Abstract
This study examined the photoelectric conversion efficiency of the dye-sensitized solar cell (DSSC) when the surface of a nanometer-sized TiO2 film, which was prepared using the solvothermal method, was modified by five acid compounds. The TiO2 film exhibited an anatase structure with an average particle size in the range of 10–15 nm, and the maximum absorption band was shown in the UV-visible spectrum around 360 nm. The surface colors of the carboxylic acid-modified TiO2 films were changed to light or dark with differing energy conversion efficiencies. Particularly, the conversion efficiency was considerably enhanced from approximately 6.25% for the non-modified TiO2 film to approximately 7.50% for the film treated by acetic acid of 1.0 mole, with the N719 dye under 100 mW/cm2 of simulated sunlight. FT-IR analysis of the films after N719 dye adsorption confirmed that the IR spectrum of the modified TiO2 showed a sharp and strong band at 500 cm−1, which was assigned to a metal-O bond, due to the formation of a new Ti-O bond between the O of COO− and the Ti atom, which was relatively weaker in the non-modified TiO2. Furthermore, these results were in agreement with an electrostatic force microscopy (EFM) study showing that the electrons were transferred rapidly to the surface of the acetic acid-modified TiO2 film, compared with that on the nonmodified TiO2 film.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
A.W. Blakers and T. Armour, Sol. Cells, 93, 1440 (2009).
Y. Wang, Z. Fang, Li. Zhu, Q. Huang, Y. Zhang and Z. Zhang, Appl. Energy, 86, 1037 (2009).
P. N. Vinod, Solid State Commun., 149, 957 (2009).
P. Li, P, Wua and J. Lin, J. Sol. Energy, 83, 845 (2009).
N. H. Rajesh, R. H. Ragunatharaddi and T. N. Sharanappa, Colloids & Surface B, 72, 259 (2009).
S. Gagliardi, L. Giorgi, R. Giorgi, N. Lisi, Th. Makris, E. Salernitano and A. Rufoloni, Superlattices & Microst., 46, 205 (2009).
R. Lee and Y. Huang, Thin Solid Films, 517, 5903 (2009).
C. S. Chou, R.Y. Yang, C.K. Yeh and Y. Lin, J. Powder Technol., 194, 95 (2009).
J. H. Park, K. J. Choi and S. Kang, J. Power Sources, 183, 812 (2008).
R. Dholam, N. Patel and M. Adami, Inter. J. Hydrogen Energy, 33, 6896 (2008).
H. P. Klug and L. F. Alexander, About Tachyons, Phys. Today, 2Ed, John Wiley & Sons, Inc., 716 (1954).
Y. Kim, J. Lee, H. Jeong, Y. Lee, M. Um, K.M. Jeong, M. Yeo and M. Kang, J. Ind. Eng. Chem., 14, 396 (2008).
M. Gratzel, J. Photochem. Photobiol., 4, 145 (2003).
K. Kalyanasundaran and M. Gratzel, Coordination Chem. Reviews, 177, 347 (1999).
F.M. Serry, K. Kjoller and T. Thorntin, Scanning Probe Microscopy, Veeco Instruments Inc. (2007).
T.V. Vorburger, J.A. Dagata, G. Wilkening and A.W. Czanderna, Beam Effects, Surface Topography, and Depth Profiling in Surface Analysis, Edited by Czanderna et al., Plenum Press, New York (1998).
H. Sun, Z. Li, J. Zhou, Y. Zhao and M. Lu, Surf. Sci., 253, 6109 (2007).
P. Girard, Phys. Puv. Nanotech., 12, 485 (2001).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Jeong, H., Lee, Y., Kim, Y. et al. Enhanced photoelectric efficiency by surface modification of TiO2 thin film using various acidic species. Korean J. Chem. Eng. 27, 1462–1468 (2010). https://doi.org/10.1007/s11814-010-0252-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11814-010-0252-1