang, Y., Wei, S., and Niu, G., The microstructure, tensile properties and creep behavior of as-cast Mg–(1–10)%Sn alloys, J. Alloys Compd., 2007, vol. 440, no. 1–2, p. 122.
Park, S.S., Kim, Y.J., Cheng, W.L., Kim, Y.M., and You, B.S., Tensile properties of extruded Mg–8Sn–1Zn alloys subjected to different heat treatments, Phil. Mag. Lett., 2011, vol. 91, no. 1, p. 37.
Ha, H.Y., Kang, J.Y., Kim, S.G., Kim, B., Park, S.S., Yim, C.D., and You, B.S., Influences of metallurgical factors on the corrosion behaviour of extruded binary Mg–Sn alloys, Corr. Sci., 2014, vol. 82, no. 2, p. 369.
Wang, Q., Chen, Y.G., Xiao, S.F., Zhang, X.P., Tang, Y.B., Wei, S.H., and Zhao, Y.H., Study on microstructure and mechanical properties of as-cast Mg–Sn–Nd alloys, J. Rare Earths, 2010, vol. 28, no. 5, p. 790.
Nayyeri, G. and Mahmudi, R., Effects of Ca additions on the microstructural stability and mechanical properties of Mg–5% Sn alloy, Mater. Des., 2011, vol. 32, no. 3, p. 1571.
Liu, H.M., Chen, Y.G., Zhao, H.F., Wei, S.H., and Gao, W., Effects of strontium on microstructure and mechanical properties of as-cast Mg–5wt % Sn alloy, J. Alloys Compd., 2010, vol. 504, no. 2, p. 345.
Elsayed, F.R., Sasaki, T.T., Mendis, C.L., Ohkubo, T., and Hono, K., Compositional optimization of Mg–Sn–Al alloys for higher age hardening response, Mater. Sci. Eng. A, 2013, no. 566, p. 22.
Zhang, M.X., Kelly, P.M., Qian, M., and Taylor, J.A., Crystallography of grain refinement in Mg–Al based alloys, Acta Mater., 2005, vol. 53, no. 11, p. 3261.
Yamasaki, M., Anan, T., Yoshimoto, S., and Kawamura, Y., Mechanical properties of warmextruded Mg–Zn–Gd alloy with coherent 14H long periodic stacking ordered structure precipitate, Scr. Mater., 2005, vol. 53, no. 7, p. 799.
Wang, L.D., Xing, C.Y., Hou, X.L., Wu, Y.M., Sun, J.F., and Wang, L.M., Microstructures and mechanical properties of as-cast Mg–5Y–3Nd–Zr–xGd (x = 0, 2 and 4 wt %) alloys, Mater. Sci. Eng. A, 2010, vol. 527, nos. 7–8, p. 1891.
Wang, X.D., Du, W.B., Liu, K., Wang, Z.H., and Li, S.B., Microstructure, tensile properties and creep behaviors of as-cast Mg–2Al–1Zn–xGd (x = 1, 2, 3, and 4 wt %) alloys, J. Alloys Compd., 2012, no. 522, p. 78.
Yu, H.Y., Yan, H.G., Chen, J.H., Su, B., Zheng, Y., Shen, Y.J., and Ma, Z.J., Effects of minor Gd addition on microstructures and mechanical properties of the high strain-rate rolled Mg–Zn–Zr alloys, J. Alloys Compd., 2014, no. 586, p. 757.
Yang, J., Xiao, W.L., Wang, L.D., Wu, Y.M., Wang, L.M., and Zhang, H.J., Influences of Gd on the microstructure and strength of Mg–4.5Zn alloy, Mater. Charact., 2008, vol. 59, no. 11, p. 1667.
National Standard of the People’s Republic of China-GB/T 228.1–2010: Metallic Materials-Tensile Testing, Part 1: Method of Test at Room Temperature, Beijing: China Standard Press, 2011 [in Chinese].
Petrzhik, M.I. and Levashov, E.A., Modern methods for investigating functional surfaces of advanced materials by mechanical contact testing, Crystallogr. Rep., 2007, vol. 52, no. 6, p. 966.
Yang, M.B., Guo, T.Z., and Li, H.L., Effects of Gd addition on as-cast microstructure, tensile and creep properties of Mg–3.8Zn–2.2Ca (wt %) magnesium alloy, Mater. Sci. Eng. A, 2013, no. 587, p. 132.
Ye, L.Y., Hu, J., Tang, C.P., Zhang, X.M., Deng, Y.L., Liu, Z.Y., and Zhou, Z.L., Modification of Mg2Si in Mg–Si alloys with gadolinium, Mater. Charact., 2013, no. 79, p. 1.
Ares, A.E., Gassa, L.M., Schvezov, C.E., and Rosenberger, M.R., Corrosion and wear resistance of hypoeutectic Zn–Al alloys as a function of structural features, Mater. Chem. Phys., 2012, vol. 136, nos. 2–3, p. 394.
Rosenberger, M.R., Ares, A.E., Gatti, I.P., and Schvezov, C.E., Wear resistance of dilute Zn–Al alloys, Wear, 2010, vol. 268, no. 11, p. 1533.
Jiang, J., Bi, G.L., Zhao, L., Li, R.G., Lian, J.S., and Jiang, Z.H., Dry sliding wear behavior of extruded Mg–Sn–Yb alloy, J. Rare Earth, 2015, no. 33, p. 77.
Jahanmir, S. and Suh, N.P., Mechanics of subsurface void nucleation in delamination wear, Wear, 1977, vol. 44, no. 1, p. 17.
Anbu Selvan, S. and Ramanathan, S., Dry sliding wear behavior of as-cast ZE41A magnesium alloy, Mater. Des., 2010, vol. 31, no. 4, p. 1930.
Poddar, P., Das, A., and Sahoo, K.L., Dry sliding wear characteristics of rheocast Mg–Sn based alloys, Mater. Des., 2014, no. 54, p. 820.
Xu, Y., Miao, Q., Liang, W.P., Yu, X.S., Jiang, Q., Zhang, Z.G., Ren, B.L., and Yao, Z.J., Tribological behavior of Al2O3/Al composite coating on γ-TiAl at elevated temperature, Mater. Charact., 2015, no. 101, p. 122.
Walker, J.C., Ross, I.M., Reinhard, C., Rainforth, W.M., and Hovsepian, P.E., High temperature tribological performance of CrAlYN/CrN nanoscale multilayer coatings deposited on gamma-TiAl, Wear, 2009, vol. 267, nos. 5–8, p. 965.
Yang, Z.R., Wang, S.Q., Zhao, Y.T., and Wei, M.X., Evaluation of wear characteristics of Al3Tip/Mg composite, Mater. Charact., 2010, vol. 61, no. 5, p. 554.
Chase, M.W., NIST-JANAF thermochemical tables, J. Phys. Chem. Ref. Data, MoNo.gr, 1998, no. 9, p. 1.
Waterhouse, R.B., Fretting wear, Wear, 1984, vol. 100, nos. 1–3, p. 107.
Manoj Kumar, B.V., Basu, B., Murthy, V.S.R., and Gupta, M., The role of tribochemistry on fretting wear of Mg–SiC particulate composites, Compos., Part A, 2005, vol. 36, no. 1, p. 13.
Wilson, S. and Alpas, A.T., Thermal effects on mild wear transitions in dry sliding of an aluminum alloy, Wear, 1999, nos. 225–229, p. 440.
Author information
Authors and Affiliations
Corresponding authors
Additional information
The article is published in the original.
About this article
Cite this article
Cong, M., Li, Z., Liu, J. et al. Effect of Gd on microstructure, mechanical properties and wear behavior of as-cast Mg–5Sn alloy. Russ. J. Non-ferrous Metals 57, 445–455 (2016). https://doi.org/10.3103/S1067821216050114
Received:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1067821216050114