Abstract
We investigated cell performance and performed phenomenological analyses of direct formic acid fuel cells (DFAFCs) incorporating anode (palladium) and cathode (platinum) catalysts prepared using a new electrospray coating technique. To optimize the design of the DFAFC, we examined the cell performance by the Pd catalyst loading and formic acid feed rate. Of Pd catalyst loaded samples, 3 mg/cm2 sample showed the highest electrical performance with formic acid feed rate of 5 ml/min. This behavior was caused by discrepancies in the mass transfer limitation. When the feed rate was greater than 10 mL/min, however, the 7 mg/cm2 sample provided the highest electrical performance, which was attributed to enhanced electrooxidation reactions. For comparison of the effect of the catalyst coating method on the cell performance of DFAFC, polarization curves of the DFAFC incorporating catalysts prepared using a conventional airspray coating method were also measured. As a result of the comparison, the electrospray coatingused DFAFC showed better cell performance. Based on these results, the cell performance of the DFAFCs was optimized when the catalysts using the electrospray catalyst coating were employed, the amount of Pd loaded on the anode electrode was 3 mg/cm2 (Pd thickness: ∼6 μm), and the formic acid feed rate was 10 mL/min.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
C. Rice, S. Ha, R. I. Masel, P. Waszczuk, A. Wieckowski and T. Barnard, J. Power Sources, 111, 83 (2002).
X. Yu and P. G. Pickup, J. Power Sources, 182, 124 (2008).
Y. Zhu, S. Ha and R. I. Masel, J. Power Sources, 130, 8 (2004).
M. Neegat, T. Selier, E. R. Savinova and U. Stimming, J. Electrochem. Soc., 153, A997 (2006).
P. Piela, R. Fields and P. Zelenay, J. Electrochem. Soc., 153, A1902 (2006).
X. Ren, T. E. Springer and S. Gottesfeld, J. Electrochem. Soc., 147, 92 (2000).
J.-H. Choi, K.-W. Park, I.-S. Park, K. Kim, J.-S. Lee and Y.-E. Sung, J. Electrochem. Soc., 153, A1812 (2006).
H. F. Oetjen, V. M. Schmidt, U. Stimming and F. Trila, J. Electrochem. Soc., 143, 3838 (1996).
U. B. Demirci, J. Power Sources, 169, 239 (2007).
G. J. K. Acres, J. Power Sources, 100, 60 (2001).
S. Gamburzev and A. J. Appleby, J. Power Sources, 107, 5 (2002).
S. Ha, C. Rice, R. I. Masel and A. Wieckowski, J. Power Sources, 112, 655 (2002).
W. S. Jung, J. H. Han and S. Ha, J. Power Sources, 173, 53 (2007).
S. Ha, R. Larsen and R. I. Masel, J. Power Sources, 144, 28 (2005).
C.M. Misse, W. S. Jung, K. J. Jeong, J.K. Lee, J. Lee, J.H. Han, S. P. Yoon, S.W. Nam, T. H. Lim and S. A. Hong, J. Power Sources, 162, 532 (2005).
K. Chu, M.A. Shannon and R. I. Masel, J. Electrochem. Soc., 153, A1562 (2006).
X. Xia and T. J. Iwasita, J. Electrochem. Soc., 140, 2559 (1993).
H. Yang and T. S. Zhao, Electrochim. Acta, 50, 3243 (2004).
H. Qiao, H. Shiroishi and T. Okada, Electrochim. Acta, 53, 59 (2007).
I.-M. Hsing, X. Wang and Y.-J. Leng, J. Electrochem. Soc., 149, A615 (2002).
R. Jiang, H. R. Kunz and J.M. Fenton, J. Electrochem. Soc., 152, A1329 (2005).
S. Ha, Z. Dunbar and R. I. Masel, J. Power Sources, 130, 129 (2003).
R. Larsen, S. Ha, J. Zakzeski and R. I. Masel, J. Power Sources, 157, 78 (2006).
R. O’Hayre, S.W. Cha, W. Colalla and F. B. Frinz, Fuel cell fundamentals, Wiley, New York, 145 (2006).
Y. Zhu, Z. Kahn and R. I. Masel, J. Power Sources, 139, 15 (2005).
R. Benítez, J. Soler and L. Daza, J. Power Sources, 151, 108 (2005).
O.A. Baturina and G. E. Wnek, Electrochem. Solid-State Lett., 8, A267 (2005).
G. Li, and P. G. Pickup, J. Electrochem. Soc., 150, C745 (2003).
H. J. Choi, J. Kim, Y. Kwon and J.H. Han, J. Power Sources, 195, 160 (2010).
Z. Xie, T. Navessin, K. Shi, R. Chow, Q. Wang, D. Song, B. Andreaus, M. Eikerling, Z. Liu and S. Holdcroft, J. Electrochem. Soc., 152, A1171 (2005).
J.H. Choi, K. J. Jeong, Y. Dong, J.H. Han, T.H. Im, J. S. Lee and Y. E. Sung, J. Power Sources, 163, 71 (2006).
M. Lukaszewski, K. Kusmierczyk, J. Kotowski, H. Siwek and A. Czerwinski, J. Solid State Electrochem., 7, 69 (2003).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kwon, Y., Baek, S., Kwon, B. et al. Evaluation of direct formic acid fuel cells with catalyst layers coated by electrospray. Korean J. Chem. Eng. 27, 836–842 (2010). https://doi.org/10.1007/s11814-010-0166-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11814-010-0166-y