Abstract
The behavior of Si3N4 etching with ion-incidence angle in high-density CF4, CHF3, and C2F6 plasmas was investigated to understand the effect of discharge chemistry on the etch characteristics of Si3N4. The normalized etch yield (NEY) plots suggest that for all plasmas considered herein, physical sputtering is more prevalent than ion-assisted chemical etching as the Si3N4 etching mechanism. In the cases of the CF4 and C2F6 plasmas, the NEYs at an ion-incidence angle of 60° were greater than unity because the thickness and the fluorine-to-carbon (F/C) ratio of the steady-state fluorocarbon films (st-st FC films) on the Si3N4 surfaces decreased and increased, respectively, as the ion-incidence angle was increased from 0° to 60°. In contrast, the NEY at this angle in the CHF3 plasma was close to unity, as a result of a small change (or a very marginal decrease) in the thickness and the F/C ratio of the st-st FC film. Additionally, the NEY at an ion-incidence angle of 60° was higher in C2F6 plasma compared to CF4 plasma because the changes in the thickness and the F/C ratio of the st-st FC film were greater in the C2F6 plasma than those in the CF4 plasma.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Y. X. Li, P. J. French and R. F. Wolffenbuttel, J. Vac. Sci. Technol. B, 13, 2008 (1995).
J. H. Choi, S. J. Kim, H. T. Kim and S. M. Cho, Korean J. Chem. Eng., 35, 1348 (2018).
B. E. E. Kastenmeier, P. J. Matsuo and G. S. Oehrlein, J. Vac. Sci. Technol. A, 17, 3179 (1999).
M. Schaepkens, G. S. Oehrlein, C. Hedlund, L. B. Jonsson and H.-O. Blom, J. Vac. Sci. Technol. A, 16, 3281 (1998).
M. Ito, K. Kamiya, M. Hori and T. Goto, J. Appl. Phys., 91, 3452 (2002).
M. Schaepkens, T. E. F. M. Standaert, N. R. Rueger, P. G. M. Sebel, G. S. Oehrlein and J. M. Cook, J. Vac. Sci. Technol. A, 17, 26 (1999).
A. M. Barklund and H.-O. Blom, J. Vac. Sci. Technol. A, 10, 1212 (1992).
A. M. Barklund and H.-O. Blom, J. Vac. Sci. Technol. A, 11, 1226 (1993).
S.-W. Cho, C.-K. Kim, J.-K. Lee, S. H. Moon and H. Chae, J. Vac. Sci. Technol. A, 30, 051301 (2012).
S.-W. Cho, J.-H. Kim, D. W. Kang, K. Lee and C.-K. Kim, ECS J. Solid State Sci. Technol., 3, Q215 (2014).
S.-W. Cho, J.-H. Kim, J. G. Bak and C.-K. Kim, ECS Solid State Lett., 4, 85 (2015).
J.-H. Kim, S.-W. Cho, C. J. Park, H. Chae and C.-K. Kim, Thin Solid Films, 637, 43 (2017).
J.-H. Kim, S.-W. Cho and C.-K. Kim, Chem. Eng. Technol., 40, 2251 (2017).
J.-H. Kim, J.-S. Park and C.-K. Kim, Thin Solid Films, 669, 262 (2019).
T. E. F. M. Standaert, C. Hudlund, E. A. Joseph and G. S. Oehrlein, J. Vac. Sci. Technol. A, 22, 53 (2004).
B.-O. Cho, S.-W. Hwang, G.-R. Lee and S. H. Moon, J. Vac. Sci. Technol. A, 18, 2791 (2000).
D. P. Hamblen and A. Cha-Lin, J. Electrochem. Soc., 135, 1816 (1988).
N. R. Rueger, J. J. Beulens, M. Schaepkens, M. F. Doemling, J. M. Mizra, T. E. F. Standaert and G. S. Oehrlein, J. Vac. Sci. Technol. A, 15, 1881 (1997).
M. Schaepkens, T. E. F. M. Standaert, N. R. Rueger, P. G. M. Sebel, G. S. Oehrlein and J. M. Cook, J. Vac. Sci. Technol. A, 17, 26 (1999).
Acknowledgements
This work was supported by the Korea Institute of Energy Technology Evaluation and Planning (KETEP) grant funded by the Korea Government Ministry of Trade, Industry and Energy (Grant No. 20172010104830), the National Research Foundation of Korea (NRF) grant funded by the Korea government (MEST) (Grant No. 2018R1A2B6002410), and the GRRC program of Gyeonggi province (GRRC AJOU 2016B03, Photonics-Medical Convergence Technology Research Center).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kim, JH., Kim, CK. Si3N4 etch rates at various ion-incidence angles in high-density CF4, CHF3, and C2F6 plasmas. Korean J. Chem. Eng. 37, 374–379 (2020). https://doi.org/10.1007/s11814-019-0449-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11814-019-0449-x