Abstract
The distribution of SiC particles in Al-SiC composite can greatly influence the mechanical performances of Al-SiC composite. To realize the homogeneous distribution of SiC particles in stir-casting Al-SiC composite, semisolid stir casting of Al-4.25vol.%SiC composite was conducted using a special electromagnetic-mechanical stirring equipment made by our team, in which there are three uniformly-distributed blades with a horizontal tilt angle of 25 ° to mechanically raise the SiC particles by creating an upward movement of slurry under electromagnetic stirring. The microstructure of the as-cast Al-SiC composites was observed by Scanning Electron Mcroscopy (SEM). The volume fraction of SiC particles was measured by image analysis using the Quantimet 520 Image Processing and Analysis System. The tensile strength of the Al-4.25vol.%SiC composites was measured by tensile testing. Results show that the Al-4.25vol.%SiC composites with the homogeneous distrbutin of SiC particles can be obtained by the electromagnetic-mechanical stirring casting with the speed of 300 and 600 r·min−1 at 620 °C. The differences between the volume fraction of SiC particles at the top of ingot and that at the bottom are both ~0.04vol.% with the stirring speed of 300 and 600 r·min−1, which are so small that the distribution of SiC particles can be seen as the homogeneous. The tensile strength of the Al matrix is enhanced by 51.2% due to the uniformly distributed SiC particles. The porosity of the composite mainly results from the solidification shrinkage of slurry and it is less than 0.04vol.%.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Xie B, Wang X G, Hua X H, et al. Process and Performance of β-SiCp/Al Prepared by Bottom-vacuum Pressureless Infiltration. Rare Metal Mat. Eng., 2014, 43(9): 2089–2094.
Mosleh-Shirazi S, Akhlaghi F, Li D Y. Effect of SiC Content on Dry Sliding Wear, Corrosion and Corrosive Wear of Al/SiC Nanocomposites. Trans. Nonferrous Met. Soc. China, 2016, 26(7): 1801–1808.
Khodabakhshi F, Gerlich A P, Švec P. Fabrication of a High Strength Ultra-fine Grained Al-Mg-SiC Nanocomposite by Multi-step Friction-stir Processing. Mater. Sci. Eng. A, 2017, 698: 313–325.
Teng F, Yu K, Luo J, et al. Microstructures and Properties of Al−50%SiC Composites for Electronic Packaging Applications. Trans. Nonferrous Met. Soc. China, 2016, 26(10): 2647–2652.
Si Y Q, You Z Y, Zhu J X, et al. Microstructure and Properties of Mechanical Alloying Particles Reinforced Aluminum Matrix Composites Prepared by Semisolid Stirring Pouring Method. China Foundry, 2016, 13(3): 176–181.
Fathy A, Sadoun A, Abdelhameed M. Effect of Matrix/ reinforcement Particle Size Ratio (PSR) on the Mechanical Properties of Extruded Al−SiC Composites. Int. J. Adv. Manuf. Tech., 2014, 73(5-8): 1049–1056.
Vijayavel P, Balasubramanian V. Effect of Pin Profile Volume Ratio on Microstructure and Tensile Properties of Friction Stir Processed Aluminum Based Metal Matrix Composites. J. Alloy. Comp., 2017, 729: 828–842.
Wu S S, Yuan D, Lü S L, et al. Nano-SiCP Particles Distribution and Mechanical Properties of Al-matrix Composites Prepared by Stir Casting and Ultrasonic Treatment. China Foundry, 2018, 15(3): 203–209.
Previtali B, Pocci D, Taccardo C. Application of Traditional Investment Casting Process to Aluminium Matrix Composites. Compos. Part A, 2008, 39(10): 1606–1617.
Naher S, Brabazon D, Looney L. Development and Assessment of a New Quick Quench Stir Caster Design for the Production of Metal Matrix Composites. J. Mater. Process. Tech., 2004, 166(3): 430–439.
Amirkhanlou S, Niroumand B. Synthesis and Characterization of 356-SiCp Composites by Stir Casting and Compocasting Methods. Trans. Nonferrous Met. Soc. China, 2010, 20(s3): s788–s793.
Ureña A, Martínez E E, Rodrigo P, et al. Oxidation Treatments for SiC Particles Used as Reinforcement in Aluminium Matrix Composites. Compos. Sci. Technol., 2004, 64(12): 1843–1854.
Singh S, Pal K. Influence of Surface Morphology and UFG on Damping and Mechanical Properties of Composite Reinforced with Spinel MgAl2O4-SiC Core-shell Microcomposites. Mater. Charact., 2017, 123: 244–255.
León C A, Drew R A L. The Influence of Nickel Coating on the Wettability of Aluminum on Ceramics. Compos. Part A, 2002, 33(10): 1429–1432.
Vanarotti M, Shrishail P, Sridhar B R, et al. Study of Mechanical Properties & Residual Stresses on Post Wear Samples of A356-SiC Metal Matrix Composites. Procedia Materials Science, 2014, 5(3873): 873–882.
Hashim J, Looney L, Hashmi M S J. The Enhancement of Wettability of SiC Particles in Cast Aluminium Matrix Composites. J. Mater. Process. Technol., 2001, 119(1-3): 329–335.
Heidary D S B, Akhlaghi F. Theoretical and Experimental Study on Settling of SiC Particles in Composite Slurries of Aluminum A356/SiC. Acta Mater., 2011, 59(11): 4556–4568.
Arab M S, Mahallawy N E, Shehata F, et al. Refining SiCp in Reinforced Al-SiC Composites Using Equal-channel Angular Pressing. Mater. Design, 2014, 64: 280–286.
Lokesh T, Mallikarjun U S. Mechanical and Morphological Studies of Al6061-Gr-SiC Hybrid Metal Matrix Composites. Applied Mechanics and Materials, 2015, 813-814: 195–202.
Mazahery A, Shabani M O. Microstructural and Abrasive Wear Properties of SiC Reinforced Aluminum-based Composite Produced by Compocasting. Trans. Nonferrous Met. Soc. China, 2013, 23(7): 1905–1914.
Li C S, Ellyin F, Koh S, et al. Influence of Porosity on Fatigue Resistance of Cast SiC Particulate-reinforced Al-Si Alloy Composite. Mater. Sci. Eng. A, 2000, 276(1-2): 218–225.
Ilegbusi O J, Yang J J. Porosity Nucleation in Metal-matrix Composites. Metall. Mater. Trans. A, 2000, 31(8): 2069–2074.
Podymova N B, Karabutov A A. Combined Effects of Reinforcement Fraction and Porosity on Ultrasonic Velocity in SiC Particulate Aluminum Alloy Matrix Composites. Compos. Part B, 2017, 113: 138–143.
Song M. Effects of Volume Fraction of SiC Particles on Mechanical Properties of SiC/Al composites. Trans. Nonferrous Met. Soc. China, 2009, 19(6): 1400–1404.
Author information
Authors and Affiliations
Corresponding author
Additional information
Yun-hui Du Female, born in 1969, professor. She has been working in the field of composites. Her research focuses on new materials and new technologies. Her academic research has lead to the publication of more than 80 papers.
Rights and permissions
About this article
Cite this article
Du, Yh., Zhang, P., Zhang, Wy. et al. Distribution of SiC particles in semisolid electromagnetic-mechanical stir-casting Al-SiC composite. China Foundry 15, 351–357 (2018). https://doi.org/10.1007/s41230-018-8086-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-018-8086-2