The simulation models of the thermal and macrostructural evolutions during directional solidification of Ni-base single crystal (SX) turbine blades under high rate solidification (HRS) and liquid metal cooling (LMC) have been constructed using ProCAST software, coupled with a 3D Cellular Automaton Finite Element (CAFE) model. The models were used to investigate the tendencies of stray grain (SG) formation in the platform region of turbine blades fabricated by HRS and LMC techniques. The results reveal that the LMC technique can prohibit SG formation by smoothing the concaved isotherm and in turn alleviating the undercooling in the platform ends to let the dendrites fill up the undercooled zone before SG nucleation. The simulation results agreed well with the experimental results, indicating that these models could be used to analyze the macrostructural evolution or to optimize process parameters to suppress SG formation. Using these models, the critical withdrawal rate for casting SX turbine blades without SG formation were determined to be around 75 μm·s-1 and 100 μm·s-1 for HRS and LMC respectively, suggesting that LMC can be used as an efficient technique in fabricating SX turbine blades without any SG defect formation.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Reed R C. The Superalloys Fundamental and Applications. Cambridge University Press, Cambridge, UK, 2006: 1–5.
Vehn M M, Dedecke D, Paul U et al. Undercooling related casting defects in single crystal turbine blades. Superalloys1996, TMS, 1996: 471–479.
Li Yafeng, Liu Lin, Huang Taiwen, et al. Multi-scale characterization of stray grain in the platform of nickel-base single crystal turbine blade. Vacuum, 2016, 131: 181–187
Bussac A D and Gandin C A. Prediction of a process window for the investment casting of dendritic single crystals. Materials Science and Engineering A, 1997, 237: 35–42.
Yang X L, Dong H B, Wang W, et al. Microscale simulation of stray grain formation in investment cast turbine blades. Materials Science and Engineering A, 2004, 386: 129–139.
Meng X B, Li J G, Chen Z Q, et al. Effect of platform dimension on the dendrite growth and stray grain formation in a Ni-base single crystal superalloy. Metallurgical and Materials Transaction, 2013, 44A: 1955–1965
Gao Sifeng, Liu Lin, Zhang Jun, et al. Simulation of stray grain formation at the platform during Ni-base single crystal superalloy DD403 casting. China Foundry, 2015, 12: 118–122.
Ma DX, Wu Q, Polaczek AB. Undercoolability of superalloys and solidification defects in single crystal components. Advanced Materials Research, 2011, 278: 114–119.
Zhang Xiaoli, Zhou Yizhou, Jin Tao, et al. Study of the tendency of stray grain formation of Ni-based single crystal superalloys. Acta Metallurgica Sinica, 2012, 48: 1229–1236. (In Chinese)
Lu Yuzhang, Wang Dawei, Zhang Jian, et al. Numerical simulation and experimental observation of single crystal castings processed by liquid metal cooling technique. Foundry, 2009, 58(3): 245–248. (In Chinese)
Cao Liu, Liao Dunming, Lu Yuzhang, et al. Heat transfer model of directional solidification by LMC process for superalloy casting based on finite element method. Metallurgical and Materials Transactions, 2016, 47A: 4640–4647.
Tang Ning, Zhang Hang, Xu Qingyan, et al. Numerical simulation of temperature field and microstructure during directional solidification hollow blades by LMC. Special Casting & Nonferrous Alloys, 2014, 34(6): 561–565. (In Chinese)
Guo Rufeng, Liu Lin, Li Yafeng, et al. Numerical simulation of temperature field and grain texture during casting single crystal superalloy DD403 with liquid metal cooling. Foundry, 2014, 63(2): 145–151. (In Chinese)
Kurz W, Giovanola B and Trivedi R. Theory of Microstructural development during rapid solidification. Acta Materialia, 1986, 34(5), 823–830.
Rappaz M, David S A, Vitek J M, et al. Analysis of solidification microstructures in Fe-Ni-Cr single-crystal welds. Metallurgical and Materials Transactions, 1990, 21A: 1767–1782.
Kermanpur A, Varahram N, Davami P, et al. Thermal and grainstructure simulation in a land-based turbine blade directionally solidified with the liquid metal cooling process. Metallurgical and Materials Transactions, 2000, 31B: 1293–1304.
Ma D X and Bührig-Polaczek A. Application of a heat conductor technique in the production of single-crystal turbine blades. Metallurgical and Materials Transactions, 2009, 40B: 738–748
Meng X B, Li J G, Zhu S Z, et al. Method of SG inhibition in the platforms with different dimensions during directional solidification of a Ni-base superalloy. Metallurgical and Materials Transactions, 2014, 45A:1230–1236.
Szeliga D, Kubiak K, Sieniawski J. Control of liquidus isotherm shape during solidification of Ni-based superalloy of single crystal platforms. Journal of Materials Processing Technology, 2016, 234: 18–26.
Author information
Authors and Affiliations
Corresponding author
Additional information
Lin Liu Male, born in 1956, Ph.D, Professor. His research and teaching interests mainly focus on the microstructure and properties of cast superalloys, theory and application of directional solidification, electromagnetic confinement and shaping of metallic materials.
The study was financially supported by the National Key Research and Development Program (2016YFB0701405), the National 973 Program (2011CB610406), National 863 Project (2012AA03A511), the National Natural Science Foundation of China (51171151, 51331005, 51501151, 51631008), the Natural Science Foundation of Shaanxi Province (2014JM6227), the Aeronautical Science Foundation of China (2015ZE53059), and the Fund of the State Key Laboratory of Solidification Processing in NWPU (SKLSP201411).
Rights and permissions
About this article
Cite this article
Li, Yf., Liu, L., Huang, Tw. et al. Simulation of stray grain formation in Ni-base single crystal turbine blades fabricated by HRS and LMC techniques. China Foundry 14, 75–79 (2017). https://doi.org/10.1007/s41230-017-6106-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-017-6106-2