Abstract
To study the feasibility of applying solution-cast membranes to polymer electrolyte membrane fuel cells (PEMFCs), single cells prepared with solution-cast membranes were tested. The solution cast membranes were fabricated from a commercial Nafion solution under various conditions. Effects of annealing temperature on characteristics of the solution-cast membranes were investigated by measuring water uptake and ionic conductivity of the membranes. Performance of the single cells using the prepared solution cast membranes was evaluated in terms of i-V curves, Nyquist plots, and H2 crossover current density. Based on the results, solution-cast membranes were fabricated by being cured at 150 °C for different hours to examine effects of curing time on cell performance. Finally, durability of solution-cast membranes was investigated with operating the single cells for 1,000 hr.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
A. J. Appleby and F. R. Foulkes, Fuel cell handbook, Van Nostrand Reinhold, New York (1989).
L. A. Zook and J. Leddy, Anal. Chem., 68, 3793 (1996).
C. H. Wirquin, J. Membr. Sci., 120, 1 (1996).
T. D. Gierke and W. S. Hsu, in A. Eisenberg and H. L. Yeager Eds., Perflourinated Ionomer Membranes, ACS Symposium Series 180, American Chemical Society, Washington DC (1982).
S. H. de Almeida and Y. Kawano, J. Therm. Anal. Calorim., 58, 569(1999).
T. A. Zawodzinski, C. Derouin, S. Radizinski, R. J. Sherman, V. T. Smith, T. E. Springer and S. Gottesfeld, J. Electrochem. Soc., 140, 1041 (1993).
J. J. Sumner, S. E. Creager, J. J. Ma and D. D. DesMarteau, J. Electrochem. Soc., 145, 107 (1998).
T. A. Zawodzinski, Jr., T. E. Springer, J. Davey, R. Jestel, C. Lopez, J. Valerio and S. Gottesfeld, J. Electrochem. Soc., 140, 1981 (1993).
D. E. Curtin, R. D. Lousenberg, T. J. Henry, P. C. Tangeman and M. E. Tisack, J. Power Sources, 131, 41 (2004).
G. Gebel, P. Albert and M. Pineri, Macromolecules, 20, 1425 (1987).
M. Laporta, M. Pegoraro and L. Zanderighi, Macromol. Mater. Eng., 282, 22 (2000).
Z. Fan and D. J. Harrison, Anal. Chem., 64, 1304 (1992).
H.Y. Jung, K. Y. Cho, Y. M. Lee, J. K. Park, J. H. Choi and Y. E. Sung, J. Power Sources, 163, 952 (2007).
X. Cheng, B. Yi, M. Han, J. Zhang, Y. Qiao and J. Yu, J. Power Sources, 79, 75 (1999).
Z. Liang, W. Chen, J. Liu, S. Wang, Z. Zhou, W. Li, G. Sun and Q. Xin, J. Membrane Science, 233, 39 (2004).
J. St-Pierre, D. P. Wilkinson, S. Knights and M. L. Bos, J. New Mat. Electrochem. Syst., 3, 99 (2000).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Vengatesan, S., Cho, E., Kim, HJ. et al. Effects of curing condition of solution cast Nafion® membranes on PEMFC performance. Korean J. Chem. Eng. 26, 679–684 (2009). https://doi.org/10.1007/s11814-009-0113-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11814-009-0113-y