Abstract
To obtain high-performance Al-Si-based cast alloys, refinement and modification of Si phases are required. An Al-12Si/ZnS powder inoculant was designed and fabricated using a chemical bath deposition method. The efficiency of the inoculant for modifying the eutectic Si phase in as-cast Al-12Si alloy was studied. Results show that Al-12Si/ZnS powder can significantly refine the eutectic Si in Al-Si cast alloys. The best refinement effect for eutectic Si is achieved with 17.5wt.% Al-12Si/ZnS powder. Coarse long needle-shaped eutectic Si with a length of 18 µm was modified into approximately spherical shape with a diameter of 6.53 µm, which is evenly distributed throughout the alloy. The E2EM model calculation indicates that the inter-plane misfit (Fp) and inter-atomic spacing misfit (Fr) between ZnS and Si are all less than 0.5%, which confirms that ZnS is a potential nucleation site for Si phase. The hardness, tensile strength, and elongation of Al-12Si alloys modified with 17.5% Al-12Si/ZnS powder increase 6.30%, 16.18% and 55.45%, respectively, compared to the unmodified Al-12Si alloy. The fracture behavior of the alloy with 17.5wt.% Al-12Si/ZnS powder is dominated by transgranular fracture supplemented by intergranular fracture.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Zhang H T, Zuo K S, Han X, et al. Effects of P+Cr complex modification and solidification conditions on microstructure of hypereutectic Al-Si alloys by wedge-shaped copper mould casting. China Foundry, 2014, 11(6): 481–486.
Fan Z, Song W, Zhang H R, et al. Effect of holding pressure on density and cooling rate of cast Al-Si alloy during additive pressure casting. China Foundry, 2019, 16(6): 363–370.
Dang B, Jian Z Y, Xu J F, et al. Effect of phosphorus and heat treatment on microstructure of Al-25%Si alloy. China Foundry, 2017, 14(1): 10–15.
Matsuura K, Kudoh M, Kinoshita H, et al. Precipitation of Si particles in a super-rapidly solidified Al-Si hypereutectic alloy. Mater. Chem. Phys., 2003, 81(2): 393–395.
Ha T K, Park W J, Ahn S, et al. Fabrication of spray-formed hypereutectic Al-25Si alloy and its deformation behavior. Journal of Materials Processing Technology, 2002, 130–131: 691–695.
Jian X G, Han Q Y. Formation of hypereutectic silicon particles in hypoeutectic Al-Si alloys under the influence of high-intensity ultrasonic vibration. China Foundry, 2013, 10(2): 118–123.
Liao H C, Sun G X. Development on mechanisms of the eutectic Si modification. Foundry, 2003, 52(12): 1127–1129. (In Chinese)
Vijayan V, Prabhu P. Review of microstructure evolution in hypereutectic Al-Si alloys and its effect on wear properties. Transactions of the Indian Institute of Metals, 2014, 67(1): 1–18.
Lu S Z, Hellawell A. Modification of Al-Si alloys: Microstructure, thermal analysis, and mechanisms. JOM, 1995, 47(2): 38–40.
Roehling J D, Coughlin D R, Gibbs J W, et al. Rapid solidification growth mode transitions in Al-Si alloys by dynamic transmission electron microscopy. Acta Materialia, 2017, 131: 22–30.
Liu W Y, Xiao W L, Xu C, et al. Synergistic effects of Gd and Zr on grain refinement and eutectic Si modification of Al-Si cast alloy. Materials Science and Engineering: A, 2017, 693(5): 93–100.
Zhang Y B, Kateryna S, Li T J. Effect of ultrasonic treatment on formation of iron-containing intermetallic compounds in Al-Si alloys. China Foundry, 2016, 13(5): 316–321.
Knuutinen A, Nogita K, McDonald S D, et al. Modification of Al-Si alloys with Ba, Ca, Y and Yb. Journal of Light Metals, 2001, 1(4): 229–240.
Subroto T, Miroux A, Bouffier L, et al. Formation of hot tear under controlled solidification conditions. Metallurgical & Materials Transactions A, 2014, 45(6): 2855–2862.
Nogita K, Yasuda H, Yoshiya M, et al. The role of trace element segregation in the eutectic modification of hypoeutectic Al-Si alloys. Journal of Alloys & Compounds, 2010, 489(2): 415–420.
Tsai Y C, Lee S L, Lin C K. Effect of trace Ce addition on the microstructures and mechanical properties of A356 (Al-7Si-0.35 Mg) aluminum alloys. Journal of the Chinese Institute of Engineers, 2011, 34(5): 609–616.
Choi H, Konishi H, Li X C. Al2O3 nanoparticles induced simultaneous refinement and modification of primary and eutectic Si particles in hypereutectic Al-20Si alloy. Materials Science and Engineering: A, 2012, 541(1): 159–165.
Zhang H H, Duan H L, Shao G J, et al. Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P. Rare Metals, 2008, 27(1): 59–63.
Wang W, Guo F X, Gai Z G, et al. The formation of nanoparticles and their competitive interaction with twins during eutectic Si growth. Materials, 2018, 11(8): 1040.
Lu L M, Nogita K, Dahle A K. Combining Sr and Na additions in hypoeutectic Al-Si foundry alloys. Materials Science and Engineering: A, 2005, 399(1/2): 244–253.
Cardinale A M, Maccio D, Luciano G, et al. Thermal and corrosion behavior of as cast Al-Si alloys with rare earth elements. Journal of Alloys & Compounds, 2017, 695: 2180–2189.
Ahmad R, Asmael M B A. Influence of lanthanum on solidification, microstructure, and mechanical properties of eutectic Al-Si piston alloy. Journal of Materials Engineering and Performance, 2016, 25(7): 2799–2813.
Ren B, Liu Z X, Zhao R F, et al. Effect of Sb on microstructure and mechanical properties of Mg2Si/Al-Si composites. Transactions of Nonferrous Metals Society of China, 2010, 20(8): 1367–1373.
Nogita K, Mcdonald S D. Eutectic modification of Al-Si alloys with rare earth metals. Materials Transactions, 2004, 45(2): 323–326.
Liu L, Samuel A M, Samuel F H, et al. Characteristics of α-dendritic and eutectic structures in Sr-treated Al-Si casting alloys. Journal of Materials Science, 2004, 39(1): 215–224.
Kawther A H, Ian S, Fan Z Y. Refinement of primary silicon crystals by novel Al-ZnS master alloy in solidification of hypereutectic Al-Si alloys. In: Edward Williams (Eds), Light Metal 2016. Switzerland: Springer International Publisher, 2016: 271–273.
Li C D, Si W Q, Zhao M, et al. A new Al-ZnS master alloy designed for modifying hypereutectic Al-Si alloy and its refinement performance on primary Si. Advanced Materials Research, 2015, 1088: 242–244.
Li C D, Sun C H, Si W Q, et al. Effects of ZnS modification on primary Si in hypereutectic Al-Si alloy. China Foundry, 2017, 14(2): 93–97.
Zhang J H, Xing S M. Modifying elements and their interaction in Al-Si alloy. Materials Review, 2018, 32(6): 1870–1877.
Quested T E, Greer A L. The effect of the size distribution of inoculant particles on as-cast grain size in aluminium alloys. Acta Materialia, 2004, 52(13): 3859–3868.
Zhang Y, Dang X Y, Jin J, et al. ZnS thin film deposited with chemical bath deposition process directed by different stirring speeds. Applied Surface Science, 2010, 256(22): 6871–6875.
Goudarzi A, Aval G M, Sahraei R, et al. Ammonia-free chemical bath deposition of nanocrystalline ZnS thin film buffer layer for solar cells. Thin Solid Films, 2008, 516(15): 4953–4957.
Liao H, Chang Y, Chen Y F, et al. Fabrication of ZnSe quantum dots under Volmer-Weber mode by metalorganic chemical vapor deposition. Applied Physics Letters, 1997, 70(17): 2256–2258.
Poulomi R, Jyoti R O, Suneel K S. Crystalline ZnS thin films by chemical bath deposition method and its characterization. Journal of Functional Materials, 2006, 515: 1512–1515.
Brune H. Encyclopedia of materials: Science and technology. Elsevier Science Ltd., 2001.
Acknowledgements
The authors gratefully acknowledge the financial support from the National Natural Science Foundation of China (Grant No. 51672145).
Author information
Authors and Affiliations
Corresponding author
Additional information
Cheng-dong Li Male, born in 1973, Ph.D. Research interests: melting, casting and powder metallurgy preparation, grain refinement and particle reinforcement of high performance aluminum alloys.
Rights and permissions
About this article
Cite this article
Wang, Y., Chen, Py., Lin, Yh. et al. An Al-12Si/ZnS powder inoculant for eutectic silicon in Al-12Si alloy. China Foundry 19, 149–157 (2022). https://doi.org/10.1007/s41230-022-9003-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-022-9003-2