Abstract
The mechanical size effect of nanostructured, dual-phase CrCoNi medium-entropy alloy (MEA) was investigated by combining in-situ micro-compression testing with post-mortem electron microscopy analysis. The alloy possesses a superior yield strength up to ∼4 GPa, primarily due to its hierarchical microstructure including column nanograins, preferred orientation, a high density of planar defects and the presence of the hexagonal close packed (HCP) phase. While the yield strength of the alloy has shown size-independency, the deformation behaviour was strongly dependent on the sample size. Specifically, with decreasing the pillar diameters, the dominant deformation mode changed from highly localized and catastrophic shear banding to apparently homogeneous deformation with appreciable plasticity. This transition is believed to be governed by the size-dependent critical stress required for a shear band traversing the pillar and mediated by the competition between shear-induced softening and subsequent hardening mechanisms. In addition, an unexpected phase transformation from HCP to face-centered cubic (FCC) was observed in the highly localized deformation zones, leading to strain softening that contributed to accommodating plasticity. These findings provide insights into the criticality of sample dimensions in influencing mechanical behaviors of nanostructured metallic materials used for nanoelectromechanical systems.
摘要
本文结合原位扫描电子显微镜微柱压缩与透射电子显微镜技术, 研究了具有双相多级纳米结构的CrCoNi中熵合金变形行为的尺寸效应. 研究表明, 该合金的屈服强度高达~4 GPa, 这主要归因于其多级微观结构特征, 包括柱状纳米尺寸晶粒、 织构、高密度的层错、 孪晶界、 晶界和相界. 在变形过程中, 该合金的屈服强度基本与微米尺度样品的尺寸无关, 但其变形行为却强烈依赖于样品大小. 具体来说, 随着微柱直径减小, 材料主要的变形模式从突发的局部剪切带变为具有明显塑性的均匀变形. 这种转变是由剪切带穿过微柱所需的临界应力与样品尺寸紧密相关所决定的, 剪切诱导的软化和随后的硬化机制之间的竞争也起了重要作用. 此外, 变形引起了六方密排结构到面心立方结构的相变, 该相变导致的应变软化对材料变形中的塑性有重要贡献. 这些发现揭示了样品尺寸对可用于微纳机电系统的纳米结构金属材料的力学行为有着重要影响.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Yeh JW, Chen SK, Lin SJ, et al. Nanostructured high-entropy alloys with multiple principal elements: novel alloy design concepts and outcomes. Adv Eng Mater, 2004, 6: 299–303
Cantor B, Chang ITH, Knight P, et al. Microstructural development in equiatomic multicomponent alloys. Mater Sci Eng-A, 2004, 375–377: 213–218
Zhang Y, Zuo TT, Tang Z, et al. Microstructures and properties of high-entropy alloys. Prog Mater Sci, 2014, 61: 1–93
Zhang W, Liaw PK, Zhang Y. Science and technology in high-entropy alloys. Sci China Mater, 2018, 61: 2–22
Gludovatz B, Hohenwarter A, Catoor D, et al. A fracture-resistant high-entropy alloy for cryogenic applications. Science, 2014, 345: 1153–1158
Lin Q, An X, Liu H, et al. In-situ high-resolution transmission electron microscopy investigation of grain boundary dislocation activities in a nanocrystalline CrMnFeCoNi high-entropy alloy. J Alloys Compd, 2017, 709: 802–807
Otto F, Yang Y, Bei H, et al. Relative effects of enthalpy and entropy on the phase stability of equiatomic high-entropy alloys. Acta Mater, 2013, 61: 2628–2638
Ma D, Grabowski B, Körmann F, et al. Ab initio thermodynamics of the CoCrFeMnNi high entropy alloy: Importance of entropy contributions beyond the configurational one. Acta Mater, 2015, 100: 90–97
Yang X, Zhang Y. Prediction of high-entropy stabilized solid-solution in multi-component alloys. Mater Chem Phys, 2012, 132: 233–238
Li Z, Pradeep KG, Deng Y, et al. Metastable high-entropy dualphase alloys overcome the strength-ductility trade-off. Nature, 2016, 534: 227–230
Lu W, Liebscher CH, Dehm G, et al. Bidirectional transformation enables hierarchical nanolaminate dual-phase high-entropy alloys. Adv Mater, 2018, 30: 1804727
An XH, Wu SD, Wang ZG, et al. Significance of stacking fault energy in bulk nanostructured materials: insights from Cu and its binary alloys as model systems. Prog Mater Sci, 2019, 101: 1–45
Liu J, Guo X, Lin Q, et al. Excellent ductility and serration feature of metastable CoCrFeNi high-entropy alloy at extremely low temperatures. Sci China Mater, 2019, 62: 853–863
Gludovatz B, Hohenwarter A, Thurston KVS, et al. Exceptional damage-tolerance of a medium-entropy alloy CrCoNi at cryogenic temperatures. Nat Commun, 2016, 7: 10602
Niu C, LaRosa CR, Miao J, et al. Magnetically-driven phase transformation strengthening in high entropy alloys. Nat Commun, 2018, 9: 1363
Ma Y, Yuan F, Yang M, et al. Dynamic shear deformation of a CrCoNi medium-entropy alloy with heterogeneous grain structures. Acta Mater, 2018, 148: 407–418
Miao J, Slone CE, Smith TM, et al. The evolution of the deformation substructure in a Ni-Co-Cr equiatomic solid solution alloy. Acta Mater, 2017, 132: 35–48
Schuh B, Mendez-Martin F, Völker B, et al. Mechanical properties, microstructure and thermal stability of a nanocrystalline CoCrFeMnNi high-entropy alloy after severe plastic deformation. Acta Mater, 2015, 96: 258–268
Slone CE, Miao J, George EP, et al. Achieving ultra-high strength and ductility in equiatomic CrCoNi with partially recrystallized microstructures. Acta Mater, 2019, 165: 496–507
Sun SJ, Tian YZ, An XH, et al. Ultrahigh cryogenic strength and exceptional ductility in ultrafine-grained CoCrFeMnNi high-entropy alloy with fully recrystallized structure. Mater Today Nano, 2018, 4: 46–53
He JY, Wang H, Huang HL, et al. A precipitation-hardened high-entropy alloy with outstanding tensile properties. Acta Mater, 2016, 102: 187–196
Guo L, Gu J, Gong X, et al. CALPHAD aided design of high entropy alloy to achieve high strength via precipitate strengthening. Sci China Mater, 2020, 63: 288–299
Yang T, Zhao YL, Tong Y, et al. Multicomponent intermetallic nanoparticles and superb mechanical behaviors of complex alloys. Science, 2018, 362: 933–937
Seol JB, Bae JW, Li Z, et al. Boron doped ultrastrong and ductile high-entropy alloys. Acta Mater, 2018, 151: 366–376
Li Z, Tasan CC, Springer H, et al. Interstitial atoms enable joint twinning and transformation induced plasticity in strong and ductile high-entropy alloys. Sci Rep, 2017, 7: 40704
Song M, Zhou R, Gu J, et al. Nitrogen induced heterogeneous structures overcome strength-ductility trade-off in an additively manufactured high-entropy alloy. Appl Mater Today, 2020, 18: 100498
Wang Z, Gu J, An D, et al. Characterization of the microstructure and deformation substructure evolution in a hierarchal high-entropy alloy by correlative EBSD and ECCI. Intermetallics, 2020, 121: 106788
Lei Z, Liu X, Wu Y, et al. Enhanced strength and ductility in a high-entropy alloy via ordered oxygen complexes. Nature, 2018, 563: 546–550
Chen Y, Zhou Z, Munroe P, et al. Hierarchical nanostructure of CrCoNi film underlying its remarkable mechanical strength. Appl Phys Lett, 2018, 113: 081905
Tsianikas SJ, Chen Y, Xie Z. Deciphering deformation mechanisms of hierarchical dual-phase CrCoNi coatings. J Mater Sci Tech, 2020, 39: 7–13
Uchic MD, Dimiduk DM, Florando JN, et al. Sample dimensions influence strength and crystal plasticity. Science, 2004, 305: 986–989
Greer JR, Nix WD. Nanoscale gold pillars strengthened through dislocation starvation. Phys Rev B, 2006, 73: 245410
Shan ZW, Mishra RK, Syed Asif SA, et al. Mechanical annealing and source-limited deformation in submicrometre-diameter Ni crystals. Nat Mater, 2008, 7: 115–119
Wang ZJ, Li QJ, Shan ZW, et al. Sample size effects on the large strain bursts in submicron aluminum pillars. Appl Phys Lett, 2012, 100: 071906
Nix WD, Greer JR, Feng G, et al. Deformation at the nanometer and micrometer length scales: effects of strain gradients and dislocation starvation. Thin Solid Films, 2007, 515: 3152–3157
Hütsch J, Lilleodden ET. The influence of focused-ion beam preparation technique on microcompression investigations: Lathe vs. annular milling. Scripta Mater, 2014, 77: 49–51
Guo W, Jägle E, Yao J, et al. Intrinsic and extrinsic size effects in the deformation of amorphous CuZr/nanocrystalline Cu nanolaminates. Acta Mater, 2014, 80: 94–106
Chen CQ, Pei YT, De Hosson JTM. Effects of size on the mechanical response of metallic glasses investigated through in situ TEM bending and compression experiments. Acta Mater, 2010, 58: 189–200
Giannuzzi LA, Stevie FA. A review of focused ion beam milling techniques for TEM specimen preparation. Micron, 1999, 30: 197–204
Greer JR, De Hosson JTM. Plasticity in small-sized metallic systems: intrinsic versus extrinsic size effect. Prog Mater Sci, 2011, 56: 654–724
Hull D, Bacon DJ. Introduction to Dislocations. Oxford: Elsevier, 2011
Liu SF, Wu Y, Wang HT, et al. Stacking fault energy of face-centered-cubic high entropy alloys. Intermetallics, 2018, 93: 269–273
Lin Q, Liu J, An X, et al. Cryogenic-deformation-induced phase transformation in an FeCoCrNi high-entropy alloy. Mater Res Lett, 2018, 6: 236–243
Schuh B, Völker B, Todt J, et al. Influence of annealing on microstructure and mechanical properties of a nanocrystalline CrCoNi medium-entropy alloy. Materials, 2018, 11: 662
Zhu ZG, Nguyen QB, Ng FL, et al. Hierarchical microstructure and strengthening mechanisms of a CoCrFeNiMn high entropy alloy additively manufactured by selective laser melting. Scripta Mater, 2018, 154: 20–24
Lu L, Chen X, Huang X, et al. Revealing the maximum strength in nanotwinned copper. Science, 2009, 323: 607–610
Lu K, Lu L, Suresh S. Strengthening materials by engineering coherent internal boundaries at the nanoscale. Science, 2009, 324: 349–352
Chen B, Wang J, Gao Q, et al. Strengthening brittle semiconductor nanowires through stacking faults: insights from in situ mechanical testing. Nano Lett, 2013, 13: 4369–4373
Chen Y, Burgess T, An X, et al. Effect of a high density of stacking faults on the Young’s modulus of GaAs nanowires. Nano Lett, 2016, 16: 1911–1916
Li Z, Tasan CC, Pradeep KG, et al. A trip-assisted dual-phase high-entropy alloy: grain size and phase fraction effects on deformation behavior. Acta Mater, 2017, 131: 323–335
Wang J, Sansoz F, Huang J, et al. Near-ideal theoretical strength in gold nanowires containing angstrom scale twins. Nat Commun, 2013, 4: 1742
Wang L, Lu Y, Kong D, et al. Dynamic and atomic-scale understanding of the twin thickness effect on dislocation nucleation and propagation activities by in situ bending of Ni nanowires. Acta Mater, 2015, 90: 194–203
Jang D, Greer JR. Size-induced weakening and grain boundary-assisted deformation in 60 nm grained Ni nanopillars. Scripta Mater, 2011, 64: 77–80
Chen CQ, Pei YT, Kuzmin O, et al. Intrinsic size effects in the mechanical response of taper-free nanopillars of metallic glass. Phys Rev B, 2011, 83: 180201
Shan ZW, Li J, Cheng YQ, et al. Plastic flow and failure resistance of metallic glass: insight from in situ compression of nanopillars. Phys Rev B, 2008, 77: 155419
Kuzmin OV, Pei YT, Chen CQ, et al. Intrinsic and extrinsic size effects in the deformation of metallic glass nanopillars. Acta Mater, 2012, 60: 889–898
Khalajhedayati A, Rupert TJ. Disruption of thermally-stable nanoscale grain structures by strain localization. Sci Rep, 2015, 5: 10663
Rice JR. The localization of plastic deformation. In: Proceedings of the 14th International Congress of Theoretical and Applied Mechanics. Delft, 1976. 1–14
Volkert CA, Donohue A, Spaepen F. Effect of sample size on deformation in amorphous metals. J Appl Phys, 2008, 103: 083539
Jang D, Greer JR. Transition from a strong-yet-brittle to a stronger-and-ductile state by size reduction of metallic glasses. Nat Mater, 2010, 9: 215–219
Gao H, Ji B, Jager IL, et al. Materials become insensitive to flaws at nanoscale: lessons from nature. Proc Natl Acad Sci USA, 2003, 100: 5597–5600
Laplanche G, Gadaud P, Bärsch C, et al. Elastic moduli and thermal expansion coefficients of medium-entropy subsystems of the CrMnFeCoNi high-entropy alloy. J Alloys Compd, 2018, 746: 244–255
Wu XL, Guo YZ, Wei Q, et al. Prevalence of shear banding in compression of Zr41Ti14Cu125Ni10Be225 pillars as small as 150 nm in diameter. Acta Mater, 2009, 57: 3562–3571
Schuster BE, Wei Q, Hufnagel TC, et al. Size-independent strength and deformation mode in compression of a Pd-based metallic glass. Acta Mater, 2008, 56: 5091–5100
Chen Y, An X, Liao X, et al. Effects of loading misalignment and tapering angle on the measured mechanical properties of nanowires. Nanotechnology, 2015, 26: 435704
Laplanche G, Kostka A, Reinhart C, et al. Reasons for the superior mechanical properties of medium-entropy CrCoNi compared to high-entropy CrMnFeCoNi. Acta Mater, 2017, 128: 292–303
Zhang ZJ, Mao MM, Wang J, et al. Nanoscale origins of the damage tolerance of the high-entropy alloy CrMnFeCoNi. Nat Commun, 2015, 6: 10143
Huang S, Huang H, Li W, et al. Twinning in metastable high-entropy alloys. Nat Commun, 2018, 9: 2381
Zhang FX, Zhao S, Jin K, et al. Pressure-induced FCC to HCP phase transition in Ni-based high entropy solid solution alloys. Appl Phys Lett, 2017, 110: 011902
Zhao H, Song M, Ni S, et al. Atomic-scale understanding of stress-induced phase transformation in cold-rolled Hf. Acta Mater, 2017, 131: 271–279
Armstrong RW, Coffey CS, Elban WL. Adiabatic heating at a dislocation pile-up avalanche. Acta Metall, 1982, 30: 2111–2116
Wei Q, Jia D, Ramesh KT, et al. Evolution and microstructure of shear bands in nanostructured Fe. Appl Phys Lett, 2002, 81: 1240–1242
Zhang ZF, Eckert J, Schultz L. Difference in compressive and tensile fracture mechanisms of Zr59Cu20Al10Ni8Ti3 bulk metallic glass. Acta Mater, 2003, 51: 1167–1179
Zhang Z, Sheng H, Wang Z, et al. Dislocation mechanisms and 3D twin architectures generate exceptional strength-ductility-toughness combination in CrCoNi medium-entropy alloy. Nat Commun, 2017, 8: 14390
Jang D, Li X, Gao H, et al. Deformation mechanisms in nanotwinned metal nanopillars. Nat Nanotech, 2012, 7: 594–601
Asaro RJ. Geometrical effects in the inhomogeneous deformation of ductile single crystals. Acta Metall, 1979, 27: 445–453
Fujita H, Ueda S. Stacking faults and f.c.c. (γ) → h.c.p. (ε) transformation in 188-type stainless steel. Acta Metall, 1972, 20: 759–767
Huang JY, Wu YK, Ye HQ. Allotropic transformation of cobalt induced by ball milling. Acta Mater, 1996, 44: 1201–1209
Liu Y, Yang H, Tan G, et al. Stress-induced FCC ↔ HCP martensitic transformation in CoNi. J Alloys Compd, 2004, 368: 157–163
Acknowledgements
This work was supported by the Australian Research Council Discovery Projects Grant, and partly supported by the Fundamental Research Funds for the Central Universities (SWU118105). An X acknowledges the financial support from Australia Research Council (DE170100053) and the Robinson Fellowship Scheme of the University of Sydney (G200726). The authors acknowledge the facilities and the scientific and technical assistance of the Australian Microscopy and Microanalysis Research Facility (ammrf.org.au) node at the University of Adelaide: Adelaide Microscopy. In particular, the authors thank Dr Animesh Basak and Dr Ashley Slattery of Adelaide Microscopy for their support and expertise.
Author information
Authors and Affiliations
Contributions
Author contributions Chen Y, Xie Z, An X and Zhang S conceived the project. Chen Y conducted the FIB, microcompression and TEM experiments. Zhou Z fabricated the samples. Chen Y, An X, Liao X and Xie Z interpreted the results and wrote the manuscript. All authors contributed to the discussion of the results, and comments on the manuscript.
Corresponding authors
Ethics declarations
Conflict of interest The authors declare that they have no conflict of interest.
Additional information
Yujie Chen obtained her BEng degree (first-class honors) in 2011 and PhD degree in materials science in 2016 from The University of Sydney. Upon completion of her PhD, she was employed as a postdoc in the School of Mechanical Engineering in the University of Adelaide in Australia. She is currently a research fellow in the Southwest University in China. Her current research involves microstructure optimization and mechanical properties enhancement of alloys, and calcified tissues.
Xianghai An received his PhD degree from the Institute of Metal Research, Chinese Academy of Sciences in 2012. After receiving his PhD degree, he commenced to work as a research fellow at The University of Sydney. He is currently a Lecture/Robinson Fellow at The University of Sydney. His research mainly focuses on materials design, mechanical behavior, and structure-property relationship of advanced metallic materials, nanomechanics and nanoplasticity, metallic additive manufacturing and advanced materials processing.
Sam Zhang received his PhD degree (1991) in ceramic materials at the University of Wisconsin-Madison, USA. He joined Nanyang Technological University as an associate professor and was promoted to full professor in 2006. He is currently a professor and head of the Center for Advanced Thin Films and Devices in the Southwest University in China. He is also Fellow of the Institute of Materials, Minerals and Mining, Fellow of the Royal Society of Chemistry and Fellow of the Thin Films Society. His research interests include preparation and characterization of hard yet tough ceramic nanocomposite coatings, and functional thin films.
Rights and permissions
About this article
Cite this article
Chen, Y., An, X., Zhou, Z. et al. Size-dependent deformation behavior of dual-phase, nanostructured CrCoNi medium-entropy alloy. Sci. China Mater. 64, 209–222 (2021). https://doi.org/10.1007/s40843-020-1377-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40843-020-1377-2